Polymer Property : Tensile Strength at Break = 43.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	43.0 MPa	6240 psi	ASTM D638
SABIC PS 126 General Purpose Polystyrene for Injection Molding Product Description: General purpose Polystyrene PS 125 is manufactured by continuous mass polymerization of styrene monomer. It is a crystal-like, hard and brittle polymer with medium flow and hi..
Tensile Strength at Break	43.0 MPa	6240 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Cycoloy® CY5005 PC+ABS (Europe-Africa-Middle East) Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering hydrolytic stability and excellent flow for a wide variety of thin wall or large size applicat..
Tensile Strength at Break	43.0 MPa	6240 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Cycoloy® CY6010 PC+ABS (Asia Pacific) Cycoloy CY6010 resin is a flame retardant PC/ABS blend featuring excellent flow together with good impact and UL-94 V0 listing at 1.5mm. Its excellent flow combined with balanced heat and good pract..
Tensile Strength at Break	43.0 MPa	6240 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Cycoloy® CY6010 PC+ABS (Europe-Africa-Middle East) Cycoloy CY6010 resin is a flame retardant PC/ABS blend featuring excellent flow together with good impact and UL-94 V0 listing at 1.5mm. Its excellent flow combined with balanced heat and good pract..
Tensile Strength at Break	43.0 MPa	6240 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Cycoloy® NX07353 PC+ABS (Asia Pacific) Cycoloy* C7230P resin is a mineral filled, flame retardant PC/ABS. Good stiffness combined with balanced flow and impact performance, makes it a good candidate for various applications.
Tensile Strength at Break	43.0 MPa	6240 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Lexan® EXL4419 PC Copolymer (Europe-Africa-Middle East) Lexan* EXL4419 polycarbonate (PC) siloxane copolymer resin is a 9% Glass Fiber (GF) reinforced opaque injection molding (IM) grade. This medium flow resin offers much higher ductility, improved rele..
Tensile Strength at Break	43.0 MPa	6240 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP DL002PC PC LNP* LUBRICOMP* DL002PC is a compound based on Polycarbonate resin containing 10% PTFE. Added features of this grade are: Wear Resistant, Exceptional Processing, Clean Compound System.
Tensile Strength at Break	<= 43.0 MPa	<= 6240 psi	ISO/R527
Polykemi AB POLYabs F20 UV4 ABS, UV-stabilized Information provided by Polykemi AB
Tensile Strength at Break	43.0 MPa	6240 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Geloy XTPM302 ASA+PC (Europe-Africa-Middle East) XTPM302 is a general purpose ASA/PC injection moulding grade, available in various colors.Typical properties measured on natural material.This data was supplied by SABIC-IP for the Europe-Africa-Mid..
Tensile Strength at Break	43.0 MPa	6240 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP DL0049EF PC (Asia Pacific) LNP* Lubricomp* DL0049EF is a compound based on Polycarbonate resin containing PTFE, Flame Retardant. Added features of this material include: Internally Lubricated.
Tensile Strength at Break	43.0 MPa	6240 psi	5mm/min; ISO 527-2/1A/5
SYNTHOS KrastenÂ® 137 General Purpose Polystyrene Easy flow. Examples of Application:Injection moulding â€“ cups and containers for the food industry, medical devices, drawing templates.Extrusion â€“ coextrusion, high gloss surface.Synthos wa..
Tensile Strength at Break	43.0 MPa	6240 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP NL001 PC+ABS (Europe-Africa-Middle East) LNP LUBRICOMP* NL001 is a wear resistant PC+ABS blend, suitable for thin wall applications.
Tensile Strength at Break	43.0 MPa @Temperature 120 Â°C	6240 psi @Temperature 248 Â°F	50 mm/min, 1A; ISO 527
SABIC Innovative Plastics SABIC STAMAX 30YK270 PP SABICÂ® STAMAX 30YK270 is a 30% long glass fiber reinforced polypropylene with improved impact and flow properties. The glass fibers are chemically coupled to the PP matrix, resulting in high stif..
Tensile Strength at Break	43.0 MPa	6240 psi	ISO 527
SABIC Innovative Plastics LNP LUBRILOY R2000A PA 66 (Asia Pacific) LNP LUBRILOY* R2000A is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Tensile Strength at Break	43.0 MPa	6240 psi	50 mm/min; ISO 527
SABIC Innovative Plastics XenoyÂ® 5720U PBT+PC (Europe-Africa-Middle East) Unfilled PBT+PC alloy. Outstanding low temperature impact/chemical resistance. UV stabilized version of XENOY
Tensile Strength at Break	43.0 MPa	6240 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-LOY AF3029U ABS (Europe-Africa-Middle East) LNP* STAT-LOY* AF3029U is a compound based on Acrylonitrile Butadiene resin containing Glass Fiber, Flame Retardant, Propietary filler. Added features include: Antistatic, UV-Stabilized.
Tensile Strength at Break	43.0 MPa	6240 psi	50 mm/min; ISO 527
SABIC Innovative Plastics XYLEX X8303 PC+POLYESTER (Europe-Africa-Middle East) PC+ POLYESTER, Transparent, Low processing Temperature, High flow with excellent impact, UV stabilized. For In Mold Decoration /Labeling.
Tensile Strength at Break	43.0 MPa	6240 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP PH1100B PA 6 LNP* THERMOCOMP* PH1100B is a compound based on Nylon 6 resin. Added feature of this material is: High Specific Gravity Filler. Added features of this material include: High Specific Gravity.
Tensile Strength at Break	43.0 MPa	6240 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP WX05505 PBT LNP* Thermocomp* WX05505 is a compound based on Thermoplastic Polyester (PBT) resin containing proprietary fillers.
Tensile Strength at Break	43.0 MPa	6240 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics NORYL PVX0800 PPE NORYL* PVX0800 resin is a high flow, V0 = 1.5 mm grade, suitable for a variety of electronics applications.
Tensile Strength at Break	43.0 MPa	6240 psi	5 mm/min; ISO 527
SABIC Innovative Plastics XenoyÂ® X6320 PBT+PC (Asia Pacific) X6320 is a mineral filled PBT/PC resin developed for automotive painted doorhandles. Key advantages are excellent surface finish, easy processing and paint quality.
Tensile Strength at Break	43.0 MPa	6240 psi	ASTM D638
Eastman DuraStar MN630 Polymer, Natural Durastar Polymer MN630 has excellent appearance and is nearly water-clear. Its most outstanding features are toughness, chemical resistance, and excellent processing characteristics. MN630 has very ..
Tensile Strength at Break	43.0 MPa	6240 psi	ASTM D638
Eastman Eastar AN011 Copolyester Eastar AN011 copolyester is a high flow product. Eastar AN011 flow lengths are increased 20-40% relative to Eastar AN001 as shown by spiral flow testing. Other outstanding features of Eastar are eas..
Tensile Strength at Break	43.0 MPa	6240 psi	ASTM D638
Eastman Eastar AN014 Copolyester Eastar AN014 copolyester is a high flow product that contains a mold release. Eastar AN014 flow lengths are increased 20-40% relative to Eastar AN004 as shown by spiral flow testing. Other outstandi..
Tensile Strength at Break	43.0 MPa	6240 psi	ISO 527
Ecomass® 1950TU76 Tungsten Filled Polyamide Nontoxic alternative to Lead (Pb), weighting, balancing and radiation shielding applicationsTungsten Powder Filled Polyamide (PA6/10)Very Good ToughnessInformation provided by Technical Polymers
Tensile Strength at Break	43.0 MPa	6240 psi	ISO R 527
Fainplast Compounds ART 20 Rigid PVC, Atoxic for General Purpose Transparent bottles medium/high antishock
Tensile Strength at Break	43.0 MPa	6240 psi	ASTM D527-2
Arkema Group OREVAC® 18760 Grafted Maleic Anhydride Polypropylene OREVAC 18760 is a maleic anhydride grafted polypropylene used in the manufacturing of three layer PP coating for steel pipeline. OREVAC 18760 is also used in multilayer EVOH – PP structures. OREVAC..
Tensile Strength at Break	43.0 MPa	6240 psi	ISO 527-2
Ascend Performance Materials Vydyne® 41H NT Nylon 66, Impact Modified, DAM Vydyne® 41H NT is general-purpose, impact-modified PA66 resin. Available in natural, it is heat-stabilized for improved resistance to elevated temperatures. The heat stabilization package for Vydyn..
Tensile Strength at Break	43.0 MPa	6240 psi	ISO 527-2
Ascend Performance Materials Vydyne® 41 NT Nylon 66, Impact Modified, DAM Vydyne® 41 NT is general-purpose, impact-modified PA66 resin. Available in natural, it is recognized for all the processing and property advantages inherent to PA66 with the addition of improved im..
Tensile Strength at Break	43.0 MPa	6240 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics NORYL RN0612 PPE+HIPS (Europe-Africa-Middle East) Noryl RN0612 is an unfilled Post Consumer recycle (PCR) based injection moldable modified polyphenylene ether resin comprising at least 30% PCR styrenic series resin content. Designed for good dimen..