Polymer Property : Tensile Strength at Break = 42.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	<= 42.0 MPa	<= 6090 psi	ISO/R527
Polykemi AB POLYabs P0P ABS, Plating Grade Information provided by Polykemi AB
Tensile Strength at Break	<= 42.0 MPa	<= 6090 psi	ISO/R527
Polykemi AB POLYabs XX0 ABS, Extrusion Grade Information provided by Polykemi AB
Tensile Strength at Break	42.0 MPa	6090 psi	ISO 527
Nilit FRIANYL C73 HS28 Nylon 6.6/6 for injection molding Nylon 6.6/6 for injection molding, medium viscosity, high impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Strength at Break	42.0 MPa	6090 psi	ASTM D638
3M Dyneon™ PVDF 1008/0001 Polyvinylidene Fluoride (discontinued **) Polyvinylidene Fluoride (PVDF) is ideal for multiple applications across a wide array of industries. Widely used in the chemical process industry, wire and cable industry, semiconductor industry, an..
Tensile Strength at Break	42.0 MPa	6090 psi	ASTM D638
3M Dyneon™ PVDF 1010/0001 Polyvinylidene Fluoride (discontinued **) Polyvinylidene Fluoride (PVDF) is ideal for multiple applications across a wide array of industries. Widely used in the chemical process industry, wire and cable industry, semiconductor industry, an..
Tensile Strength at Break	42.0 MPa	6090 psi	50mm/min; ASTM D638
3M Dyneon™ PVDF 1015/1001 Polyvinylidene Fluoride (discontinued **) Ultra-high molecular weight grade PVDFPowder gradeExcellent chemical resistance to a wide variety of aggressive fluids and solventsGood permeation resistanceExcellent strength and dimensional stabil..
Tensile Strength at Break	42.0 MPa	6090 psi	0.025" extruded film; DIN 53504
Huntsman IROGRANÂ® PS455-200 TPU-Polyester Introduction: IROGRAN PS455-200 is a polyester based thermoplastic polyurethane intended for extrusion applications. IROGRAN PS455-200 is part of the HUNTSMAN film and sheet product range and offers..
Tensile Strength at Break	42.0 MPa	6090 psi	ASTM D638
IRPC Polimaxx Polene GG3245 High Density Polyethylene CHARACTERISTICS: EXCELLENT ENVIRONMENTAL STRESS CRACKING RESISTANCE (ESCR) EXCELLENT IMPACT STRENGTH, GOOD PROCESSABILITY, HIGH TOUGHNESSAPPLICATIONS: BLOW MOLDING/ SHEET/ THERMOFORMING EXTRUSION CO..
Tensile Strength at Break	42.0 MPa	6090 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DL003P PC LNP LUBRICOMP* DL003P is a compound based on Polycarbonate resin containing 15% PTFE. Added features of this material include: Exceptional Processing, Internally Lubricated.
Tensile Strength at Break	42.0 MPa	6090 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP DL003P PC (Asia Pacific) LNP LUBRICOMP* DL003P is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Exceptional Processing.
Tensile Strength at Break	42.0 MPa	6090 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DP003 PC (Asia Pacific) LNP LUBRICOMP* DP003 is a compound based on Polycarbonate resin containing Silicone, PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength at Break	42.0 MPa	6090 psi	50 mm/min; ISO 527
SABIC Innovative Plastics NORYL WCV072 PPE+PP (Asia Pacific) Flexible, halogen free mPPE extrusion grade material for applications such as automotive wire insulation. Low specific gravity with good flame retardant and very good scrape abrasion resistance. De..
Tensile Strength at Break	42.0 MPa	6090 psi	50 mm/min; ISO 527
SABIC Innovative Plastics NORYL WCV072 PPE+PP (Europe-Africa-Middle East) Flexible, halogen free mPPE extrusion grade material for applications such as automotive wire insulation. Low specific gravity with good flame retardant and very good scrape abrasion resistance. De..
Tensile Strength at Break	42.0 MPa	6090 psi	ISO 527 Type 1A
Solvay TECHNYLÂ® C 236SI PA6, Conditioned Description: Unreinforced polyamide 6 with high impact strength for injection molding.Available in: Europe and North AmericaProduct Applications: TECHNYLÂ® C 236SI has high impact strength and fle..
Tensile Strength at Break	42.0 MPa	6090 psi	ISO 527 Type 1A
Solvay TECHNYLÂ® C 536XT PA6, Conditioned Description: TECHNYLÂ® C 536XT is an unreinforced polyamide 6, high viscosity, for extrusion blow molding. This product is available in natural color.Benefits: The product offers a good processing..
Tensile Strength at Break	42.0 MPa	6090 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRILOY Z2000 PPE+PS (Asia Pacific) LNP* Lubriloy* Z2000 is a compound based on PPE+PS Blend resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Tensile Strength at Break	42.0 MPa	6090 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics XenoyÂ® ENH2900 PBT+PC (Asia Pacific) Xenoy* ENH2900 is a Non-Braominated, Non Chlorinated flame retarded PC/PBT resin with good flow, high impact and excellent chemical resistance. It was designed quite suitable for E&E housing applic..
Tensile Strength at Break	42.0 MPa	6090 psi	ASTM D638
SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS LNP* STAT-LOY* AF3009 is a compound based on ABS resin containing 10% Glass Fiber. Added features of this material include: Antistatic, Flame Retardant.
Tensile Strength at Break	42.0 MPa	6090 psi	ISO 527
SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS LNP* STAT-LOY* AF3009 is a compound based on ABS resin containing 10% Glass Fiber. Added features of this material include: Antistatic, Flame Retardant.
Tensile Strength at Break	42.0 MPa	6090 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS (Asia Pacific) LNP* Stat-loy* AF3009 is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber, Flame Retardant. Added features of this material include: Antistat, Flame Retardant.
Tensile Strength at Break	42.0 MPa	6090 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics NORYL PVX516 PPE PREVEX* PVX516 resin is a high flow, non FR grade, 110 C HDT
Tensile Strength at Break	42.0 MPa	6090 psi	ASTM D638
Total PS CPDS 850S Chlorine and Bromine Free Flame Retardant High Impact Polystyrene Total Petrochemicals Polystyrene 850S is a chlorine and bromine free flame retardant high impact polystyrene with excellent thermal stability and processability for injection molding.Suitable Applic..
Tensile Strength at Break	42.0 MPa	6090 psi	ISO 527-2
Total PSC 1540(EU) Crystal Polystyrene 1540 is an easy flowing crystal polystyrene designed for extrusion or injection applications. In extrusion, it improves extruder output and thermoforming cycle times when mixed with a high impact p..
Tensile Strength at Break	42.0 MPa	6090 psi	ISO 527-2
Total PSC 1810/1811 Polystyrene 1811 is a very easy flowing crystal polystyrene designed, principally, for the injection molding industry. The excellent processing characteristics of this grade allows for the production of articl..
Tensile Strength at Break	42.0 MPa	6090 psi	ASTM D638
Braskem HB 0155 HDPE Blow Molding Polyethylene Applications: Large containers from 60 to 200 litersInformation provided by Braskem
Tensile Strength at Break	42.0 MPa	6090 psi	ASTM D638
Aclo Accutech Polypropylene Homopolymer HP0334G15M15CL Glass/Mineral Reinforced Coupled
Tensile Strength at Break	42.0 MPa	6090 psi	ISO 527-2
Ascend Performance Materials Vydyne® 49H NT Nylon 66, Impact Modified, Conditioned Vydyne® 49H NT is general-purpose, impact-modified PA66 resin. Available in natural, it is heat-stabilized for improved resistance to elevated temperatures. The heat-stabilized for improved resista..
Tensile Strength at Break	42.0 - 54.0 MPa	6090 - 7830 psi	5 mm/min.; IS 867-1963
Amity Thermosets ATG 116 Phenolic Molding Organic and inorganic Filler, Compression Molded Characteristics:Medium mechanical strength Medium electrical insulationGeneral purposeColor- BlackMedium flow Applications: Electrical accessories & fittings ( medium quality ) Domestic appliance ha..
Tensile Strength at Break	42.0 MPa	6090 psi	50 mm/min; ISO 527
SABIC Innovative Plastics NORYL PX2060 PPE+PS (Asia Pacific) Noryl* PX2060 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and high flow , this resin also uses non-chlorinated, non-brominated FR ..
Tensile Strength at Break	42.0 MPa	6090 psi	50 mm/min; ISO 527
SABIC Innovative Plastics NORYL RN0612 PPE+HIPS (Europe-Africa-Middle East) Noryl RN0612 is an unfilled Post Consumer recycle (PCR) based injection moldable modified polyphenylene ether resin comprising at least 30% PCR styrenic series resin content. Designed for good dimen..