Polymer Resources PPX-FR1 Modified-PPO, V-0 Flame Retardant

Category	Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Heat Resistant
Manufacturer	Polymer Resources, LTD
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polymer Resources PPX-FR1 Modified-PPO, V-0 Flame Retardant.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Modified-Polyphenylene Oxide, V-0 Flame Retardant, 190F HDTFeatures: • Bromine Free • Chlorine FreeProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.

Physical Properties	Metric	English	Comments
Specific Gravity	1.08 g/cc	1.08 g/cc	ASTM D792
Linear Mold Shrinkage	0.0050 - 0.0070 cm/cm	0.0050 - 0.0070 in/in	ASTM D955
Melt Flow	25 - 50 g/10 min @Load 11.6 kg, Temperature 250 °C	25 - 50 g/10 min @Load 25.6 lb, Temperature 482 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	118	118	ASTM D785
Tensile Strength at Break	41.4 MPa	6000 psi	ASTM D638
Tensile Strength, Yield	44.8 MPa	6500 psi	ASTM D638
Elongation at Break	9.0 %	9.0 %	ASTM D638
Elongation at Yield	3.5 %	3.5 %	ASTM D638
Tensile Modulus	2.41 GPa	350 ksi	ASTM D638
Flexural Strength	89.6 MPa	13000 psi	ASTM D790
Flexural Modulus	2.07 GPa	300 ksi	ASTM D790
Izod Impact, Notched	0.801 J/cm @Temperature -30.0 °C	1.50 ft-lb/in @Temperature -22.0 °F	ASTM D256
	2.67 J/cm @Temperature 22.8 °C	5.00 ft-lb/in @Temperature 73.0 °F	ASTM D256
Izod Impact, Unnotched	6.94 J/cm @Temperature 22.8 °C	13.0 ft-lb/in @Temperature 73.0 °F	ASTM D4812
Charpy Impact, Notched	1.89 J/cm² @Temperature 22.8 °C	9.00 ft-lb/in² @Temperature 73.0 °F	ISO 179/1eA
Gardner Impact	16.9 J	12.5 ft-lb	ASTM D3029

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	87.8 °C	190 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	82.2 °C	180 °F	ASTM D648
Vicat Softening Point	103 °C	218 °F	120°C/h, 50 N; ASTM D1525
UL RTI, Electrical	110 °C @Thickness 1.50 mm	230 °F @Thickness 0.0591 in	UL 746
	110 °C @Thickness 1.70 mm	230 °F @Thickness 0.0669 in	UL 746
	110 °C @Thickness 3.00 mm	230 °F @Thickness 0.118 in	UL 746
UL RTI, Mechanical with Impact	110 °C @Thickness 1.50 mm	230 °F @Thickness 0.0591 in	UL 746
	110 °C @Thickness 1.70 mm	230 °F @Thickness 0.0669 in	UL 746
	110 °C @Thickness 3.00 mm	230 °F @Thickness 0.118 in	UL 746
UL RTI, Mechanical without Impact	95.0 °C @Thickness 1.50 mm	203 °F @Thickness 0.0591 in	UL 746
	95.0 °C @Thickness 1.70 mm	203 °F @Thickness 0.0669 in	UL 746
	95.0 °C @Thickness 3.00 mm	203 °F @Thickness 0.118 in	UL 746
Flammability, UL94	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in
	V-0 @Thickness 3.00 mm	V-0 @Thickness 0.118 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+17 ohm-cm	1.00e+17 ohm-cm	ASTM D257
Dielectric Strength	22.0 kV/mm	560 kV/in	ASTM D149
Comparative Tracking Index	250 - 400 V	250 - 400 V	UL 746
Hot Wire Ignition, HWI	>= 120 sec @Thickness 1.50 mm	>= 120 sec @Thickness 0.0591 in	UL 746
	>= 120 sec @Thickness 1.70 mm	>= 120 sec @Thickness 0.0669 in	UL 746
	>= 120 sec @Thickness 3.00 mm	>= 120 sec @Thickness 0.118 in	UL 746
High Amp Arc Ignition, HAI	60 - 120 arcs @Thickness 1.50 mm	60 - 120 arcs @Thickness 0.0591 in	UL 746
	60 - 120 arcs @Thickness 1.70 mm	60 - 120 arcs @Thickness 0.0669 in	UL 746
	60 - 120 arcs @Thickness 3.00 mm	60 - 120 arcs @Thickness 0.118 in	UL 746
High Voltage Arc-Tracking Rate, HVTR	80.0 - 150 mm/min	3.15 - 5.91 in/min	UL 746

Processing Properties	Metric	English
Rear Barrel Temperature	216 - 266 °C	420 - 510 °F
Middle Barrel Temperature	227 - 271 °C	440 - 520 °F
Front Barrel Temperature	238 - 277 °C	460 - 530 °F
Melt Temperature	246 - 274 °C	475 - 525 °F
Mold Temperature	54.4 - 76.7 °C	130 - 170 °F
Drying Temperature	71.1 - 82.2 °C	160 - 180 °F
Dry Time	3.00 - 4.00 hour	3.00 - 4.00 hour

Descriptive Properties	Value	Comments
Vent	0.001