Lanxess Durethan® BKV 30 W1 000000 Nylon 6, 30% Glass Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Durethan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® BKV 30 W1 000000 Nylon 6, 30% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, Injection molding grade, 30% glass fibers, weather stabilized
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
ISO 1183
Water Absorption 7.0 %
7.0 %
Test Sim. to ISO 62
Moisture Absorption at Equilibrium 2.1 %
2.1 %
23°C/50% R.H.; Test Sim. to ISO 62
Viscosity Test 140 cm³/g
140 cm³/g
Viscosity number; ISO 307, 1157, 1628
Mechanical Properties Metric English Comments
Tensile Strength at Break 110 MPa
16000 psi
Conditioned; ISO 527-1/-2
180 MPa
26100 psi
ISO 527-1/-2
Elongation at Break 3.0 %
3.0 %
ISO 527-1/-2
7.0 %
7.0 %
Conditioned; ISO 527-1/-2
Tensile Modulus 6.10 GPa
885 ksi
Conditioned; ISO 527-1/-2
9.80 GPa
1420 ksi
ISO 527-1/-2
Charpy Impact Unnotched 7.00 J/cm²

@Temperature -30.0 °C
33.3 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
7.00 J/cm²

@Temperature -30.0 °C
33.3 ft-lb/in²

@Temperature -22.0 °F
Conditioned; ISO 179/1eU
8.00 J/cm²

@Temperature 23.0 °C
38.1 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
9.00 J/cm²

@Temperature 23.0 °C
42.8 ft-lb/in²

@Temperature 73.4 °F
Conditioned; ISO 179/1eU
Charpy Impact, Notched 1.00 J/cm²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
1.00 J/cm²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
Conditioned; ISO 179/1eA
1.30 J/cm²

@Temperature 23.0 °C
6.19 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
2.00 J/cm²

@Temperature 23.0 °C
9.52 ft-lb/in²

@Temperature 73.4 °F
Conditioned; ISO 179/1eA
Puncture Energy 8.00 J
5.90 ft-lb
ISO 6603-2
14.0 J
10.3 ft-lb
Conditioned; ISO 6603-2
6.00 J

@Temperature -30.0 °C
4.43 ft-lb

@Temperature -22.0 °F
ISO 6603-2
6.00 J

@Temperature -30.0 °C
4.43 ft-lb

@Temperature -22.0 °F
Conditioned; ISO 6603-2
Tensile Creep Modulus, 1 hour 5100 MPa
740000 psi
ISO 899-1
Tensile Creep Modulus, 1000 hours 4100 MPa
595000 psi
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 µm/m-°C
11.1 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C
44.4 µin/in-°F
ISO 11359-1/-2
Melting Point 222 °C
432 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
ISO 75-1/-2
Vicat Softening Point 200 °C
392 °F
50°C/h 50N; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
IEC 60695-11-10
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
IEC 60695-11-10
Oxygen Index 22 %
22 %
ISO 4589-1/-2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
Conditioned; IEC 60093
1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+12 ohm
1.00e+12 ohm
IEC 60093
Dielectric Constant 4.0

@Frequency 1.00e+6 Hz
4.0

@Frequency 1.00e+6 Hz
Conditioned; IEC 60250
4.0

@Frequency 1.00e+6 Hz
4.0

@Frequency 1.00e+6 Hz
IEC 60250
4.0

@Frequency 100 Hz
4.0

@Frequency 100 Hz
IEC 60250
10

@Frequency 100 Hz
10

@Frequency 100 Hz
Conditioned; IEC 60250
Dielectric Strength 35.0 kV/mm
889 kV/in
Conditioned; IEC 60243-1
40.0 kV/mm
1020 kV/in
IEC 60243-1
Dissipation Factor 0.0050

@Frequency 100 Hz
0.0050

@Frequency 100 Hz
IEC 60250
0.015

@Frequency 1.00e+6 Hz
0.015

@Frequency 1.00e+6 Hz
IEC 60250
0.12

@Frequency 1.00e+6 Hz
0.12

@Frequency 1.00e+6 Hz
Conditioned; IEC 60250
0.20

@Frequency 100 Hz
0.20

@Frequency 100 Hz
Conditioned; IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Descriptive Properties Value Comments
Additives Release agent
Features U.V. stabilized or stable to weather
Form Pellets
ISO Shortname ISO 1874-PA 6,MLR,14-100,GF30
Processing Injection molding