Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 180 MPa | 26100 psi | DIN 53 455 |
Albis Plastics Tedur® L V 9200-1 PPS, 60% Glass Fiber/Mineral
(discontinued **) Mineral-filled Grade with Improved Impact Strength, Low Mold Temp. Incandescent wire resistance (2 mm) is 960°C per VDE 0471 T1.2.Applications: Shaft Seals, FlangesProcessing: Injection Molding (M.. |
|||
Tensile Strength at Break | 180 MPa | 26100 psi | ISO 527-1/-2 |
Lanxess Durethan® AKV 30 HR H2.0 900116 Nylon 66, 30% Glass Fiber PA 66, injection molding grade, 30% glass fibers, hydrolysis stabilized, good heat-ageing resistance |
|||
Tensile Strength at Break | 180 MPa | 26100 psi | ISO 527-1/-2 |
Lanxess Durethan® AKV 30 HR H2.0 901510 Nylon 66, 30% Glass Fiber PA 66, injection molding grade, 30% glass fibers, hydrolysis stabilized, good heat-ageing resistance |
|||
Tensile Strength at Break | 180 MPa | 26100 psi | ISO 527-1/-2 |
Lanxess Durethan® BCF 30 X H2.0 901510 Nylon 6, 30% Glass + Carbon Fiber PA 6, injection molding grade, 30% reinforced (glass fibers + carbon fibers), conductive, intrinsic color black, good heat-ageing resistance |
|||
Tensile Strength at Break | 180 MPa | 26100 psi | d.a.m.; ISO 527-1, -2; 5 mm/min |
Lanxess Durethan® BKV 140 H2.0 DUS008 900051 Nylon 6, Glass Fiber Reinforced, Impact Modified PA 6, 40% glass fibers, injection molding, impact modified, heat-aging stabilizedInformation provided by LANXESS. |
|||
Tensile Strength at Break | 180 MPa | 26100 psi | ISO 527-1/-2 |
Lanxess Durethan® BKV 30 000000 Nylon 6, 30% Glass Fiber 30% Glass fiber reinforced; injection molding grade |
|||
Tensile Strength at Break | 180 MPa | 26100 psi | ISO 527 Type 1A |
Solvay TECHNYLSTARâ„¢ S 216 V30 PA6, 30% glass filled, DRY Description: TECHNYL STAR TM Polyamide, reinforced with 30% of glass fiber, for injection molding. Characterized by a high fluidity of the melt.Available in: Asia Pacific, Europe and North AmericaPr.. |
|||
Tensile Strength at Break | 180 MPa | 26100 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem PW2400 PEI (Europe-Africa-Middle East) 40% Glass fiber filled, standard flow Polyetherimide (Tg 217°C). Product designed and certified for use in Potable Water
applications. KTW, WRAS, ACS certified. NSF61 and W270 pending. US FDA and.. |
|||
Tensile Strength at Break | 180 MPa | 26100 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem HU2400 PEI (Europe-Africa-Middle East) 40% Glass fiber filled, standard flow Polyetherimide (Tg 217C). For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food.. |
|||
Tensile Strength at Break | 180 MPa | 26100 psi | ISO 527-2 |
Tisan TISLAMID® 66 30% Glass Fiber Reinforced Nylon 66 TISLAMID has a wide area of application in electric/electronic, automotive, durable goods and telecommunications industries. It demonstrates characteristics such as Excellent chemical resistanceElec.. |
|||
Tensile Strength at Break | 180 MPa | 26100 psi | ISO 527-93 |
Wellman Wellamid® GF1398 BK12 30% Glass Fiber Reinforced Nylon 66 Description: Glass Fiber Reinforced Nylon 66Information provided by Wellman. |
|||
Tensile Strength at Break | 180 MPa | 26100 psi | ISO 527-93 |
Wellman Wellamid® GF33A099-HRBK Nylon 66, 33% Glass Fiber Reinforced, Hydrolysis Resistant All information provided by Wellman Engineered Resins. |
|||
Tensile Strength at Break | 180 MPa | 26100 psi | ISO 527-93 |
Wellman Wellamid® GF33AO99-HRBK 33% Glass Fiber Reinforced, Hydrolysis Resistant Nylon 66 Description: Glass Fiber Reinforced, Hydrolysis Resistant Nylon 66Information provided by Wellman. |
|||
Tensile Strength at Break | 180 MPa | 26100 psi | ISO 527-93 |
Wellman Wellamid® GF43-66 XE-NBK1 43% Glass Fiber Reinforced, Engineering Grade Nylon 66 Description: Glass Fiber Reinforced, Engineering Grade Nylon 66Information provided by Wellman. |
|||
Tensile Strength at Break | 180 MPa | 26100 psi | ISO 527-1/-2 |
DSM Akulon® K224-G6U (Dry) 33% Glass Reinforced Nylon 6 (North America) Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis.. |
|||
Tensile Strength at Break | 180 MPa | 26100 psi | ISO 527-1/-2 |
DSM Stanyl® TE250F8 Nylon 46-40% Glass Reinforced (European and Asian Grade) (Dry) Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temper.. |
|||
Tensile Strength at Break | 180 MPa | 26100 psi | ISO 527-1/-2 |
DSM Stanyl® TS250F6D Nylon 46-30% Glass Reinforced (Asian Grade) (Dry) Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temper.. |
|||
Tensile Strength at Break | 180 MPa | 26100 psi | ISO 527-1/-2 |
DSM Stanyl® TS256F8 Nylon 46-40% Glass Reinforced (Asian Grade) (Dry) Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temper.. |
|||
Tensile Strength at Break | 180 MPa | 26100 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® LV-65H SST black 9288 PA12-GF65 Product description: Grilamid LV-65H SST black 9288 is a 65% glass fiber reinforced, heat stabilized engineering thermoplastic based on polyamide 12, designed for complex structural parts with the f.. |
|||
Tensile Strength at Break | 180 MPa | 26100 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® TSG-30/4 H black 9836 PA666-GF30 Information provided by EMS Grivory |
|||
Tensile Strength at Break | 180 MPa | 26100 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® XE 5026 (BG-30 H) PA6-GF30 Product description: Grilon B XE 5026 (BG-30 H) black 9922 is a high heat stabilized, 30% glass fiber reinforced PA6- Injection molding grade with modified flowability. Grilon B XE 5026 (BG-30 H) bl.. |
|||
Tensile Strength at Break | 180 MPa | 26100 psi | DAM; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® HTN FG52G35HSL BK011 Polyphthalamide (PPA)
(Unverified Data**) 35% Glass Reinforced PPA High Performance Polyamide Zytel HTNFG52G35HSL BK011 is a 35% glass reinforced lubricated heat stabilized high performance polyamide resin developed for consideration into a.. |
|||
Tensile Strength at Break | 180 MPa | 26100 psi | ISO 527 |
Eurotec® Tecopet® PT74 CR30 BK111 PR PET, 30% carbon fiber reinforced, black, fast crystallization grade Information provided by Eurotec® |
|||
Tensile Strength at Break | 180 MPa | 26100 psi | 5 [mm/min]; ISO 527-1/2 |
Akro-Plastic Akromid® T6 GF30 (3501) PPA Conditioned, 30% Glass Filled The new AKROMID® T is characterized primarily by high heat resistance and the lowest moisture absorption of the three PA grades, making it particularly well-suited in the automotive sector for high.. |
|||
Tensile Strength at Break | 180 MPa | 26100 psi | ISO 527-1/-2 |
DSM Stanyl® TE250F6 Nylon 46-30% Glass Reinforced (European and Asian Grade) (Dry) Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temper.. |
|||
Tensile Strength at Break | 180 MPa | 26100 psi | d.a.m.; ISO 527-1, -2; 5 mm/min |
Lanxess Durethan® BKV 35 CX H2.0 900876 Nylon 6, Glass Fiber Reinforced PA 6, 35% glass fibers, injection molding, heat-aging stabilizedInformation provided by LANXESS. |