Qualchem Danamid FEHUV Polyamide 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Qualchem Zrt. |
| Trade Name | Danamid |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Qualchem Danamid FEHUV Polyamide 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Heat and UV stabilized, for long-lasting use at 120-130°C, protected against artificial lightInformation provided by Qualchem Zrt.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | DIN 53479 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | 50 mm/min; ISO 527-1,2 |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527-1,2 |
| Tensile Modulus | 2.50 GPa | 363 ksi | ISO 527-1,2 |
| Charpy Impact Unnotched | NB @Temperature -20.0 °C |
NB @Temperature -4.00 °F |
DIN 53453 |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature -20.0 °C |
0.952 ft-lb/in² @Temperature -4.00 °F |
DIN 53453 |
| 0.300 J/cm² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 4.00 mm |
HB @Thickness 0.157 in |
MSZ 10383 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Comparative Tracking Index | 600 V | 600 V | IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Moisture Content | 2.5 - 2.7 % | 2.5 - 2.7 % | DIN 53714 |
Users viewing this material also viewed the following:
- GEHR Plastics PVC-ELS Polyvinylchloride, Electrically Conductive Grade
- Monmouth Rubber & Plastics Durafoamâ„¢ N207 100% Neoprene
- Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled
- Silberline SilBerCote® 554-20Y
- Samsung Cheil Industries Starex® NH-1926 HIPS, Unreinforced FR
- Weartech International WT-21 Cobalt Hardfacing & Wear Resistant Alloy
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR Atomite Whiting Filler
- China Tungsten WC 96 Tungsten Carbide Powder
- Chosun Refractories PMCT-165 Special Castable
- CIMBAR Suspengel™ 325 Plus High Purity Bentonite, Industrial Grade