- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 200 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 200 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C @Thickness 3.20 mm |
392 °F @Thickness 0.126 in |
ASTM D648 |
| Ovation Polymers Opnyl OP6GF15 Nylon 6, 15% Glass Reinforced, Dry Nylon 6 - Glass reinforced (15 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. For Nylon compounds the m.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75 |
| Nilit FRIANYL A63 HH-KV20 Nylon 6.6 for injection molding, 20% glass ball reinforced Nylon 6.6 for injection molding, heat and hydrolysis stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75 |
| Nilit FRIANYL B63 KV50 Nylon 6 for injection molding, 50% glass ball reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ASTM D648 |
| RTP Company RTP 2100 LF Z Polyetherimide (PEI) FDA Type - Low Flow
(discontinued **) FDA Type - Low FlowComments:FDA CompliantLow FlowUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Com.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-1/-2 |
| DSM Akulon® K224-PG6U (Dry) 33% Glass Reinforced, Impact Modified Nylon 6 (North America)
(discontinued **)&l Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 200 °C | >= 392 °F | ISO 75-2 |
| Menzolit Menzolit® SMC 0800 Unsaturated Polyester UP SMC 0800 is a special SMC for applications within househould and kitchenware. The glass level has been selected to combine good mouldability with good strength and stiffness properties. The product .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 200 °C | >= 392 °F | ISO 75-2 |
| Menzolit Menzolit® SMC 1400 Unsaturated Polyester UP SMC 1400 is a special SMC being used in the environment of a combustion engine. The glass level has been selected to combine good mouldability with good stiffness and strength properties. The produc.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 200 °C | >= 392 °F | ISO 75-2 |
| Menzolit Menzolit® SMC 1650 Unsaturated Polyester UP SMC 1650 is a specially designed anti-microbial polyester moulding compound which incorporates a "germ killer" . It has been tested and found to be compliant for resistance to fungal defacement in .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ASTM D648 |
| Gromax PBT 4115-104D 15% Glass Fiber Filled Product Description: A glass fiber 15% reinforced injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature Excellent .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-1/-2 |
| Lanxess Pocan® B 3225 XF 000000 PBT, 20% Glass Fiber PBT, 20% glass fibers, injection molding, improved flowability |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-1, -2 |
| Lanxess Pocan® ECO T 3230 000000 PBT + PET, 30% Glass Fiber PBT + PET, 30% glass fibers, injection molding, improved surface finish, contains 30% post-consumer recycled material, increased temperature peak loadInformation provided by LANXESS. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | |
| LATI Latamid SP1 G/30 PA 6.10, 30% Glass Fiber Reinforced Polyamide 6.10 (PA6.10) based compound. Glass fibers. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Indus.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | |
| Lehmann & Voss LUVOCOM® 1106-8154/GY Polyether imide, unreinforced, laser markable Applications: High continuous use and heat distortion temperature. Non flammable.Dynamic stressed parts at high movement velocity.High dimensionally stable precision parts.Information provided by Le.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 200 °C | >= 392 °F | ISO 75-2 |
| Menzolit Menzolit® SMC 2500 Unsaturated Polyester UP SMC 2500 is a special SMC for high voltage isolating applications. The glass level has been selected to combine good mouldability with good strength and stiffness properties. Even without a specific.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ASTM D648 |
| LG Chemical Lupox® GP-2151F General Purpose PBT, 15% Glass Fiber Reinforced, Flame Retardant LUPOX semi-crystalline thermoplastic PBT resins exhibit properties including high strength, rigidity and good resistance to fatigue and creep at elevated temperatures. Furthermore, LUPOX resins sho.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | |
| LATI Latamid 6 CUVHPX10 G/35 PA 6, 30% Glass Fiber Reinforced, Heat Stabilized Polyamide 6 (PA6) based compound. High viscosity. Toughened. Glass fibers. Heat stabilized. UV stabilized. Good elongation.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; No.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C @Thickness 3.20 mm |
392 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP ICL34 PA6.12 LNP* LUBRICOMP* ICL34 is a compound based on Nylon 6/12 containing 20% Carbon Fiber, 15% PTFE. Added features include: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics ULTEM UF5011S PEI (Asia Pacific) Enhanced flow, Specialty filtered Polyetherimide (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics and ketones. ECO Conforming. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Radel® R-7159 Polyphenylsulfone (PPSU) Radel® R-7159 polyphenylsulfone (PPSU) was developed specifically for aircraft interior applications. The product complies with the FAA regulation 14CFR Part 25 Appendix F, offering vertical burn.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C @Thickness 3.20 mm |
392 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® K4560 PBT 30% glass reinforced PBT. Impact modified, high flow, hydrolytically stable. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | Unannealed; ASTM D648 |
| Chase Plastics CP Pryme® N140MGHL (Dry) Nylon 6, 40% Glass Fiber Reinforced, Heat Stabilized, Lubricated Features: Heat StabilizedLubricatedForm: PelletsInformation provided by Chase Plastics. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-93 |
| Wellman Wellamid® MRGF25/15 42H-WBK Nylon 6, 25% Mineral and 15% Glass Fiber Reinforced, Weatherable Grade BlackAll information provided by Wellman Engineered Resins. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-1/-2 |
| DSM Akulon® K224-HG4 Nylon 6-20% Glass Reinforced (European Grade) (Dry) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-1/-2 |
| DSM Akulon® S223-HM8 (Dry) 40% Mineral Reinforced, Heat Stabilized Nylon 66 (North America) Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® 2SV-30H nat PA610-GF30 Product Description: GRILAMID XE3976 natural 9992 is a 30% glass fiber reinforced, heat stabilized polyamide 610 injection molding grade. This product is to a large extent based on renewable raw mat.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Crastin® HR5315HF BK503 Polybutylene Terephthalate (PBT)
(Unverified Data**)& 15% Glass Reinforced Hydrolysis Resistant Polybutylene Terephthalate Crastin HR5315HF is a 15% glass reinforced PBT with high flow (HF) moderately toughened hydrolysis resistant (HR) resin. Excellen.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75 |
| Eurotec® Tecomid® NB40 GR30 NL MB PA6, 30% glass fiber reinforced, impact modified, heat stabilized, natural Information provided by Eurotec® |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-2 |
| BASF Ultradur B 4406 G4 PBT Description: Is a PBT, flame-retardant injection-molding grades, with 20% glass fibers, for parts requiring enhanced fire resistance, e.g. plug-and-socket connectors, housings, coil formers and ligh.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ASTM D648 |
| Asia International Enterprise (Hong Kong) 30G3 Polybutylene terephthalate, 15% Glass Fiber Filled Information provided by Asia International Enterprise (Hong Kong) Ltd. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 - 248 °C | 392 - 478 °F | Average value: 227 °C Grade Count:18 |
| Overview of materials for Polyethylene Terephthalate (PET), 40% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), 40% Glass Reinforced". Specific grades with glass content between 35% .. |
|||