Ineos ABS Lustran® 451 ABS, Injection Molding Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® 451 ABS, Injection Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lustran® ABS 451 is a soft flowing, medium impact injection molding resin designed with a unique balance of impact, heat resistance, flow, and gloss.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM-D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM-D955 |
| Melt Flow | 4.4 g/10 min @Load 3.80 kg, Temperature 230 °C |
4.4 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 107 | 107 | ASTM-D785 |
| Tensile Strength, Yield | 42.7 MPa | 6200 psi | ASTM-D638 |
| Tensile Modulus | 2.62 GPa | 380 ksi | ASTM-D638 |
| Flexural Yield Strength | 74.5 MPa | 10800 psi | ASTM-D790 |
| Flexural Modulus | 2.59 GPa | 375 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.694 J/cm @Thickness 3.17 mm, Temperature -17.8 °C |
1.30 ft-lb/in @Thickness 0.125 in, Temperature 0.000 °F |
ASTM-D256 |
| 1.82 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
3.40 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 82.8 µm/m-°C | 46.0 µin/in-°F | ASTM-D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.6 °C @Thickness 12.7 mm |
177 °F @Thickness 0.500 in |
Unannealed; ASTM-D648 |
| 102 °C @Thickness 12.7 mm |
215 °F @Thickness 0.500 in |
Annealed (24h @ 185°F); ASTM-D648 | |
| Vicat Softening Point | 96.1 °C @Load 1.00 kg |
205 °F @Load 2.20 lb |
120°C/hour; ASTM-D1525 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 232 - 274 °C | 450 - 525 °F | Injection Molding |
| Mold Temperature | 26.7 - 65.6 °C | 80.0 - 150 °F | Injection Molding |
| Drying Temperature | 71.1 - 76.7 °C | 160 - 170 °F | 4 hours |
| 82.2 - 87.8 °C | 180 - 190 °F | 2 hours | |
| Dew Point | <= -28.9 °C | <= -20.0 °F | inlet air |
| Back Pressure | 0.000 - 0.172 MPa | 0.000 - 25.0 psi | Injection Molding |
| Cushion | <= 0.317 cm | <= 0.125 in | Injection Molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed | Moderate to High | Injection Molding |
| Screw Compression Ratio | 2.5:1 | Injection Molding |
| Screw Length-to-Diameter Ratio | >= 20:1 | Injection Molding |
| Screw Speed | Moderate, Injection Molding | |
| Shot Weight-to-Machine Capacity Ratio | 0.5-0.75 | Injection Molding |
Users viewing this material also viewed the following:
- Polykemi AB SCANTEC PC S75R GF30 Polycarbonate, Glass Fiber Reinforced
- Petromont 5001 High Density Polyethylene Resin
- Solvay Specialty Polymers Ryton® R-4-230BL Polyphenylene Sulfide Compound (Unverified Data**)
- Kingfa JH830T Flame Retardant PC
- Lanxess Durethan® AKV 30 HR H2.0 900116 Nylon 66, 30% Glass Fiber
- Techmer ES HiFill® TPX-HTN-01092 A 50% Glass Filled
- Lubrizol ESTANE® 58370 Ether Based Thermoplastic Polyurethane (European Grade)
- Elastocon TPE Technologies Elastocon® 8058BL Thermoplastic Elastomer
- DuPont Performance Polymers Zytel® HTN 51G35HSLR BK420J Polyphthalamide (PPA) (Unverified Data**)
- 3M Scotchcal™ 1000-41 Graphic Film
Copyright © lookpolymers.com All Rights Reserved