Victrex® PEEK 150FW30 PEEK, 30% Carbon Fibre/PTFE Reinforced
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled , Polyetheretherketone, PEEK, PTFE-Filled |
| Manufacturer | Victrex |
| Trade Name | PEEK |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Victrex® PEEK 150FW30 PEEK, 30% Carbon Fibre/PTFE Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description:High performance thermoplastic material, 30% reinforced with carbon fibre / PTFE Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding, easy flow, FDA food contact compliant, colour black.Typical Application Areas:Tribological applications with thin cross sections or long flow lengths for high strength. Excellent wear resistance, very low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments.Information Provided by VICTREX®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | Crystalline; ISO 1183 |
| Water Absorption at Saturation | 0.30 % @Temperature 23.0 °C |
0.30 % @Temperature 73.4 °F |
Equilibrium; by immersion; ISO 62-1 |
| Viscosity | 250000 cP @Temperature 400 °C |
250000 cP @Temperature 752 °F |
melt; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | 360°C nozzle, 160°C tool; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | 385°C nozzle, 180°C tool; ISO 294-4 |
| Spiral Flow | 16.5 cm @Thickness 1.00 mm |
6.50 in @Thickness 0.0394 in |
385°C nozzle, 180°C tool |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 89 @Temperature 23.0 °C |
89 @Temperature 73.4 °F |
ISO 868 |
| Tensile Strength at Break | 115 MPa @Temperature 125 °C |
16700 psi @Temperature 257 °F |
ISO 527 |
| 180 MPa @Temperature 23.0 °C |
26100 psi @Temperature 73.4 °F |
ISO 527 | |
| Elongation at Break | 1.8 % @Temperature 23.0 °C |
1.8 % @Temperature 73.4 °F |
ISO 527 |
| Tensile Modulus | 16.0 GPa @Temperature 23.0 °C |
2320 ksi @Temperature 73.4 °F |
ISO 527 |
| Flexural Strength | 60.0 MPa @Temperature 275 °C |
8700 psi @Temperature 527 °F |
ISO 178 |
| 100 MPa @Temperature 175 °C |
14500 psi @Temperature 347 °F |
ISO 178 | |
| 170 MPa @Temperature 125 °C |
24700 psi @Temperature 257 °F |
ISO 178 | |
| 280 MPa @Temperature 23.0 °C |
40600 psi @Temperature 73.4 °F |
ISO 178 | |
| Flexural Modulus | 14.0 GPa @Temperature 23.0 °C |
2030 ksi @Temperature 73.4 °F |
ISO 178 |
| Compressive Strength | 60.0 MPa @Temperature 200 °C |
8700 psi @Temperature 392 °F |
ISO 604 |
| 155 MPa @Temperature 120 °C |
22500 psi @Temperature 248 °F |
ISO 604 | |
| 210 MPa @Temperature 23.0 °C |
30500 psi @Temperature 73.4 °F |
ISO 604 | |
| Izod Impact, Notched (ISO) | 6.50 kJ/m² @Temperature 23.0 °C |
3.09 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 180/U |
| Charpy Impact Unnotched | 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1U |
| Charpy Impact, Notched | 0.500 J/cm² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 45.0 µm/m-°C @Temperature <=143 °C |
25.0 µin/in-°F @Temperature <=289 °F |
Average below Tg; ISO 11359 |
| 110 µm/m-°C @Temperature >=143 °C |
61.1 µin/in-°F @Temperature >=289 °F |
Average above Tg; ISO 11359 | |
| CTE, linear, Parallel to Flow | 9.00 µm/m-°C @Temperature <=143 °C |
5.00 µin/in-°F @Temperature <=289 °F |
Below Tg; ISO 11359 |
| 9.00 µm/m-°C @Temperature >=143 °C |
5.00 µin/in-°F @Temperature >=289 °F |
Above Tg; ISO 11359 | |
| Melting Point | 343 °C | 649 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 325 °C | 617 °F | ISO 75-f |
| Glass Transition Temp, Tg | 143 °C | 289 °F | Onset; ISO 11357 |
| 147 °C | 297 °F | Midpoint; ISO 11357 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+7 ohm-cm | 1.00e+7 ohm-cm | 1V; IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 100 °C | <= 212 °F | Hopper Temperature |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| 170 - 200 °C | 338 - 392 °F | ||
| Drying Temperature | 120 °C @Time 18000 sec |
248 °F @Time 5.00 hour |
|
| 150 °C @Time 10800 sec |
302 °F @Time 3.00 hour |