Processing Properties | Metric | English | Comments |
---|---|---|---|
Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
Lehmann & Voss LUVOCOM® 1105-7751 PEEK, with carbon fiber, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High-strength and high-stiff parts; low coefficient of expansion.Dynamic stressed parts at.. |
|||
Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
Lehmann & Voss LUVOCOM® 1105-7753/BL PEEK, unreinforced, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistan.. |
|||
Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
Lehmann & Voss LUVOCOM® 1105-8102 PEEK, with PTFE, lubricant modified, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts.Improved friction and wear behaviour. Emergency r.. |
|||
Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
Lehmann & Voss LUVOCOM® 1105-8161 PEEK, with carbon fiber, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts; low thermal coefficient of expansion.Dynamic stressed parts at high m.. |
|||
Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
Lehmann & Voss LUVOCOM® 1105-8173 PEEK, with PTFE Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts, non flammable.Improved friction and wear behavio.. |
|||
Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
Lehmann & Voss LUVOCOM® 1105-8174 PEEK, with PTFE, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts, non flammable.Improved friction and wear behavio.. |
|||
Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
Lehmann & Voss LUVOCOM® 1105-8355 PEEK, with carbon fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High-strength and high-stiff parts; low coefficient of expansion.Dynamic stressed parts at.. |
|||
Drying Temperature | 120 °C @Time 14400 - 21600 sec |
248 °F @Time 4.00 - 6.00 hour |
Dehumidifying dryer |
Lehmann & Voss LUVOCOM® 1850/TF/30 PBT, with PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri.. |
|||
Drying Temperature | 120 °C @Time 14400 - 21600 sec |
248 °F @Time 4.00 - 6.00 hour |
Dehumidifying dryer |
Lehmann & Voss LUVOCOM® 1850-7431 PBT, with carbon fiber and glass spheres Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Low warpage.Low waterabsorbtion, for dimensional stable precision parts.Par.. |
|||
Drying Temperature | 120 °C @Time 14400 - 21600 sec |
248 °F @Time 4.00 - 6.00 hour |
Dehumidifying dryer |
Lehmann & Voss LUVOCOM® 1850-7784 PBT, with glass fiber, glass spheres and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri.. |
|||
Drying Temperature | 120 °C @Time 14400 - 21600 sec |
248 °F @Time 4.00 - 6.00 hour |
Dehumidifying dryer |
Lehmann & Voss LUVOCOM® 1850-7795 PBT, with PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri.. |
|||
Drying Temperature | 120 °C @Time 14400 - 21600 sec |
248 °F @Time 4.00 - 6.00 hour |
Dehumidifying dryer |
Lehmann & Voss LUVOCOM® 1850-8282 PBT, with carbon fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Electrically conductive, suitable for continuous discharging of statically generated electricit.. |
|||
Drying Temperature | 120 °C @Time 7200 - 14400 sec |
248 °F @Time 2.00 - 4.00 hour |
Air-Circulation Dryer |
Lehmann & Voss LUVOCOM® 80-7353/NAT Polyacetal-copolymer, with aramid reinforcement and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.High dimensionally stable prec.. |
|||
Drying Temperature | 120 °C @Time 7200 - 14400 sec |
248 °F @Time 2.00 - 4.00 hour |
Air-Circulation Dryer |
Lehmann & Voss LUVOCOM® 80-8444 Polyacetal-copolymer, unreinforced Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.dynamic stressReduced moment of inertia compared with metal parts.Isotropic shrinkage character.. |
|||
Drying Temperature | 120 °C @Time 14400 sec |
248 °F @Time 4.00 hour |
dehumidifying dryer |
LG Chemical Lupox® GP-2301F General Purpose PBT, 30% Glass Fiber Reinforced, Flame Retardant LUPOX semi-crystalline thermoplastic PBT resins exhibit properties including high strength, rigidity and good resistance to fatigue and creep at elevated temperatures. Furthermore, LUPOX resins sho.. |
|||
Drying Temperature | 120 °C @Time 14400 sec |
248 °F @Time 4.00 hour |
dehumidifying dryer |
LG Chemical Lupox® HI-2302 High Impact PBT, 30% Glass Fiber Reinforced LUPOX semi-crystalline thermoplastic PBT resins exhibit properties including high strength, rigidity and good resistance to fatigue and creep at elevated temperatures. Furthermore, LUPOX resins sho.. |
|||
Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
Lehmann & Voss LUVOCOM® 1105/MS/15/TF/15 PEEK, with PTFE, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts,.. |
|||
Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
Lehmann & Voss LUVOCOM® 1105-0831 PEEK, unreinforced, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High chemical resistance parts, non flammable.Suitable for biocompatible application.Not f.. |
|||
Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
Lehmann & Voss LUVOCOM® 1105-0904/GN PEEK, with glass fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.High dimensionally stable precision parts, high continuous use tempera.. |
|||
Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
Lehmann & Voss LUVOCOM® 1105-0948/YL2 PEEK, with glass fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts; impact resistance.Dynamic stressed parts at high movement velocity.Ch.. |
|||
Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
Lehmann & Voss LUVOCOM® 1105-7107 PEEK, with glass fiber, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts, non flammable.High dimensionally stable precisio.. |
|||
Drying Temperature | 120 °C @Time >=28800 sec |
248 °F @Time >=8.00 hour |
Dehumidifying dryer |
Lehmann & Voss LUVOCOM® 1106-7743 Polyether imide, with PTFE Applications: High continuous use and heat distortion temperature. Non flammable.Dynamic stressed parts at high movement velocity.High dimensionally stable precision parts.Information provided by Le.. |
|||
Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
Lehmann & Voss LUVOCOM® 1105/XCF/15-S PEEK, with carbon fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High-strength and high-stiff parts; low coefficient of expansion.Dynamic stressed parts at.. |
|||
Drying Temperature | 120 °C @Time 21600 sec |
248 °F @Time 6.00 hour |
Horizontal Oven |
Zhejiang Juner PA66-301-G0 Flame-Retardant & Glass Reinforced, Non-Halogen PA66 Applications: Electric Appliance PedestalInformation provided by Zhejiang Juner New Materials Co, Ltd. |
|||
Drying Temperature | 120 °C @Time 18000 sec |
248 °F @Time 5.00 hour |
Chute Hot-Wind |
Zhejiang Juner PA66-301-G20 Flame-Retardant & Glass Reinforced, Environmental PA66 Applications: Framework of CoilsInformation provided by Zhejiang Juner New Materials Co, Ltd. |
|||
Drying Temperature | 120 °C @Time 14400 sec |
248 °F @Time 4.00 hour |
Chute Hot-Wind |
Zhejiang Juner PC-A2-1 Top-Grade Flame Retardant UV-Resistant Applications: Top-Grade Wall Switch, BracketInformation provided by Zhejiang Juner New Materials Co, Ltd. |
|||
Drying Temperature | 120 °C @Time 21600 sec |
248 °F @Time 6.00 hour |
Horizontal Oven |
Zhejiang Juner PC-A7-7 Top-Grade Flame Retardant UV-Resistant Applications: Top-Grade Wall Switch, BracketInformation provided by Zhejiang Juner New Materials Co, Ltd. |
|||
Drying Temperature | 120 °C @Time 14400 sec |
248 °F @Time 4.00 hour |
Chute Hot-Wind |
Zhejiang Juner PC-A1-33 Top-Grade Flame Retardant UV-Resistant Applications: Top-Grade Wall Switch, BracketInformation provided by Zhejiang Juner New Materials Co, Ltd. |
|||
Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
Lehmann & Voss LUVOCOM® 1105-8135/OR PEEK, unreinforced, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistan.. |