Polymer Property : Flexural Strength = 14500 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	100 MPa @Temperature 175 °C	14500 psi @Temperature 347 °F	ISO 178
Victrex® PEEK 150FW30 PEEK, 30% Carbon Fibre/PTFE Reinforced Product Description:High performance thermoplastic material, 30% reinforced with carbon fibre / PTFE Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding, easy flow, FDA fo..
Flexural Strength	100 MPa @Temperature 175 °C	14500 psi @Temperature 347 °F	ISO 178
Victrex® PEEK 150GL20 Polyetheretherketone, 20% Glass Fibre Reinforced Product Description:High performance thermoplastic material, 20% glass fibre reinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding, very easy flow, FDA food conta..
Flexural Strength	100 MPa @Strain 3.50 %, Temperature 23.0 °C	14500 psi @Strain 3.50 %, Temperature 73.4 °F	ISO 178
Victrex® PEEK 450FE20 Polyetheretherketone, 20% PTFE Product Description:High performance thermoplastic material, 20% filled with PTFE Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding and extrusion, standard flow, FDA foo..
Flexural Strength	100 MPa @Temperature 275 °C	14500 psi @Temperature 527 °F	ISO 178
Victrex® PEEK 90HMF20 Polyetheretherketone (PEEK), 20% Carbon Fiber Reinforced Product Description: High performance thermoplastic material, 20% carbon fiber reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection molding, very easy flow, color black.T..
Flexural Strength	100 MPa @Temperature 275 °C	14500 psi @Temperature 527 °F	ISO 178
Victrex® PEEK -HT™ 22CA30 PolyEtherKetone, 30% Carbon Fibre Reinforced Product Description:High performance thermoplastic material, 30% carbon fibre reinforced PolyEtherKetone (PEK), semi crystalline, granules for injection moulding, standard flow, FDA food contact com..
Flexural Strength	100 MPa @Temperature 275 °C	14500 psi @Temperature 527 °F	ISO 178
Victrex® ST™ ST45CA30 PolyEtherKetoneEtherKetoneKetone, 30% Carbon Fibre Reinforced Product Description:High performance thermoplastic material, 30% carbon fibre reinforced PolyEtherKetoneEtherKetoneKetone (PEKEKK), semi crystalline, granules for injection moulding, standard flow, ..
Flexural Strength	100 MPa @Strain 8.00 %	14500 psi @Strain 8.00 %	Conditioned; ISO 178
Lanxess DurethanÂ® BG 30 X H3.0 000000 Nylon 6, 30% Glass Fibers/Glass Spheres PA 6, 30% glass fibers/glass spheres, injection molding, heat-ageing stabilized, low tendency to warp
Flexural Strength	100 MPa @Strain 8.00 %	14500 psi @Strain 8.00 %	cond., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® BG 30 X W1 000000 Nylon 6, Glass Fiber Reinforced PA 6, 30% glass fibers/glass spheres, injection molding, low tendency to warp, weather stabilizedInformation provided by LANXESS.
Flexural Strength	100 MPa @Strain 7.30 %	14500 psi @Strain 7.30 %	cond., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® BKV 15 H2.0 DUS008 901510 Nylon 6, Glass Fiber Reinforced PA 6, 15% glass fibers, injection molding, heat-aging stabilizedInformation provided by LANXESS.
Flexural Strength	100 MPa @Strain 7.30 %	14500 psi @Strain 7.30 %	cond., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® DP 2-2240/15 H2.0 901510 Nylon 66, 15% Glass Fiber PA 66, 15% glass fibers, blow molding, heat-aging stabilized, hydrolysis stabilizedInformation provided by LANXESS.
Flexural Strength	100 MPa @Strain 6.50 %	14500 psi @Strain 6.50 %	Conditioned; ISO 178
Lanxess DurethanÂ® BKV 325 Z H2.0 901510 Nylon 6, 25% Glass Fibers PA 6, 25% glass fibers, blow molding, impact modified, heat-ageing stabilized
Flexural Strength	100 MPa @Temperature -40.0 °C	14500 psi @Temperature -40.0 °F	Practical Use (Water Absorption 3.0%); ASTM-D790
Toyobo GLAMIDE® T-400G15 Nylon-6 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	100 MPa @Temperature 80.0 °C	14500 psi @Temperature 176 °F	Practical Use (Water Absorption 2.5%); ASTM-D790
Toyobo GLAMIDE® T-402 Nylon-6 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	100 MPa @Temperature 80.0 °C	14500 psi @Temperature 176 °F	Practical Use (Water Absorption 2.0%); ASTM-D790
Toyobo GLAMIDE® T-403 Nylon-6 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	100 MPa @Temperature 80.0 °C	14500 psi @Temperature 176 °F	Absolute Drying; ASTM-D790
Toyobo GLAMIDE® T-663G15 Nylon-66 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	100 MPa @Temperature 23.0 °C	14500 psi @Temperature 73.4 °F	Absolute Drying; ASTM-D790
Toyobo GLAMIDE® T-808-02 Nylon-6 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	100 MPa @Thickness >=1.50 mm	14500 psi @Thickness >=0.0591 in	1hr/150°C/measured at 150°C; ISO 178; IEC/EN 60893-2 5.1
Elektro-Isola G-Etronax PM H Polyester, Glass Mat, Creme, Sheets Description: A reasonably-priced alternative to other high-temperature types. Low thermal conductivity. Applications: Used as, among other things, thermal insulation plates where high strength prope..
Flexural Strength	100 MPa @Temperature 23.0 °C	14500 psi @Temperature 73.4 °F	ASTM D790
BASF Ultramid® 8281 HS GP PA6 (Dry) Description: Ultramid 8281 HS GP is an unreinforced, heat stabilized PA6 rot molding compound. It is available in natural and black and can be painted. It exhibits excellent balance of engineering p..
Flexural Strength	100 MPa @Temperature 23.0 °C	14500 psi @Temperature 73.4 °F	Practical Use (Water Absorption 2.8%); ASTM-D790
Toyobo GLAMIDE® T-401 Nylon-6 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..