Polymer Property : Flexural Strength = 170 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	170 MPa @Temperature 125 °C	24700 psi @Temperature 257 °F	ISO 178
Victrex® PEEK 150FW30 PEEK, 30% Carbon Fibre/PTFE Reinforced Product Description:High performance thermoplastic material, 30% reinforced with carbon fibre / PTFE Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding, easy flow, FDA fo..
Flexural Strength	170 MPa @Temperature 23.0 °C	24700 psi @Temperature 73.4 °F	Absolute Drying; ASTM-D790
Toyobo GLAMIDE® T-400G15 Nylon-6 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	170 MPa @Temperature -40.0 °C	24700 psi @Temperature -40.0 °F	Practical Use (Water Absorption 2.1%); ASTM-D790
Toyobo GLAMIDE® T-663G15 Nylon-66 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	170 MPa @Temperature -40.0 °C	24700 psi @Temperature -40.0 °F	Absolute Drying; ASTM-D790
Toyobo GLAMIDE® T-777-02 Nylon-6 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	170 MPa @Temperature -40.0 °C	24700 psi @Temperature -40.0 °F	Absolute Drying; ASTM-D790
Toyobo GLAMIDE® NB-5550 Nylon/Olefin GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	170 MPa @Treatment Temp. 100 °C, Time 3600 sec	24700 psi @Treatment Temp. 212 °F, Time 1.00 hour	ISO 178; IEC/EN 60893-2 5.1
Elektro-Isola G-Etronax PM 953 Polyester, Glass Mat, Off White, Sheets Description: Good electrical properties such as high breakdown voltage in air and oil and highest arc resistance and tracking resistance. Self-extinguishing. Low smoke emission, halogen-free. Very m..
Flexural Strength	170 MPa @Thickness >=1.50 mm	24700 psi @Thickness >=0.0591 in	24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.1
Elektro-Isola G-Etronax PM GPO 3 Polyester, Glass Mat, Red, Sheets Description: Good electrical properties such as high breakdown voltage in air and oil and highest arc resistance and tracking resistance. Self-extinguishing. Low smoke emission, halogen-free.Applica..
Flexural Strength	170 MPa @Treatment Temp. 20.0 °C, Time 3600 sec	24700 psi @Treatment Temp. 68.0 °F, Time 1.00 hour	ISO 178; IEC/EN 60893-2 5.1
Elektro-Isola G-Etronax PM GPO 3 Polyester, Glass Mat, Red, Sheets Description: Good electrical properties such as high breakdown voltage in air and oil and highest arc resistance and tracking resistance. Self-extinguishing. Low smoke emission, halogen-free.Applica..
Flexural Strength	>= 170 MPa @Temperature 150 °C	>= 24700 psi @Temperature 302 °F	Perpendicular to laminations; IEC 1212-2 5.1
Hippe EP GC 203 Woven Glass Cloth Reinforced Epoxy Resin - Sheet Used in mechanical, electrical and electronic applications. Extremely high mechanical strength at moderate temperature. Very good stability of electrical properties under high humidity. High mech..
Flexural Strength	>= 170 MPa @Temperature 150 °C	>= 24700 psi @Temperature 302 °F	Perpendicular to laminations; IEC 1212-2 5.1
Hippe EP GC 204 Woven Glass Cloth Reinforced Epoxy Resin - Sheet Used in mechanical, electrical and electronic applications. Extremely high mechanical strength at moderate temperature. Very good stability of electrical properties under high humidity. High mech..
Flexural Strength	>= 170 MPa @Temperature 150 °C	>= 24700 psi @Temperature 302 °F	Perpendicular to laminations; IEC 1212-2 5.1
Hippe EP GC 205 Woven Glass Cloth Reinforced Epoxy Resin - Sheet Used in mechanical, electrical and electronic applications. Extremely high mechanical strength at moderate temperature. Very good stability of electrical properties under high humidity. High mech..
Flexural Strength	170 MPa @Temperature -40.0 °C	24700 psi @Temperature -40.0 °F	ASTM D790
BASF Ultramid® 8202 L Intermediate PA6 (Dry) Description: Ultramid 8202 L-Intermediate is an unreinforced, low viscosity, non-lubricated PA6 injection molding homopolymer exhibiting excellent melt fluidity for filling thin sections. It is avai..
Flexural Strength	170 MPa @Temperature -40.0 °C	24700 psi @Temperature -40.0 °F	ISO 178
DuPont Performance Polymers Crastin® HR5315HF NC010 PBT (Unverified Data**) Crastin® HR5315HF is a 15% glass reinforced PBT with high flow (HF), moderately toughened, hydrolysis resistant (HR) resin. Excellent balance of properties between terminal pullout and impact resis..
Flexural Strength	170 MPa @Temperature 125 °C	24700 psi @Temperature 257 °F	ISO 178
Victrex® PEEK 650GL30 30% Glass Fiber Filled, PolyEtherEtherKetone High performance thermoplastic material, 30% glass fiber reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection molding and extrusion, low flow, color natural/beige.Typical..