Polymer Property : Flexural Modulus = 2030 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	14.0 GPa	2030 ksi	ISO 178
PolyOne OnForce™ LFT NN-50LGF/000 HS Natural Polyamide 66 (Nylon 66) PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. ..
Flexural Modulus	14.0 - 16.0 GPa	2030 - 2320 ksi	Injection and Compression; ISO 178
Raschig Group 3505 Epoxy Glass-fiber reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. This product meets the allowed..
Flexural Modulus	14.0 - 16.0 GPa	2030 - 2320 ksi	Injection and Compression; ISO 178
Raschig Group 3535 Epoxy Glass fiber-reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties adn dimensional stability even at high temperatures. Form: Low dust granulate pack..
Flexural Modulus	14.0 GPa	2030 ksi	ASTM D790
Premix Premi-Glas® 1281-47 VE SMC Description: Premi-Glas® 1281-47 VE is a sheet molding compound.Market: StructuralInformation provided by Premix.
Flexural Modulus	14.0 - 16.0 GPa	2030 - 2320 ksi	Injection; ISO 178
Raschig Group RALUPOL® 8601 UP Glass-fiber reinforced polyester molding compound. Mold shrinkage similar to phenolic moulding compounds, low post-shrinkage, good electrical values, excellent heat resistance, good mechanical stren..
Flexural Modulus	14.0 GPa	2030 ksi	ISO 178
Celanese VECTRA C130 LCP, 30% Glass Reinforced (Unverified Data**) Has the same excellent balance of properties as A130 with higher temperature capability and easier flow. Slightly more dimensional stability in vapor phase soldering than A130. Suitable for some i..
Flexural Modulus	14.0 GPa	2030 ksi	ISO 178
Celanese VECTRA E115i LCP, 15% Glass Reinforced (Unverified Data**) 15% Glass ReinforcedInformation provided by Celanese
Flexural Modulus	14.0 GPa	2030 ksi
Lehmann & Voss LUVOCOMÂ® 1-7305/BK Polyamide 66, with carbon fiber and glass fiber, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Improved friction and wear beh..
Flexural Modulus	14.0 GPa	2030 ksi
Lehmann & Voss LUVOCOMÂ® 1850-8282 PBT, with carbon fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Electrically conductive, suitable for continuous discharging of statically generated electricit..
Flexural Modulus	14.0 GPa	2030 ksi
Lehmann & Voss LUVOCOMÂ® 19-7277 Polyamide 46, with carbon fiber and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Reduced moment of inertia compared with metal parts.Electrically conductive..
Flexural Modulus	14.0 GPa	2030 ksi
Lehmann & Voss LUVOCOMÂ® 3-8097 Polyamide 6, with glass fiber, thermally conductive modified Applications: Automotive industry, textile machinery, apparatus- and precision engineering.High-strength and stiff parts with low creep.dynamic stressSuitable for metall inserts.Parts for electric a..
Flexural Modulus	14.0 GPa	2030 ksi
Lehmann & Voss LUVOCOMÂ® 50-7844 Polycarbonate, with carbon fiber Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Strong, stiff parts; low thermal coefficient of expansion.Redu..
Flexural Modulus	14.0 GPa	2030 ksi	ASTM D790
IDI Composites C-108 Thermoset Polyester, Molding Vinylester compounds in a range of strengths with superior corrosion resistance.Data provided by the manufacturer.
Flexural Modulus	14.0 GPa	2030 ksi	ASTM D790
IDI Composites E-206 Thermoset Polyester, Sheet ELECTRICAL - U.L. recognized (E53587). Versatile family of compounds designed to meet the most demanding electrical and electronic applications. Excellent dielectric properties and arc/track resista..
Flexural Modulus	14.0 GPa	2030 ksi
Lehmann & Voss LUVOCOMÂ® 1105/XCF/15-S PEEK, with carbon fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High-strength and high-stiff parts; low coefficient of expansion.Dynamic stressed parts at..
Flexural Modulus	14.0 GPa	2030 ksi	ASTM D790
Solvay TECHNYLSTARâ„¢ SX 218 V50 PA6, 50% glass filled, DRY Description: TECHNYLSTARâ„¢ SX 218 V50 is based on a patented high flow polyamide 6 resin (Technylstar), heat stabilized, reinforced with 50% of glass fiber, for injection molding. This product i..
Flexural Modulus	14.0 GPa	2030 ksi	ISO 178
Solvay Specialty Polymers RytonÂ® R-4 Polyphenylene Sulfide (PPS), 40% Glass Fiber RytonÂ® R-4 and R-4-02 40% glass fiber reinforced polyphenylene sulfide compounds provide a good combination of mechanical and electrical properties with outstanding chemical resistance, even at e..
Flexural Modulus	14.0 GPa	2030 ksi	ISO 178
Solvay Specialty Polymers RytonÂ® R-4-240NA Polyphenylene Sulfide (PPS), 40% Glass Fiber RytonÂ® R-4-240NA and R-4-240BL 40% glass fiber reinforced polyphenylene sulfide compounds provide enhanced mechanical strength and toughness compared to other polyphenylene sulfide compounds.Feat..
Flexural Modulus	14.0 GPa	2030 ksi	ISO 178
Solvay Specialty Polymers RytonÂ® R-4-280BL Polyphenylene Sulfide (PPS), Glass Fiber RytonÂ® R-4-280BL 40% glass fiber reinforced polyphenylene sulfide compound provides a combination of enhanced mechanical strength and good flow for injection molding.Features: Good Chemical Resis..
Flexural Modulus	14.0 GPa	2030 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP OF008A PPS - Branched (Europe-Africa-Middle East) LNP* Thermocomp* OF008A is a compound based on PPS - Branched resin containing Glass Fiber.
Flexural Modulus	14.0 GPa	2030 ksi	ISO 178
Polyram PlusTek PB302G50BK39D Nylon 6, 50% Glass Fiber Reinforced, UV and Heat Stabilized 50% Glass fiber reinforced, UV and heat stabilized Nylon 6. Approved and listed by W.R.C. Potable Water and NSF/ANSI 61 International.Information provided by Polyram.
Flexural Modulus	14.0 GPa	2030 ksi
Cytec Thornel® VCK Carbon Cloth Laminate with Mil R-9299 Resin Data provided by the manufacturer, Amoco Performance Products, Inc.Carbon and graphite cloths, consisting entirely of flexible filaments, are produced by pyrolysis of rayon cloth at high temperature..
Flexural Modulus	14.0 GPa	2030 ksi	ISO 178
Celanese Celstran® TPU-GF50-01-US TPU, 50% Glass Reinforced 50% long strand fiber glass reinforced thermoplastic polyurethaneInformation provided by Celanese
Flexural Modulus	14.0 GPa	2030 ksi	ISO 178
Celanese VECTRA E115i LCP, 15% Glass Reinforced 15% glass reinforcedInformation provided by Celanese
Flexural Modulus	14.0 GPa	2030 ksi	DIN 53 457
Albis Plastics Tedur® P 9519 PPS, ~45% Glass Fiber (black only) Compounded Regrind and/or Production Scrap, Excellent Cost-Performance Ratio. Incandescent wire resistance (2 mm) is 960°C per VDE 0471 T1.2.Applications: Handles, Fixing ElementsProcessing: Injec..
Flexural Modulus	14.0 GPa	2030 ksi	ISO 178
Celanese VECTRA A700 LCP, 30% Specialty Some conductivity. Suitable for electrostatic dissipation (ESD) applications. 30% glass reinforced.Information provided by Celanese
Flexural Modulus	14.0 GPa	2030 ksi	ASTM D790
A. Schulman ComAlloy E-16902N PPS Alloy, Electrically Conductive - Stainless Steel Fiber Filled Data provided by the manufacturer, ComAlloy International Company.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Modulus	14.0 GPa	2030 ksi	ISO 178
Celanese FORTRON MT9140L4 PPS, 40% Medical Technology (Unverified Data**) Fortron MT 9140L4 is a 40% glass fiber reinforced injection molding grade that exhibits excellent heat and chemical resistance, inherent flame retardancy, and high hardness and rigidity at elevated..
Flexural Modulus	14.0 GPa	2030 ksi	ISO 178
Celanese Vectra® C130 Liquid Crystal Polymer (LCP), 30% Glass Reinforced Information provided by Celanese Corporation.
Flexural Modulus	14.0 GPa	2030 ksi	ASTM D790
Chevron Phillips Ryton® R-4 04 PPS (Polyphenylene Sulfide) (discontinued **) Ryton® PPS is used in many electronic and automotive applications because of its high strength, favorable electrical properties, and high temperature stability.Data provided by the manufacturer.Sol..