Solvay Specialty Polymers Amodel® AS-4145 HS Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® AS-4145 HS Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel AS-4145 HS polyphthalamide (PPA) is a 45% glass reinforced resin that is hot-water moldable. Key properties include high heat resistance, high strength and stiffness over a broad temperature range, low moisture absorption, excellent chemical resistance and excellent electrical properties. This resin is ideal for automotive electrical and electronic applications, including connectors, sockets, switches and sensors. It is also a good choice for under-hood enclosures that protect critical control systems such as anti-lock brakes, traction control, steering, electronic engine control, transmission and chassis control units. Its rapid crystallization rate and high flow can result in shorter cycles, thereby enhancing molding productivity and lowering costs. - Black: AS-4145 HS BK 324Data is presented for dry polymer unless noted as 'conditioned'.Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.55 g/cc
0.0560 lb/in³
ISO 1183/A
Filler Content 45 %
45 %
Glass Fiber Reinforcement
Water Absorption 0.21 %

@Time 86400 sec
0.21 %

@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 186 MPa
27000 psi
Conditioned; ASTM D638
224 MPa
32500 psi
ISO 527-2
228 MPa
33100 psi
ASTM D638
Elongation at Break 2.1 %
2.1 %
Conditioned; ASTM D638
2.2 %
2.2 %
ISO 527-2
2.4 %
2.4 %
ASTM D638
Tensile Modulus 15.2 GPa
2200 ksi
Conditioned; ASTM D638
15.2 GPa
2200 ksi
ASTM D638
16.1 GPa
2340 ksi
ISO 527-2
Flexural Strength 327 MPa
47400 psi
ISO 178
Flexural Yield Strength 269 MPa
39000 psi
Conditioned; ASTM D790
328 MPa
47600 psi
ASTM D790
Flexural Modulus 13.1 GPa
1900 ksi
ASTM D790
13.1 GPa
1900 ksi
Conditioned; ASTM D790
13.4 GPa
1940 ksi
ISO 178
Compressive Strength 159 MPa
23100 psi
Conditioned; ASTM D695
172 MPa
24900 psi
ASTM D695
Poissons Ratio 0.40
0.40
ASTM E132
Shear Modulus 5.43 - 5.75 GPa
788 - 834 ksi
Calculated
Shear Strength 75.8 MPa
11000 psi
Conditioned; ASTM D732
89.6 MPa
13000 psi
ASTM D732
Izod Impact, Notched 0.960 J/cm
1.80 ft-lb/in
Conditioned; ASTM D256
1.00 J/cm
1.87 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched 6.30 J/cm²
30.0 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 13.0 µm/m-°C

@Temperature 149 - 249 °C
7.22 µin/in-°F

@Temperature 300 - 480 °F
TMA; ASTM E831
16.0 µm/m-°C

@Temperature 0.000 - 90.0 °C
8.89 µin/in-°F

@Temperature 32.0 - 194 °F
TMA; ASTM E831
CTE, linear, Transverse to Flow 59.0 µm/m-°C

@Temperature 0.000 - 90.0 °C
32.8 µin/in-°F

@Temperature 32.0 - 194 °F
ASTM E831
110 µm/m-°C

@Temperature 149 - 249 °C
61.1 µin/in-°F

@Temperature 300 - 480 °F
ASTM E831
Melting Point 320 °C
608 °F
ISO 11357-3
320 °C
608 °F
ASTM D570
Maximum Service Temperature, Air 210 °C

@Time 4.32e+6 sec
410 °F

@Time 1200 hour
Continuous; ASTM D3045
Deflection Temperature at 0.46 MPa (66 psi) 320 °C

@Thickness 3.18 mm
608 °F

@Thickness 0.125 in
Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 298 °C
568 °F
Unannealed; ISO 75-2/A
300 °C

@Thickness 3.18 mm
572 °F

@Thickness 0.125 in
Annealed; ASTM D648
Flammability, UL94 HB

@Thickness 3.18 mm
HB

@Thickness 0.125 in
UL 94
Electrical Properties Metric English Comments
Volume Resistivity 6.00e+14 ohm-cm
6.00e+14 ohm-cm
Conditioned; ASTM D257
8.00e+15 ohm-cm
8.00e+15 ohm-cm
ASTM D257
Dielectric Constant 3.7

@Frequency 1.00e+6 Hz
3.7

@Frequency 1.00e+6 Hz
ASTM D150
4.0

@Frequency 1.00e+6 Hz
4.0

@Frequency 1.00e+6 Hz
Conditioned; ASTM D150
4.0

@Frequency 60.0 Hz
4.0

@Frequency 60.0 Hz
ASTM D150
4.9

@Frequency 60.0 Hz
4.9

@Frequency 60.0 Hz
Conditioned; ASTM D150
Dielectric Strength 24.0 kV/mm

@Thickness 1.59 mm
610 kV/in

@Thickness 0.0626 in
ASTM D149
25.0 kV/mm

@Thickness 1.59 mm
635 kV/in

@Thickness 0.0626 in
Conditioned; ASTM D149
Dissipation Factor 0.0040

@Frequency 60.0 Hz
0.0040

@Frequency 60.0 Hz
ASTM D150
0.011

@Frequency 1.00e+6 Hz
0.011

@Frequency 1.00e+6 Hz
ASTM D150
0.024

@Frequency 60.0 Hz
0.024

@Frequency 60.0 Hz
Conditioned; ASTM D150
0.037

@Frequency 1.00e+6 Hz
0.037

@Frequency 1.00e+6 Hz
Conditioned; ASTM D150
Comparative Tracking Index 600 V
600 V
UL 746
600 V
600 V
Conditioned; UL 746
High Voltage Arc-Tracking Rate, HVTR 13.0 mm/min
0.512 in/min
UL 746
14.0 mm/min
0.551 in/min
Conditioned; UL 746
Processing Properties Metric English Comments
Feed Temperature 79.4 °C
175 °F
Hopper Temperature
Rear Barrel Temperature 318 - 324 °C
604 - 615 °F
Front Barrel Temperature 327 - 332 °C
621 - 630 °F
Melt Temperature 329 - 343 °C
624 - 649 °F
Mold Temperature 65.6 - 93.3 °C
150 - 200 °F
Drying Temperature 121 °C
250 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content 0.10 %
0.10 %
Descriptive Properties Value Comments
Additive Heat Stabilizer
Lubricant
Mold Release
Appearance Black
Automotive Specifications ASTM D6779 PA102G45
TYCO 100-1632 Color: BK-324 Black
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Fast Molding Cycle
Good Chemical Resistance
Good Creep Resistance
Good Dimensional Stability
Good Stiffness
Heat Stabilized
High Heat Resistance
High Strength
Hot Water Moldability
Low Moisture Absorption
Lubricated
Forms Pellets
Generic PPA
Processing Method Water-Heated Mold Injection Molding
RoHS Compliance RoHS Compliant
Uses Abrasive Cleaning Material