Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 320 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	320 °C @Thickness 3.20 mm	608 °F @Thickness 0.126 in	Annealed; ASTM D648
Solvay Specialty Polymers Amodel® AS-4133 HS Polyphthalamide (PPA) (Unverified Data**) Amodel AS-4133 HS is a 33% glass reinforced, lubricated, heat stabilized grade of polyphthalamide (PPA) that offers fast cycle times and moldability in hot water molds. Typical applications include ..
Deflection Temperature at 0.46 MPa (66 psi)	320 Â°C @Thickness 3.20 mm	608 Â°F @Thickness 0.126 in	Annealed; ASTM D648
Solvay Specialty Polymers AmodelÂ® AS-4133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry) AmodelÂ® AS-4133 HS is a 33% glass reinforced, lubricated, heat stabilized grade of polyphthalamide (PPA) that offers fast cycle times and moldability in hot water molds. Testing conducted on samp..
Deflection Temperature at 0.46 MPa (66 psi)	320 Â°C @Thickness 3.20 mm	608 Â°F @Thickness 0.126 in	Annealed; ASTM D648
Solvay Specialty Polymers AmodelÂ® AS-4133 L Polyphthalamide (PPA), 33% Glass Fiber (Dry) AmodelÂ® AS-4133 L polyphthalamide (PPA) a 33% glass reinforced, lubricated, structural grade of polyphthalamide (PPA) that offers fast cycle times and is hot water moldable. Typical applications ..
Deflection Temperature at 0.46 MPa (66 psi)	320 Â°C @Thickness 3.20 mm	608 Â°F @Thickness 0.126 in	Annealed; ASTM D648
Solvay Specialty Polymers AmodelÂ® AS-4145 HS Polyphthalamide (PPA), 45% Glass Fiber (Dry) AmodelÂ® AS-4145 HS polyphthalamide (PPA) is a 45% glass reinforced resin that is hot-water moldable. Key properties include high heat resistance, high strength and stiffness over a broad tempera..
Deflection Temperature at 0.46 MPa (66 psi)	320 °C @Thickness 3.18 mm	608 °F @Thickness 0.125 in	Annealed; ASTM D648
Solvay Specialty Polymers Amodel® AS-4133 L Polyphthalamide (PPA) (Unverified Data**) Amodel AS-4133 L polyphthalamide (PPA) a 33% glass reinforced, lubricated, structural grade of polyphthalamide (PPA) that offers fast cycle times and is hot water moldable. Typical applications incl..
Deflection Temperature at 0.46 MPa (66 psi)	320 °C @Thickness 3.20 mm	608 °F @Thickness 0.126 in	Annealed; ASTM D648
Solvay Specialty Polymers Amodel® AS-4133 HN Polyphthalamide (PPA), Dry, 33% Glass Fiber Reinforcement, Heat Stabilizer Amodel AS-4133 HN polyphthalamide (PPA) is a non-lubricated, heat stabilized grade that offers fast cycle times and is hot-water moldable. Typical applications include electrical and electronic comp..
Deflection Temperature at 0.46 MPa (66 psi)	320 °C @Thickness 3.18 mm	608 °F @Thickness 0.125 in	Annealed; ASTM D648
Solvay Specialty Polymers Amodel® AS-4145 HS Polyphthalamide (PPA) (Unverified Data**) Amodel AS-4145 HS polyphthalamide (PPA) is a 45% glass reinforced resin that is hot-water moldable. Key properties include high heat resistance, high strength and stiffness over a broad temperature..
Deflection Temperature at 0.46 MPa (66 psi)	320 °C @Thickness 3.20 mm	608 °F @Thickness 0.126 in	Annealed; ASTM D648
Solvay Specialty Polymers Amodel® A-4133 L Polyphthalamide (PPA), Dry (discontinued **) Amodel A-4133L polyphthalamide (PPA) is a 33% glass reinforced resin designed to offer high crystallinity when molded in water-cooled molds. Key properties include high heat resistance, reduced outg..