SABIC Innovative Plastics Valox® DR51 PBT (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® DR51 PBT (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
VALOX DR51 is a 15% glass fiber reinforced PBT injection moulding resin with excellent mechanical, thermal and electrical performance. Applications: spotlights, appliance housings, handles.
Physical Properties Metric English Comments
Specific Gravity 1.45 g/cc
1.45 g/cc
ASTM D792
Density 1.45 g/cc
0.0524 lb/in³
ISO 1183
Filler Content 17 %
17 %
ASTM D229
Water Absorption 0.070 %

@Time 86400 sec
 0.070 %

@Time 24.0 hour
 ASTM D570
Moisture Absorption 0.0700 %
0.0700 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.20 %
0.20 %
ISO 62
Viscosity 170000 cP
170000 cP
Melt Viscosity, 260°C, 1500 sec-1; ISO 11443
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm
0.0050 - 0.0080 in/in
on Tensile Bar; SABIC Method
0.0040 - 0.0060 cm/cm

@Thickness 1.50 - 3.20 mm
 0.0040 - 0.0060 in/in

@Thickness 0.0591 - 0.126 in
 SABIC Method
0.0060 - 0.0090 cm/cm

@Thickness 3.20 - 4.60 mm
 0.0060 - 0.0090 in/in

@Thickness 0.126 - 0.181 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0060 - 0.0090 cm/cm
0.0060 - 0.0090 in/in
on Tensile Bar; SABIC Method
0.0050 - 0.0080 cm/cm

@Thickness 1.50 - 3.20 mm
 0.0050 - 0.0080 in/in

@Thickness 0.0591 - 0.126 in
 SABIC Method
0.0080 - 0.011 cm/cm

@Thickness 3.20 - 4.60 mm
 0.0080 - 0.011 in/in

@Thickness 0.126 - 0.181 in
 SABIC Method
Melt Flow 18 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 18 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 ISO 1133
80 g/10 min

@Load 5.00 kg,
Temperature 265 °C
 80 g/10 min

@Load 11.0 lb,
Temperature 509 °F
 ASTM D1238
Melt Index of Compound 15 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 15 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
43 g/10 min

@Load 5.00 kg,
Temperature 250 °C
 43 g/10 min

@Load 11.0 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
65 g/10 min

@Load 5.00 kg,
Temperature 265 °C
 65 g/10 min

@Load 11.0 lb,
Temperature 509 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 118
118
ASTM D785
120
120
ISO 2039-2
Hardness, H358/30 100 MPa
14500 psi
ISO 2039-1
Tensile Strength at Break 90.0 MPa
13100 psi
Type I, 5 mm/min; ASTM D638
100 MPa
14500 psi
5 mm/min; ISO 527
Tensile Strength, Yield 90.0 MPa
13100 psi
Type I, 5 mm/min; ASTM D638
95.0 MPa
13800 psi
5 mm/min; ISO 527
Elongation at Break 3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
3.0 %
3.0 %
5 mm/min; ISO 527
5.0 %
5.0 %
Flexural Strain, break, 2 mm/min; ISO 178
Elongation at Yield 3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
3.0 %
3.0 %
5 mm/min; ISO 527
Tensile Modulus 5.90 GPa
856 ksi
5 mm/min; ASTM D638
6.00 GPa
870 ksi
1 mm/min; ISO 527
Flexural Strength 140 MPa
20300 psi
1.3 mm/min, 50 mm span; ASTM D790
155 MPa
22500 psi
2 mm/min; ISO 178
Flexural Yield Strength 140 MPa
20300 psi
1.3 mm/min, 50 mm span; ASTM D790
150 MPa
21800 psi
2 mm/min; ISO 178
Flexural Modulus 4.50 GPa
653 ksi
1.3 mm/min, 50 mm span; ASTM D790
5.10 GPa
740 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.400 J/cm
0.749 ft-lb/in
ASTM D256
0.400 J/cm

@Temperature 0.000 °C
 0.749 ft-lb/in

@Temperature 32.0 °F
 ASTM D256
0.400 J/cm

@Temperature -30.0 °C
 0.749 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Unnotched 3.30 J/cm
6.18 ft-lb/in
ASTM D4812
3.30 J/cm

@Temperature -30.0 °C
 6.18 ft-lb/in

@Temperature -22.0 °F
 ASTM D4812
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
4.00 kJ/m²

@Temperature 0.000 °C
 1.90 ft-lb/in²

@Temperature 32.0 °F
 80*10*4; ISO 180/1A
4.00 kJ/m²

@Temperature -20.0 °C
 1.90 ft-lb/in²

@Temperature -4.00 °F
 80*10*4; ISO 180/1A
4.00 kJ/m²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
4.00 kJ/m²

@Temperature -40.0 °C
 1.90 ft-lb/in²

@Temperature -40.0 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 30.0 kJ/m²
14.3 ft-lb/in²
80*10*4; ISO 180/1U
30.0 kJ/m²

@Temperature -30.0 °C
 14.3 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1U
Charpy Impact Unnotched 3.00 J/cm²
14.3 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eU
3.00 J/cm²
14.3 ft-lb/in²
ISO 179/2C
2.70 J/cm²

@Temperature -30.0 °C
 12.8 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/2C
3.00 J/cm²

@Temperature -30.0 °C
 14.3 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
ISO 179/2C
0.500 J/cm²
2.38 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.400 J/cm²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.400 J/cm²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/2C
Taber Abrasion, mg/1000 Cycles 16
16
CS-17, 1 kg; SABIC Method
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
ASTM D257
>= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 2.9

@Frequency 1.00e+6 Hz
 2.9

@Frequency 1.00e+6 Hz
 IEC 60250
3.0

@Frequency 50.0 - 60.0 Hz
 3.0

@Frequency 50.0 - 60.0 Hz
 IEC 60250
3.4

@Frequency 1.00e+6 Hz
 3.4

@Frequency 1.00e+6 Hz
 ASTM D150
3.6

@Frequency 100 Hz
 3.6

@Frequency 100 Hz
 ASTM D150
Dielectric Strength 18.0 kV/mm

@Thickness 3.20 mm
 457 kV/in

@Thickness 0.126 in
 in oil; IEC 60243-1
19.6 kV/mm

@Thickness 3.20 mm
 498 kV/in

@Thickness 0.126 in
 in air; ASTM D149