- Polymer Property : Tensile Strength at Break = 100 MPa
Polymer Property : Tensile Strength at Break = 100 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | STN EN ISO 527-2 |
| Plastcom SLOVALEN PH 49 GF 50 Polypropylene Homopolymer, 50% Glass Fiber FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 50% glass fiber, contains the modifier of mechanical properties. Increased strength in comparison with unfilled PP.. |
|||
| Tensile Strength at Break | 100 MPa | 14500 psi | STN EN ISO 527-2 |
| Plastcom SLOVALEN PH 69 GF 40 Polypropylene Homopolymer, 40% Glass Fiber FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 40% glass fiber, contains the modifier of mechanical properties. Increased strength in comparison with unfilled PP.. |
|||
| Tensile Strength at Break | 100 MPa | 14500 psi | ASTM D638 |
| Celanese Celanex® 3216 PBT, 15% Glass Reinforced
(Unverified Data**) Celanex 3216 is a non-exuding (UL and CSA approved V-0 at 1/32 inch and 5V at 1/8 inch ),15% fiberglass reinforced polybutylene terephthalate which has an excellent balance of mechanical properties .. |
|||
| Tensile Strength at Break | 100 MPa | 14500 psi | 5mm/min; ISO 527-2/1A |
| Celanese Celanex® 3216 PBT, 15% Glass Reinforced
(Unverified Data**) Celanex 3216 is a non-exuding (UL and CSA approved V-0 at 1/32 inch and 5V at 1/8 inch ),15% fiberglass reinforced polybutylene terephthalate which has an excellent balance of mechanical properties .. |
|||
| Tensile Strength at Break | 100 MPa | 14500 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP DFL16E PC (Asia Pacific) LNP* Lubricomp* DFL16E is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Easy Molding. |
|||
| Tensile Strength at Break | 100 MPa | 14500 psi | ASTM D638 |
| Ravago Manufacturing Americas Hylon® N1033STL Nylon 6/6 (Cond)
(discontinued **) Information provided by Ravago. |
|||
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527-1/-2 |
| DSM Akulon® K230-HXG6 Nylon 6-30% Glass Reinforced (European Grade) (Cond)
(discontinued **) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527-1/-2 |
| DSM Akulon® Ultraflow™ K-FKGS6 Nylon 6-30% Glass Reinforced (European and Asian Grade) (Cond)
(discontinued * The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527-1/-2 |
| Lanxess Pocan® TP 740-101 000000 PBT + ASA, 15% Glass Fiber PBT+ASA, 15% glass fibers, injection molding, low tendency to warp, improved surface finish |
|||
| Tensile Strength at Break | 100 MPa | 14500 psi | 5 mm/min; ASTM D638 |
| Lavergne VYPET VNT 615 HP PET 15% Glass Reinforced Vypet VNT 615HP is a modified 15% fiberglass reinforced PET injection molding compound designed for automotive structural applications.Features: Easy, fast processing; Excellent strength and stiffne.. |
|||
| Tensile Strength at Break | 100 MPa | 14500 psi | Conditioned; ISO 527-1/-2 |
| Lanxess Durethan® BKV 330 H2.0 901510 Nylon 6, 30% Glass Fiber PA 6, injection molding type, 30% glass fibers, branched/structural viscosity, good weldability (vibration or hot plate), good heat-ageing resistance |
|||
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 Type 1A |
| Solvay TECHNYL® A 218 V20 Black 21N PA66, 20% glass fiber, Conditioned Description: Polyamide PA66, reinforced with 20% of glass fiber, heat stabilized, for injection molding.Available in: EuropeProduct Applications: TECHNYL A 218 V20 is used in all sectors of industry.. |
|||
| Tensile Strength at Break | 100 MPa | 14500 psi | ASTM D638 |
| SABIC Innovative Plastics LNP STAT-KON DE002ER PC (Asia Pacific) LNP STAT-KON* DE002ER is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Easy Molding. |
|||
| Tensile Strength at Break | 100 MPa | 14500 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Noryl GTX GTX8710 PPE+PA Noryl GTX8710 resin is a glass filled, high performance blend of PPE/PA that exhibits an exceptional balance of high-heat resistance, strength, flow, and conductivity. This grade can be electro-sta.. |
|||
| Tensile Strength at Break | 100 MPa | 14500 psi | ASTM D638 |
| SABIC Innovative Plastics LNP STAT-KON DEL22P PC (Asia Pacific) LNP STAT-KON* DEL22P is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
| Tensile Strength at Break | 100 MPa | 14500 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL GFN3V PPE+HIPS (Europe-Africa-Middle East) NORYL GFN3V is a 30 % glass fibre reinforced material with a HDT/A of 145C according ISO 75. NORYL GFN3V has been approved for potable water applications up to 85C by the UK WFBS according BS 6920 i.. |
|||
| Tensile Strength at Break | 100 MPa | 14500 psi | ASTM D 638 |
| RTP Company RTP 1379 Polyphenylene Sulfide (PPS), Glass Fiber - Mineral |
|||
| Tensile Strength at Break | 100 MPa | 14500 psi | ASTM D 638 |
| RTP Company RTP 201 A Nylon 6 (PA), Glass Fiber |
|||
| Tensile Strength at Break | 100 MPa | 14500 psi | ASTM D 638 |
| Cossa Polimeri ESTAPROP H 0580 GFC Polypropylene, 40% Glass Filled PP homopolymer 40% chemically coupled glass fiberExcellent stiffness, excellent impact strengthInformation provided by Cossa Polimeri S.r.l. |
|||
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527-1/-2 |
| DSM Stanyl® TS250F4D Nylon 46-40% Glass Reinforced (Asian Grade) (Cond) Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temper.. |
|||
| Tensile Strength at Break | 100 MPa | 14500 psi | 5 mm/min; ISO 527 |
| CP-Polymer-Technik Wellamid® 6000/58 GV 15 HWUVCP 15% Glass Fiber Nylon 6, Impact Modified Until -40°C, UV Stabilized, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
| Tensile Strength at Break | 100 MPa | 14500 psi | DAM; ISO 527-1/-2 |
| DuPont Performance Polymers Zytel® BM73G15THS BK317 Nylon 6
(Unverified Data**) 15% Glass Reinforced Heat Stabilized Polyamide 6 Zytel BM73G15THS is a 15% glass fiber reinforced heat stabilized lubricated toughened polyamide 6 for blow molding.Information provided by DuPont Per.. |
|||
| Tensile Strength at Break | 100 MPa | 14500 psi | 50%RH; ISO 527-1/-2 |
| DuPont Performance Polymers Zytel® HTN 54G15HSLR NC010 Polyphthalamide (PPA)
(Unverified Data**) 15% Glass Reinforced Toughened PPA High Performance Polyamide Zytel HTN54G15HSLR NC010 is a 15% glass reinforced toughened heat stabilized hydrolysis resistant high performance polyamide resin. It i.. |
|||
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 |
| Eurotec® Tecodur® PB70 GR15 NL100 KA01 PBT/PET, 15% glass fiber reinforced, heat stabilized, natural, gas injection grade Information provided by Eurotec® |
|||
| Tensile Strength at Break | 100 MPa @Temperature 140 - 150 °C, Time 7.20e+7 sec |
14500 psi @Temperature 284 - 302 °F, Time 20000 hour |
5 [mm/min], 50% Loss of Tensile Strength; ICE 216 |
| Akro-Plastic Akroloy® PA GF 40 (2845) PA 6.6 & PA6I/6T Conditioned, 40% Glass Filled One of the most characteristic properties of polyamide (PA 6.6) is the absorption of moisture. This essentially leads to increased toughness and elongation at break, to name the most important param.. |
|||
| Tensile Strength at Break | 100 MPa @Temperature 160 - 175 °C, Time 1.80e+7 sec |
14500 psi @Temperature 320 - 347 °F, Time 5000 hour |
5 [mm/min], 50% Loss of Tensile Strength; ICE 216 |
| Akro-Plastic Akromid® A3 GF 30 (2397) PA 6.6 Dry, 30% Glass Filled AKROMID® A (Polyamide 6.6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperat.. |
|||
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 |
| Celanese Thermx® CG923 NC010 PCT Thermx® CG923 NC010 is a 20% glass fiber reinforced, flame retardant polycyclohexylenedimethylene terephthalate resin for injection molding.Celenese acquired the Thermx product line from DuPont in .. |
|||
| Tensile Strength at Break | 100 MPa | 14500 psi | ASTM D638 |
| Beijing Chemical Industry KAIFA® MN201-G20 Nylon 66 Resin 20% glass fiber reinforced, thermal resistantInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
| Tensile Strength at Break | 100 MPa | 14500 psi | ASTM D638 |
| Sumitomo Bakelite North America TEM 9053C Hardware Grade Epoxy Short fiberglass and mineral filled, toughened epoxy molding compound with excellent dimensional stability and high strength properties.Information provided by Vyncolit, a Sumitomo Bakelite Group |
|||