Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics EXTEM VH1003 PEI Copolymer (Asia Pacific) Transparent, Thermoplastic Polyimide (TPI) resin. Glass transition Temp. (Tg) of 247°C. This resin has thinwall FR capability and has a UL94 V0 listing. Resin is RoHS compliant and halogen free acc.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics EXTEM VH1003F PEI Copolymer Transparent, Thermoplastic Polyimide (TPI) resin with a glass transition temperature (Tg) of 247C. This product has thinwall FR capability and has a UL94 V0 listing. This material is RoHS compliant.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics EXTEM VH1003P PEI Copolymer (Europe-Africa-Middle East) Transparent, Thermoplastic Polyimide (TPI) resin with a glass transition temperature (Tg) of 247C. Powder version of VH1003. This resin is a Dual-use item and is subject to export control restrictio.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527-1/2 |
Radici Radilon® SRCP3010LK (dry) Nylon 6 Heat stabilized glass-fiber reinforced and mineral reinforcedInformation provided by Radici group. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527 |
Victrex® PEEK 600G Polyetheretherketone
(discontinued **) Product Description: High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, low viscosity, FDA food conta.. |
|||
Tensile Strength, Yield | 95.1 MPa @Thickness 3.20 mm |
13800 psi @Thickness 0.126 in |
ASTM D638 |
LG Chemical LUMILOY GP2200 Injection Molding Grade, General Purpose 20% Glass Reinforced PPE NSF Certified for KA02 and E2035. Noted for High Flow, High Impact Strength, and Hydrolytic Stability. Uses include electric/electronic parts and water pump Housing or impellers and other parts wi.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527 type 1 A |
Solvay TECHNYL® A 222 Black 1N PA66, DRY Description: Unreinforced polyamide PA66, medium viscosity, heat stabilized, for injection molding, fast crystallization, for short cycles .Available in: EuropeProduct Applications: TECHNYL A 222 of.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO-DIS 527 |
Schwartz Technical Plastics LAMIGAMID® 319 Cast Polyamide 6, Oil Filled, Dry Application: sheaves and wheels without additional bearings, sliding linersInformation provided by Schwartz Technical Plastics GmbH |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM 4001 PEI (Europe-Africa-Middle East) PTFE filled, standard flow Polyetherimide (Tg 217C). Resin is RoHS compliant. UL94 V0 and 5VA listing. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem HATX200 PEI+PCE (Asia Pacific) High flow Polyetherimide blend. ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compli.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem HATX200 PEI+PCE (Europe-Africa-Middle East) High flow Polyetherimide blend. ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compli.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM HU1004 PEI (Europe-Africa-Middle East) High Temperature, Transparent, Polyetherimide Blend with Improved Ductility and Enhanced Hydrostability. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI) and FDA and EUFC f.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem XH6050 PEI Copolymer (Europe-Africa-Middle East) Transparent, enhanced flow Polyetherimidesulfone copolymer (Tg 247C). ECO Conforming, UL94 V0 listing. Resin is subject to U.S. Commerce Control Laws (15CFR Chapter VII, Part 774).This data was su.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | Type 1A, 50 mm/min; ISO 527-2 |
Solvay Specialty Polymers KetaSpire® KT-851 Polyetheretherketone (PEEK) KetaSpire® KT-851 resin is a depth-filtered grade of polyetheretherketone (PEEK) specially designed for use in extruded wire insulation coating. KT-851 offers the needed balance of properties and.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® IQ8280SF PBT+PET (Europe-Africa-Middle East) Valox iQ8280SF resin is an environmentally responsible, low carbon footprint, and sustainable resin. Valox iQ8280SF resin offer Super High Flow characteristics combined with high modulus and excell.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Thermocomp PX05046 PA 6 (Europe-Africa-Middle East) LNP* THERMOCOMP* PX05046 is a compound based on PA 6 resin containing Glass Bead, Glass Fiber.
Added features include: Heat Stabilized, UV-Stabilized.This data was supplied by SABIC-IP for the Europ.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | Nominal Stress, yld, Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL GTX GTX8410W PPE+PA High flow, 10% Glass Reinforced PPE+PA. Typically used in Automotive connectors. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | ASTM-D638 |
Polyram PlusTek PA340S6 Nylon 6.6, 30% Glass beads 30% glass beads reinforced polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | 95.1 MPa @Thickness 3.17 mm |
13800 psi @Thickness 0.125 in |
ASTM D638 |
Polyram PlusTek RA353M8 Nylon 66, 40% Mineral Filled Information provided by Polymer Technology and Services, LLC (PTS). |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527 |
Polyram RamOfin PPH308G6 Polypropylene, 30% Glass Fiber, Impact Modified 30% Glass fiber reinforced, heat stabilized, impact modified polypropylene for injection molding applications.Information provided by Polyram. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527 |
Polyram RamTough PZ324G4NT Polycarbonate, 20% Glass Fiber, Flame Retardant 20% glass fiber reinforced, flame retardant polycarbonate for injection molding applications.Information provided by Polyram. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527-1/-2 |
DSM Akulon® K222-D Nylon 6 (European and Asian Grade) (Dry) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527 |
Eurostar Starglas GX05052 PSU, Glass Fiber Filled Starglas GX05052 is a Glass Fiber Reinforced PSU resin (also known as Starglas PSU A 10V ¾)Information provided by Eurostar. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527-1/-2 |
DSM Akulon® S223-EH Nylon 66 (European and Asian Grade) (Dry) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
Eurostar Staramide PX05046 PA6, Glass Bead/Fiber Filled, Injection Molded Staramide XP05046 is Glass Bead and Glass Fiber Reinforced Polyamide 6 Injection Molding ResinInformation provided by Eurostar. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® 20NSP1 Nylon 66, DAM Availability:Asia PacificEuropeNorth AmericaFiller/Reinforcement:Glass Fiber, 43% Filler by Weight Additive:Nucleating AgentLubricant Features:Fast Molding CycleGeneral PurposeGood Mold Release Good.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | ASTM D638 |
Beijing Ranger Chem PBT-201-G10 Flame Retarding FR PBT Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | |
Radici Radilon® A 38 (dry) Nylon 66 Radilon® A is a range of polyamide 66 (PA66) products obtained through the polymerization of hexamethylendiamine and adipic acid, and used for injection, extrusion and blow-molding.Information prov.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® 3412ECR PC (Asia Pacific) Lexan* 3412ECR Polycarbonate (PC) resin is a 20% glass fiber filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant GF-PC has an UL-94 V0 rating and is available in v.. |
|||
Tensile Strength, Yield | 95.0 MPa | 13800 psi | 50 mm/min; ISO 527-1/-2 |
BASF Ultramid® B3UG4 LS BK 23215 20% Glass Filled PA66 FR (Dry) Description: Halogen-free and phosphorus free flame retardant injection-molding grade with outstanding free-flow properties, good electrical properties and low smoke density; resistant to glow wire.. |