Polymer Property : Tensile Strength at Break = 14500 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 100 MPa
14500 psi
Plastcom SLOVAMID 66 GF 10 FRA 3 PA66, 10% glass fibre
Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.0..
Tensile Strength at Break 100 MPa
14500 psi
ISO 527
Nilit FRIANYL A63 SG30 Nylon 6.6 for injection molding, 30% mineral filled
Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Strength at Break 100 MPa
14500 psi
50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® BFL2015HF PC (Asia Pacific)
Non-brominated, non-chlorinated flame retardant, glass reinforced PC. Opaque colors only. UL94 V0 1.5 mm for BLACK; V1 1.5 mm for OTHER Color.
Tensile Strength at Break 100 MPa
14500 psi
5mm/min; ISO 527-2/1A
Celanese Celanex® 3200-2 PBT, 15% Glass Reinforced  (Unverified Data**)
Celanex 3200-2 is a general purpose, 15% glass reinforced polybutylene terephthalate with a good balance of mechanical properties and processability. Celanex 3200-2 contains an internal lubricant.15..
Tensile Strength at Break 100 MPa
14500 psi
ASTM D 638
RTP Company RTP 807 TFE 15 Acetal (POM), Glass Fiber - PTFE Lubricated
Tensile Strength at Break 100 MPa
14500 psi
ISO 527-1/-2
DSM Akulon® K224-HG5 (Cond.) 25% Glass Reinforced Nylon 6 (North America)  (discontinued **)
Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis..
Tensile Strength at Break 100 MPa
14500 psi
Idemitsu Kosan Xarec® EA 522 SPS, 22% Glass Filled
Crystalline Polymer, Glass Filled, Ignition Resistant, Impact Modified. Used in Electronic and Electrical applications
Tensile Strength at Break 100 MPa
14500 psi
Conditioned; ISO 527-1/-2
Lanxess Durethan® AKV 325 H2.0 901510 Nylon 66, 25% Glass Fiber
PA 66, 25% glass fibers, extrusion- and blow molding grade, branched, high viscosity, good heat-ageing resistance, good hydrolysis resistance
Tensile Strength at Break 100 MPa
14500 psi
Conditioned; ISO 527-1/-2
Lanxess Durethan® BKV 30 H2.0 EF 901510 Nylon 6, 30% Glass Fiber
PA 6, 30% glass fibers, good flowability (Easy Flow), good heat-ageing resistance
Tensile Strength at Break 100 MPa
14500 psi
conditioned, 5 mm/min; ISO 527-1,-2
Lanxess Durethan® DP 2131/20 H3.0 000000 Nylon 6, 20% Glass Fiber
PA 6, 20% glass fiber, injection molding, heat-ageing stabilized, weather stabilized, improved surface finishInformation provided by LANXESS.
Tensile Strength at Break 100 MPa
14500 psi
ISO 527-1/-2
Lanxess Pocan® KU 1-7635 901510 PBT + PC, 30% Glass Fiber
PBT+PC, 30% glass fibers, injection molding, low tendency to warp, improved surface finish
Tensile Strength at Break 100 MPa
14500 psi
LATI Latilub 75/4-15ST G/30 PBT, 30% Glass Fiber Reinforced, Silicone/PTFE Filled
Self-lubricating product based on Polybutylene Terephthalate (PBT). Silicone / PTFE. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation pr..
Tensile Strength at Break 100 MPa
14500 psi
50 mm/min; ISO 527
SABIC Innovative Plastics ULTEM 3452 PEI (Europe-Africa-Middle East)
45% Glass fiber and mineral filled, enhanced flow Polyetherimide (Tg 217C) with enhanced dimensional stability. Resin is RoHS compliant. UL94 V0 and 5VA listing in recognized colors.
Tensile Strength at Break 100 MPa
14500 psi
ISO 527
SABIC Innovative Plastics LNP THERMOCOMP GF006XXZ PSU
LNP THERMOCOMP* GF006XXZ is a compound based on Polysulfone resin containing 30% Glass Fiber.
Tensile Strength at Break 100 MPa
14500 psi
50mm/min; ISO 527
Teijin Panlite® G-3430H Low Anisotropy, Glass Fiber Reinforced Polycarbonate Resin
Reinforced with 30 % of special GF and improved appearance grade, meeting UL 94 V-2.Applications:Mechanical, electric and electronic components that need good appearance and mechanical propertyPreci..
Tensile Strength at Break 100 MPa
14500 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Noryl GTX GTX8710 PPE+PA
Noryl GTX8710 resin is a glass filled, high performance blend of PPE/PA that exhibits an exceptional balance of high-heat resistance, strength, flow, and conductivity. This grade can be electro-sta..
Tensile Strength at Break 100 MPa
14500 psi
ASTM D 638
RTP Company RTP 2599 X 65037 FR A Polycarbonate/ABS Alloy (PC/ABS), Glass Fiber - PTFE Lubricated - Flame Retardant - UL94 V-0
Tensile Strength at Break 100 MPa
14500 psi
ASTM D 638
Cossa Polimeri ESTAPROP H 0580 GFC Polypropylene, 40% Glass Filled
PP homopolymer 40% chemically coupled glass fiberExcellent stiffness, excellent impact strengthInformation provided by Cossa Polimeri S.r.l.
Tensile Strength at Break 100 MPa
14500 psi
dry; ISO 527-1/-2
EMS-Grivory Grivory® AG-30 LF 15 PA66-(GF+Z)45
Product description: Grilon AG-30 LF 15 black 9832 is a heat stabilized, normal viscosity PA66 injection molding grade with 30% glass fibers and 15% of a combination of PTFE and silicone. Grilon AG-..
Tensile Strength at Break 100 MPa
14500 psi
dry; ISO 527-1/-2
EMS-Grivory Grivory® BG-30 FR PA6-GF30 FR
Information provided by EMS Grivory
Tensile Strength at Break 100 MPa
14500 psi
50%RH; ISO 527-1/-2
DuPont Performance Polymers Zytel® HTN 54G15HSLR NC010 Polyphthalamide (PPA)  (Unverified Data**)
15% Glass Reinforced Toughened PPA High Performance Polyamide Zytel HTN54G15HSLR NC010 is a 15% glass reinforced toughened heat stabilized hydrolysis resistant high performance polyamide resin. It i..
Tensile Strength at Break 100 MPa
14500 psi
5mm/min; ISO 527-2/1A
Celanese CELANEX 3200FC PBT, 15% Glass Reinforced
Celanex 3200FC is a general purpose, 15% glass reinforced polybutylene terephthalate with a good balance of mechanical properties and processability.Information provided by Celanese
Tensile Strength at Break 100 MPa
14500 psi
5mm/min; ISO 527-2/1A
Celanese Celanex® 3200 PBT, 15% Glass Reinforced
Celanex 3200 is a general purpose, 15% glass reinforced polybutylene terephthalate with a good balance of mechanical properties and processability.To avoid hydrolytic degradation during processing, ..
Tensile Strength at Break 100 MPa

@Temperature -40.0 °C
14500 psi

@Temperature -40.0 °F
ISO Data
BASF Ultramid® 8253 HS PA6 (Dry)
Ultramid 8253 HS is a heat stabilized, impact modified type 6 graft copolymer developed for both injection molding and extrusion applications requiring improved dry as molded toughness and increased..
Tensile Strength at Break 100 MPa

@Temperature -40.0 °C
14500 psi

@Temperature -40.0 °F
ASTM Test
BASF Ultramid® 8253 PA6 (Dry)
Ultramid 8253 is an unfilled, impact modified type 6 graft copolymer developed for both injection molding and extrusion applications. It is also available in heat stabilized (Ultramid 8253 HS) and/o..
Tensile Strength at Break 100 MPa
14500 psi
ISO 527
Celanese Thermx® TE3002 BK010 PCT
Thermx® TE3002 BK010 is a 30% glass fiber reinforced, flame retardant, black high performance polyester resin for injection molding.Celenese acquired the Thermx product line from DuPont in 2010.
Tensile Strength at Break 100 MPa
14500 psi
5mm/min; ISO 527-2/1A
Celanese ZENITE 7755 LCP, 55% Mineral / Glass Reinforced
Zenite 7755 is a 55% glass/mineral-reinforced liquid crystal polymer resin for injection molding. It has good impact resistance, excellent temperature resistance, and is suitable for applications i..
Tensile Strength at Break 100 MPa
14500 psi
5 [mm/min]; ISO 527-1/2
Akro-Plastic Akromid® A3 GF 20 (2419) PA 6.6 Conditioned, 20% Glass Filled
AKROMID® A (Polyamide 6.6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperat..
Tensile Strength at Break 100 MPa
14500 psi
5mm/min; ISO 527-2/1A
Celanese Celstran® PP-GF30-0553 Black PP, 30% Glass Reinforced
Material code according to ISO 1043-1: PPInformation provided by Celanese
Tensile Strength at Break 100 MPa
14500 psi
5mm/min; ISO 527-2/1A
Celanese THERMX CG023 PCT, 20% Glass Reinforced
Thermx« CG023 is a 20% glass fiber reinforced polycyclohexylenedimethylene terephthalate for injection molding.Information provided by Celanese