Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 150 MPa | 21800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
Ovation Polymers Nima™ HL 30525 GF FR PET, 25% Glass Fiber PET – Flame Retardant 25% Short Glass Fiber Reinforced. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared according to ASTM s.. |
|||
Flexural Yield Strength | 150 MPa | 21800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
Ovation Polymers Opnyl OP6GF15 Nylon 6, 15% Glass Reinforced, Dry Nylon 6 - Glass reinforced (15 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. For Nylon compounds the m.. |
|||
Flexural Yield Strength | 150 MPa | 21800 psi | 1.3 mm/min; ASTM D790 |
Ovation Polymers RIGITRON 30525 GF FR PET, 25% Glass Reinforced PET – 25% Short Glass Fiber Reinforced with Flame retardant. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared according to AS.. |
|||
Flexural Yield Strength | 150 MPa | 21800 psi | ISO 178, ASTM D790 |
Nilit Nilamid A3 H G3 ZB 13% Glass Reinforced High Impact PA66 Description: Nilamid A3 H G3 ZB (13% Glass Reinforced) was developed for applications that require a combination of high stiffness and good elongation or impact resistance. It is widely used for app.. |
|||
Flexural Yield Strength | 150 MPa | 21800 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics EXTEM XH1005 TPI Resin Thermoplastic Polyimide Extem* XH1005 Resin. |
|||
Flexural Yield Strength | 150 MPa | 21800 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics EXTEM XH1005 TPI Resin (Asia Pacific) Thermoplastic Polyimide Extem* XH1005 Resin. |
|||
Flexural Yield Strength | 150 MPa | 21800 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics EXTEM XH1005 TPI Resin (Europe-Africa-Middle East) Thermoplastic Polyimide Extem* XH1005 Resin. |
|||
Flexural Yield Strength | 150 MPa | 21800 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics EXTEM XH1005F TPI Resin (Europe-Africa-Middle East) High Heat Amorphous TPI Blend, Tg 267C, High Continuous Use Temperature (CUT). EFSA Food Contact Approved. Material is UL listed. This material is RoHS compliant and also halogen free according VDE/.. |
|||
Flexural Yield Strength | 150 MPa | 21800 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® BFL2015 PC Non-brominated, non-chlorinated flame retardant, glass reinforced PC. Opaque colors only |
|||
Flexural Yield Strength | 150 MPa | 21800 psi | ASTM Data |
BASF Capron® HPN 9333G Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned)
(discontinued **) Capron HPN 9333G is a 33% glass reinforced, impact modified polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with excellent surface a.. |
|||
Flexural Yield Strength | 150 - 188 MPa | 21800 - 27300 psi | Average value: 171 MPa Grade Count:15 |
Overview of materials for Polycyclohexylenedimethylene Terephthalate (PCT), 30% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "PCT or PCTA, 30% Glass Reinforced".Specific grades with glass content between 25% and 34% are included. .. |
|||
Flexural Yield Strength | 150 MPa | 21800 psi | ISO 178 |
Wellman Wellamid® GFT15N050-N2 15% Impact Modified Glass Reinforced Nylon 66/6, Lubricated & Heat Stabilized
&n Typical Applications: Machinery gear trains and linkage, conveyor belt links, fasteners, auto under hood and door parts, automotive door handles, appliance parts, sporting goods, lawn and garden equ.. |
|||
Flexural Yield Strength | 150 MPa | 21800 psi | Bending Strength; ASTM D790 |
EVALCA EVAL® LC-L101A Ethylene Vinyl Alcohol Copolymer Resin
(discontinued **) 27 mol % Ethylene.Data provided by EVALCA. Applications: Blown film, melt phase forming. Highest gas barrier EVOH available. EVOH is used in packaging applications because of its outstanding gas .. |
|||
Flexural Yield Strength | 150 MPa @Thickness 3.20 mm |
21800 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical Lupox® NH2306F PBT+GF30% Description: Injection Molding, PBT+GF30%, Halogen Free Flame RetardantApplication: IT/OA, E&E (Connector)CAS No. 65997-17-3 and 24968-12-5Information provided by LG Chemical |
|||
Flexural Yield Strength | 150 MPa | 21800 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DX07035 PC (Europe-Africa-Middle East) LNP* LUBRICOMP* DX07035 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE, Flame Retardant. Added features include: Flame retardant, Easy Molding, Internally Lubricated, Mold R.. |
|||
Flexural Yield Strength | 150 MPa | 21800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP WFL33 PBT LNP* LUBRICOMP* WFL33 is a compound based on PBT containing 15% Glass Fiber, 15% PTFE. Added feature of this grade is: Wear Resistant. |
|||
Flexural Yield Strength | 150 MPa | 21800 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® 815 PBT (Europe-Africa-Middle East) VALOX 815 is a 15% glass reinforced PBT+PET blend with excellent surface finish. Applications: hot air gun housings assemblies, industrial glue guns, appliance housings and handles. |
|||
Flexural Yield Strength | 150 MPa | 21800 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® DR51 PBT (Europe-Africa-Middle East) VALOX DR51 is a 15% glass fiber reinforced PBT injection moulding resin with excellent mechanical, thermal and electrical performance. Applications: spotlights, appliance housings, handles. |
|||
Flexural Yield Strength | 150 MPa | 21800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® ENH4560 PBT (Europe-Africa-Middle East) Valox* ENH4560 resin is a non-brominated/non-chlorinated flame retardant product based on Valox* PBT resin. |
|||
Flexural Yield Strength | 150 MPa | 21800 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® K4530 PBT (Europe-Africa-Middle East) 15% glass reinforced PBT, Hydrolytically stable, High flow, Automotive connectors. |
|||
Flexural Yield Strength | 150 MPa | 21800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Xenoy® 6370 PBT+PC 30% glass-reinforced, impact modified thermoplastic alloy. Improved toughness and ductility. |
|||
Flexural Yield Strength | 150 MPa | 21800 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL GFN2 PPE+HIPS (Asia Pacific) PPE+PS blend. 20% Glass reinforced. FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including pump.. |
|||
Flexural Yield Strength | 150 MPa | 21800 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL NH7114 PPE+HIPS Noryl* NH7114 resin is a 20% glass reinforced, modified PPE-PS blend. The material uses non-halogenated flame retardants to achieve UL94 flame ratings while offering an exceptional balance of streng.. |
|||
Flexural Yield Strength | 150 MPa | 21800 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL NH7114 PPE+HIPS (Asia Pacific) Noryl* NH7114 resin is a 20% glass reinforced, modified PPE-PS blend. The material uses non-halogenated flame retardants to achieve UL94 flame ratings while offering an exceptional balance of streng.. |
|||
Flexural Yield Strength | 150 MPa | 21800 psi | ASTM D790 |
PlastxWorld Veroplas PB3150 Nylon 66 15% glass filled injection molding gradeInformation provided by PlastxWorld Inc. |
|||
Flexural Yield Strength | 150 MPa | 21800 psi | ISO 178-93 |
Wellman Wellpet® MRGF102-BK1 PET, 35% Mineral/Glass Fiber Reinforced Typical data obtained from injection molded test bars, tested dry as molded at 73°F (23°C). Information provided by Wellman, Inc. Engineering Resins Division. |
|||
Flexural Yield Strength | 150 MPa | 21800 psi | ASTM D790 |
E-Polymers Tekaster® F615GM , 40% GF/MF Reinforced PET 40% GF/MF Reinforced, Low warpageInformation provided by E-Polymers Co. Ltd. |
|||
Flexural Yield Strength | 150 - 230 MPa | 21800 - 33400 psi | ASTM D790 |
Chang Chun Plastic PBT4830 Fire Retardant & 30% Glass Fiber Enforced Grade PBT Information provided by Dowell Trading Company Ltd. |
|||
Flexural Yield Strength | 150 MPa | 21800 psi | ASTM Data |
BASF Capron® 8331G HI HS BK-102 Impact Modified, 14% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron 8331G HI HS BK-102 is a black pigmented, heat stabilized, 30% glass reinforced, impact modified polyamide 6 injection molding compound developed for applications requiring improved dry as mol.. |
|||
Flexural Yield Strength | 150 MPa | 21800 psi | ASTM Data |
BASF Capron® HPN 9333G HS Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned)
(discontinued **) Capron HPN 9333G HS is a heat stabilized, 33% glass reinforced, impact modified polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with.. |