SABIC Innovative Plastics LNP LUBRICOMP SP003 PA 12 (Asia Pacific)

Category Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP SP003 PA 12 (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* SP003 is a compound based on Nylon 12 resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.09 g/cc
0.0394 lb/in³
ASTM D792
1.09 g/cc
0.0394 lb/in³
ISO 1183
Moisture Absorption 0.200 %
0.200 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0090 - 0.011 cm/cm

@Time 86400 sec
0.0090 - 0.011 in/in

@Time 24.0 hour
ASTM D955
0.010 cm/cm

@Time 86400 sec
0.010 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.018 - 0.020 cm/cm

@Time 86400 sec
0.018 - 0.020 in/in

@Time 24.0 hour
ASTM D955
0.019 cm/cm

@Time 86400 sec
0.019 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 35.0 MPa
5080 psi
ASTM D638
36.0 MPa
5220 psi
ISO 527
Tensile Strength, Yield 37.0 MPa
5370 psi
ASTM D638
38.0 MPa
5510 psi
ISO 527
Elongation at Break 23.9 %
23.9 %
ASTM D638
32.9 %
32.9 %
ISO 527
Elongation at Yield 17.5 %
17.5 %
ASTM D638
18.4 %
18.4 %
ISO 527
Tensile Modulus 1.37 GPa
199 ksi
50 mm/min; ASTM D638
1.58 GPa
229 ksi
1 mm/min; ISO 527
Flexural Strength 44.0 MPa
6380 psi
ISO 178
Flexural Modulus 1.30 GPa
189 ksi
ISO 178
1.37 GPa
199 ksi
ASTM D790
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
Izod Impact, Unnotched 6.83 J/cm
12.8 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 48.0 kJ/m²
22.8 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 5.00 J
3.69 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 7.00 J
5.16 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.23
0.23
ASTM D3702 Modified
Coefficient of Friction, Static 0.14
0.14
ASTM D3702 Modified
K (wear) Factor 26.2 x 10-8 mm³/N-M
13.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 112 µm/m-°C

@Temperature -40.0 - 40.0 °C
62.2 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
113 µm/m-°C

@Temperature -40.0 - 40.0 °C
62.8 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 108 µm/m-°C

@Temperature -40.0 - 40.0 °C
60.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
108 µm/m-°C

@Temperature -40.0 - 40.0 °C
60.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 134 °C
273 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
150 °C

@Thickness 3.20 mm
302 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 147 °C
297 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
146 °C

@Thickness 3.20 mm
295 °F

@Thickness 0.126 in
unannealed; ASTM D648