Polymer Property : Linear Mold Shrinkage, Transverse = 0.019 cm/cm Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Transverse	0.019 cm/cm @Thickness 4.00 mm	0.019 in/in @Thickness 0.157 in	ISO 294-4
DuPont Performance Polymers Delrin® 500AL NC010 Acetal Homopolymer (Unverified Data**) Delrin® 500AL is a medium viscosity acetal homopolymer, with an advanced system of lubrication for applications requiring low wear and/or coefficient of friction against steel, itself or other plas..
Linear Mold Shrinkage, Transverse	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Lubricomp FX00617 PE LNP* Lubricomp* FX00617 is a compound based on Polyethylene resin containing Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Amer..
Linear Mold Shrinkage, Transverse	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP Lubricomp FX00617 PE LNP* Lubricomp* FX00617 is a compound based on Polyethylene resin containing Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Amer..
Linear Mold Shrinkage, Transverse	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Lubricomp FX00617 PE (Asia Pacific) LNP* Lubricomp* FX00617 is a compound based on Polyethylene resin containing Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Asia..
Linear Mold Shrinkage, Transverse	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP Lubricomp FX00617 PE (Asia Pacific) LNP* Lubricomp* FX00617 is a compound based on Polyethylene resin containing Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Asia..
Linear Mold Shrinkage, Transverse	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP LL004C PEEK LNP* LUBRICOMP* LL004C is a compound based on Polyetheretherketone resin containing 20% PTFE. Added features of this material include: Wear Resistant, Clean Compounding System.
Linear Mold Shrinkage, Transverse	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP LL004C PEEK (Asia Pacific) LNP* Lubricomp* LL004C is a compound based on Polyetheretherketone resin containing PTFE. Added features of this material include: Internally Lubricated, Clean Compounding System.
Linear Mold Shrinkage, Transverse	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP LL004E PEEK LNP* LUBRICOMP* LL004E is a compound based on Polyetheretherketone resin containing 20% PTFE. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Transverse	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP LL004E PEEK (Asia Pacific) LNP* Lubricomp* LL004E is a compound based on Polyetheretherketone resin containing PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP RFL34 PA 66 LNP* LUBRICOMP* RFL34 is a compound based on Nylon 66 resin containing 20% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Transverse	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP RFL34 PA 66 LNP* LUBRICOMP* RFL34 is a compound based on Nylon 66 resin containing 20% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Transverse	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP RFL34 PA 66 (Asia Pacific) LNP* Lubricomp* RFL34 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP RFL34 PA 66 (Asia Pacific) LNP* Lubricomp* RFL34 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.019 - 0.033 cm/cm @Time 86400 sec	0.019 - 0.033 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP RL004S PA 66 LNP LUBRICOMP* RL004S is a compound based on Nylon 66 resin containing 20% PTFE. Added features of this material include: Heat Stabilized, Wear Resistant.
Linear Mold Shrinkage, Transverse	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP RP004 PA 66 (Asia Pacific) LNP* Lubricomp* RP004 is a compound based on Nylon 66 resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Lubricomp RP0049 PA 66 LNP LUBRICOMP* RP0049 is a compound based on Nylon 66 resin containing Flame Retardant, PTFE, Silicone. Added features of this material include: Flame Retardant.This data was supplied by SABIC-IP f..
Linear Mold Shrinkage, Transverse	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP SP003 PA 12 (Asia Pacific) LNP* Lubricomp* SP003 is a compound based on Nylon 12 resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.019 - 0.024 cm/cm @Time 86400 sec	0.019 - 0.024 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Stat-loy K3000 Acetal Copoly LNP* Stat-loy* K3000 is a compound based on Acetal Copolymer resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for the Americas regi..
Linear Mold Shrinkage, Transverse	0.019 - 0.024 cm/cm @Time 86400 sec	0.019 - 0.024 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP Stat-loy K3000 Acetal Copoly LNP* Stat-loy* K3000 is a compound based on Acetal Copolymer resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for the Americas regi..
Linear Mold Shrinkage, Transverse	0.019 - 0.024 cm/cm @Time 86400 sec	0.019 - 0.024 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Stat-loy K3000 Acetal Copoly (Asia Pacific) LNP* Stat-loy* K3000 is a compound based on Acetal Copolymer resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for the Asia Pacific ..
Linear Mold Shrinkage, Transverse	0.019 - 0.024 cm/cm @Time 86400 sec	0.019 - 0.024 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP Stat-loy K3000 Acetal Copoly (Asia Pacific) LNP* Stat-loy* K3000 is a compound based on Acetal Copolymer resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for the Asia Pacific ..
Linear Mold Shrinkage, Transverse	0.019 - 0.021 cm/cm @Time 86400 sec	0.019 - 0.021 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Thermocomp KF003 Acetal Copoly LNP* Thermocomp* KF003 is a compound based on Acetal Copolymer resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
Linear Mold Shrinkage, Transverse	0.019 - 0.021 cm/cm @Time 86400 sec	0.019 - 0.021 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Thermocomp KF003 Acetal Copoly (Asia Pacific) LNP* Thermocomp* KF003 is a compound based on Acetal Copolymer resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
Linear Mold Shrinkage, Transverse	0.019 - 0.021 cm/cm @Time 86400 sec	0.019 - 0.021 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP RB008 PA 66 (Asia Pacific) LNP THERMOCOMP* RB008 is a compound based on Nylon 66 resin containing Glass Bead.
Linear Mold Shrinkage, Transverse	0.019 - 0.021 cm/cm @Time 86400 sec	0.019 - 0.021 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP RB008 PA 66 (Asia Pacific) LNP THERMOCOMP* RB008 is a compound based on Nylon 66 resin containing Glass Bead.
Linear Mold Shrinkage, Transverse	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP LL004 PEEK LNP LUBRICOMP* LL004 is a compound based on Polyetheretherketone resin containing 20% PTFE. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Transverse	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP LL004 PEEK (Europe-Africa-Middle East) LNP LUBRICOMP* LL004 is a compound based on Polyetheretherketone resin containing PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP WBL36L PBT LNP* LUBRICOMP* WBL36L is a compound based on PBT resin containing 30% Glass Bead, 15% PTFE. Added features of this material include: Wear Resistant, Low Extractible.
Linear Mold Shrinkage, Transverse	0.019 - 0.021 cm/cm @Time 86400 sec	0.019 - 0.021 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP RB008 PA 66 LNP THERMOCOMP* RB008 is a compound based on Nylon 66 resin containing 40% Glass Bead.
Linear Mold Shrinkage, Transverse	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP 2X04505 ETFE LNP* THERMOCOMP* 2X04505 is a compound based on ETFE resin containing Proprietary Filler(s).