Polymer Property : Linear Mold Shrinkage, Flow = 0.0090 in/in Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Linear Mold Shrinkage, Flow 0.0090 cm/cm

@Time 86400 sec
0.0090 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP KONDUIT MT00E PP
LNP KONDUIT* MT00E is a compound based on Polypropylene resin containing 70% Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
Linear Mold Shrinkage, Flow 0.0090 cm/cm

@Time 86400 sec
0.0090 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP KONDUIT MT00E PP (Asia Pacific)
LNP KONDUIT* MT00E is a compound based on Polypropylene resin containing Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
Linear Mold Shrinkage, Flow 0.0090 cm/cm

@Time 86400 sec
0.0090 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP KONDUIT MT00E PP (Europe-Africa-Middle East)
LNP KONDUIT* MT00E is a compound based on Polypropylene resin containing Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
Linear Mold Shrinkage, Flow 0.0090 cm/cm

@Time 86400 sec
0.0090 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP KONDUIT RTF2B PA 66 (Europe-Africa-Middle East)
LNP* Konduit* RTF2B is a compound based on Nylon 66 resin containing Glass Fiber, Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
Linear Mold Shrinkage, Flow 0.0090 cm/cm

@Time 86400 sec
0.0090 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP KONDUIT RTF2B PA 66
LNP* KONDUIT* RTF2B is a compound based on Nylon 66 resin containing 10% Glass Fiber, 55% Thermal Filler. Added features of this material include: Thermally Conductive.
Linear Mold Shrinkage, Flow 0.0090 cm/cm

@Time 86400 sec
0.0090 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP KONDUIT RTF2B PA 66 (Asia Pacific)
LNP* Konduit* RTF2B is a compound based on Nylon 66 resin containing Glass Fiber, Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
Linear Mold Shrinkage, Flow 0.0090 - 0.010 cm/cm

@Time 86400 sec
0.0090 - 0.010 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP DP003 PC
LNP LUBRICOMP* DP003 is a compound based on Polycarbonate resin containing 15% PTFE/Silicone. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow 0.0090 - 0.010 cm/cm

@Time 86400 sec
0.0090 - 0.010 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP DP003 PC (Asia Pacific)
LNP LUBRICOMP* DP003 is a compound based on Polycarbonate resin containing Silicone, PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow 0.0090 - 0.011 cm/cm

@Time 86400 sec
0.0090 - 0.011 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP DX94375H PC
LNP* LUBRICOMP* DX94375H is a compound based on Polycarbonate resin containing Proprietary Fillers. Added features of this material include: Healthcare, Wear Resistant.
Linear Mold Shrinkage, Flow 0.0090 - 0.011 cm/cm

@Time 86400 sec
0.0090 - 0.011 in/in

@Time 24.0 hour
ASTM D 955
SABIC Innovative Plastics LNP Lubricomp EL004 PEI (Asia Pacific)
LNP* Lubricomp* EL004 is a compound based on Polyetherimide resin containing PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Asia Pac..
Linear Mold Shrinkage, Flow 0.0090 - 0.011 cm/cm

@Time 86400 sec
0.0090 - 0.011 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP SP003 PA 12
LNP* LUBRICOMP* SP003 is a compound based on Nylon 12 resin containing 15% PTFE/Silicone. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Flow 0.0090 - 0.011 cm/cm

@Time 86400 sec
0.0090 - 0.011 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP SP003 PA 12 (Asia Pacific)
LNP* Lubricomp* SP003 is a compound based on Nylon 12 resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow 0.0090 - 0.016 cm/cm

@Thickness 0.750 - 2.30 mm
0.0090 - 0.016 in/in

@Thickness 0.0295 - 0.0906 in
SABIC Method
SABIC Innovative Plastics Valox® 195 PBT
PELLET FORM. For compounding only (not for injection molding). Unreinforced PBT. Melt viscosity between 740 and 900 poise. Natural Color (1001) Only.
Linear Mold Shrinkage, Flow 0.0090 - 0.016 cm/cm

@Thickness 0.750 - 2.30 mm
0.0090 - 0.016 in/in

@Thickness 0.0295 - 0.0906 in
SABIC Method
SABIC Innovative Plastics Valox® 195HP PBT
PELLET FORM. For compounding only (not for injection molding). Unreinforced PBT. FDA 21CFR177.1660 compliant. Melt viscosity between 740 and 900 poise. Natural Color (1001) Only.
Linear Mold Shrinkage, Flow 0.0090 - 0.016 cm/cm

@Thickness 0.750 - 2.30 mm
0.0090 - 0.016 in/in

@Thickness 0.0295 - 0.0906 in
SABIC Method
SABIC Innovative Plastics Valox® 215HPR PBT
Unreinforced PBT with mold release. FDA food contact compliant in limited colors. Effective March 2008 this grade will no longer be supported with biocompatibility data. Alternative grade Valox HX21..
Linear Mold Shrinkage, Flow 0.0090 - 0.016 cm/cm

@Thickness 0.750 - 2.30 mm
0.0090 - 0.016 in/in

@Thickness 0.0295 - 0.0906 in
SABIC Method
SABIC Innovative Plastics Valox® 310 PBT
Unreinforced, general purpose. Typical viscosity 5000-7000.
Linear Mold Shrinkage, Flow 0.0090 - 0.016 cm/cm

@Thickness 0.750 - 2.30 mm
0.0090 - 0.016 in/in

@Thickness 0.0295 - 0.0906 in
SABIC Method
SABIC Innovative Plastics Valox® 310 PBT (Asia Pacific)
Unreinforced, general purpose. Typical viscosity 5000-7000.
Linear Mold Shrinkage, Flow 0.0090 - 0.016 cm/cm

@Thickness 0.750 - 2.30 mm
0.0090 - 0.016 in/in

@Thickness 0.0295 - 0.0906 in
SABIC Method
SABIC Innovative Plastics Valox® 311 PBT
Unreinforced, improved resistance to UV. Medium viscosity.
Linear Mold Shrinkage, Flow 0.0090 - 0.016 cm/cm

@Thickness 0.750 - 2.30 mm
0.0090 - 0.016 in/in

@Thickness 0.0295 - 0.0906 in
SABIC Method
SABIC Innovative Plastics Valox® 312 PBT
Unreinforced, For compounding only (not for injection molding), FDA (21 CFR 177.1660) compliant. Medium viscosity.This data was supplied by SABIC-IP for the Americas region.
Linear Mold Shrinkage, Flow 0.0090 - 0.016 cm/cm

@Thickness 0.750 - 2.30 mm
0.0090 - 0.016 in/in

@Thickness 0.0295 - 0.0906 in
SABIC Method
SABIC Innovative Plastics Valox® 312 PBT (Asia Pacific)
Unreinforced, For compounding only (not for injection molding), Medium viscosity.
Linear Mold Shrinkage, Flow 0.0090 - 0.016 cm/cm

@Thickness 0.750 - 2.30 mm
0.0090 - 0.016 in/in

@Thickness 0.0295 - 0.0906 in
SABIC Method
SABIC Innovative Plastics Valox® 315 PBT
Unreinforced, For extrusion/compounding only (not for injection molding). High viscosity. Melt viscosity between 7500 and 9500 poise.
Linear Mold Shrinkage, Flow 0.0090 - 0.016 cm/cm

@Thickness 0.750 - 2.30 mm
0.0090 - 0.016 in/in

@Thickness 0.0295 - 0.0906 in
SABIC Method
SABIC Innovative Plastics Valox® 325 PBT
General purpose, unreinforced, improved processing. Applications like sprinklers and nozzles, pumps, door handle, tank covers, pens, pencils etc.
Linear Mold Shrinkage, Flow 0.0090 - 0.016 cm/cm

@Thickness 0.750 - 2.30 mm
0.0090 - 0.016 in/in

@Thickness 0.0295 - 0.0906 in
SABIC Method
SABIC Innovative Plastics Valox® 325M PBT (Asia Pacific)
325M is a high flow VALOX 325 for restrictive gate tooling (key buttons)This data was supplied by SABIC-IP for the Asia Pacific region.
Linear Mold Shrinkage, Flow 0.0090 cm/cm

@Time 86400 sec
0.0090 in/in

@Time 24.0 hour
ASTM D 955
SABIC Innovative Plastics LNP Thermocomp MX88073 PP (Asia Pacific)
LNP* Thermocomp* MX88073 is a compound based on Polypropylene resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
Linear Mold Shrinkage, Flow 0.0090 cm/cm

@Time 86400 sec
0.0090 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP RF0039S PA 66
LNP THERMOCOMP* RF0039S is a compound based on Nylon 66 resin containing 15% Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant, Heat Stabilized.
Linear Mold Shrinkage, Flow 0.0090 - 0.011 cm/cm

@Time 86400 sec
0.0090 - 0.011 in/in

@Time 24.0 hour
ASTM D 955
SABIC Innovative Plastics LNP Lubricomp KCL22 Acetal Copoly
LNP* Lubricomp* KCL22 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This data ..
Linear Mold Shrinkage, Flow 0.0090 - 0.011 cm/cm

@Time 86400 sec
0.0090 - 0.011 in/in

@Time 24.0 hour
ASTM D 955
SABIC Innovative Plastics LNP Thermocomp 9X04488 POLYPHENYLENESULFONE
LNP* Thermocomp* 9X04488 is a compound based on POLYPHENYLENESULFONE resin containing Mineral.This data was supplied by SABIC-IP for the Americas region.
Linear Mold Shrinkage, Flow 0.0090 cm/cm

@Time 86400 sec
0.0090 in/in

@Time 24.0 hour
ASTM D 955
SABIC Innovative Plastics LNP Thermocomp MX88073 PP
LNP* Thermocomp* MX88073 is a compound based on Polypropylene resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
Linear Mold Shrinkage, Flow 0.0090 - 0.011 cm/cm

@Time 86400 sec
0.0090 - 0.011 in/in

@Time 24.0 hour
ASTM D 955
SABIC Innovative Plastics LNP Thermocomp OF002A PPS (Asia Pacific)
LNP* Thermocomp* OF002A is a compound based on Polyphenylene Sulfide resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
Linear Mold Shrinkage, Flow 0.0090 cm/cm

@Time 86400 sec
0.0090 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP RX93402 PA 66
LNP THERMOCOMP* RX93402 is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Flame Retardant.