Polymer Property : Linear Mold Shrinkage, Transverse = 0.018 in/in Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Transverse	0.018 cm/cm @Time 86400 sec	0.018 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP IL004 PA 6/12 LNP* LUBRICOMP* IL004 is a compound based on Nylon 6/12 resin containing 20% PTFE. Added features of this material include: Wear Resistant.
Linear Mold Shrinkage, Transverse	0.018 cm/cm @Time 86400 sec	0.018 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP IL004 PA 6/12 (Asia Pacific) LNP* Lubricomp* IL004 is a compound based on Nylon 6/12 resin containing PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.018 cm/cm @Time 86400 sec	0.018 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP QAP22S PA 6/10 (Asia Pacific) LNP* Lubricomp* QAP22S is a compound based on Nylon 6/10 resin containing PTFE, Aramid Fiber, Silicone. Added features of this material include: Internally Lubricated, Heat Stabilized.
Linear Mold Shrinkage, Transverse	0.018 cm/cm @Time 86400 sec	0.018 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP QAP22S PA 6/10 (Asia Pacific) LNP* Lubricomp* QAP22S is a compound based on Nylon 6/10 resin containing PTFE, Aramid Fiber, Silicone. Added features of this material include: Internally Lubricated, Heat Stabilized.
Linear Mold Shrinkage, Transverse	0.018 cm/cm @Time 86400 sec	0.018 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP QAP22S PA6.10 LNP* LUBRICOMP* QAP22S is a compound based on Nylon 6/10 resin containing 10% PTFE/Silicone, 10% Aramid Fiber. Added features of this material include: Wear Resistant, Heat Stabilized.
Linear Mold Shrinkage, Transverse	0.018 cm/cm @Time 86400 sec	0.018 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP QAP22S PA6.10 LNP* LUBRICOMP* QAP22S is a compound based on Nylon 6/10 resin containing 10% PTFE/Silicone, 10% Aramid Fiber. Added features of this material include: Wear Resistant, Heat Stabilized.
Linear Mold Shrinkage, Transverse	0.018 - 0.020 cm/cm @Time 86400 sec	0.018 - 0.020 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP SP003 PA 12 LNP* LUBRICOMP* SP003 is a compound based on Nylon 12 resin containing 15% PTFE/Silicone. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Transverse	0.018 - 0.020 cm/cm @Time 86400 sec	0.018 - 0.020 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP SP003 PA 12 (Asia Pacific) LNP* Lubricomp* SP003 is a compound based on Nylon 12 resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.018 cm/cm @Time 86400 sec	0.018 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP YL003C Polyester Elastomer LUBRICOMP* YL003C is a compound based on Polyester Elastomer resin containing 15% PTFE. Added features of this grade include: Clean Compound System, Wear Resistant.
Linear Mold Shrinkage, Transverse	0.018 cm/cm @Time 86400 sec	0.018 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP YL003C Polyester Elastomer (Asia Pacific) LUBRICOMP* YL-4030 CCS is a PTFE Lubricated Compound based on Polyester Elastomer resin which has low ionic and low outgassing performance for the Semicon and Internal Hard Disk Drive applications.
Linear Mold Shrinkage, Transverse	0.018 - 0.020 cm/cm @Time 86400 sec	0.018 - 0.020 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP KZ004 Acetal Copolymer LNP THERMOCOMP* KZ004 is a compound based on Acetal Copolymer resin containing 20% Milled Glass.
Linear Mold Shrinkage, Transverse	0.018 - 0.020 cm/cm @Time 86400 sec	0.018 - 0.020 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP KZ004 Acetal Copolymer LNP THERMOCOMP* KZ004 is a compound based on Acetal Copolymer resin containing 20% Milled Glass.
Linear Mold Shrinkage, Transverse	0.018 - 0.020 cm/cm @Time 86400 sec	0.018 - 0.020 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP KZ004 Acetal Copolymer (Asia Pacific) LNP* THERMOCOMP* KZ004 is a compound based on Acetal Copolymer resin containing Glass Fiber, Milled Glass.
Linear Mold Shrinkage, Transverse	0.018 - 0.020 cm/cm @Time 86400 sec	0.018 - 0.020 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP KZ004 Acetal Copolymer (Asia Pacific) LNP* THERMOCOMP* KZ004 is a compound based on Acetal Copolymer resin containing Glass Fiber, Milled Glass.
Linear Mold Shrinkage, Transverse	0.018 cm/cm @Time 86400 sec	0.018 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP STAT-LOY K3000SZ Acetal Copoly LNP* STAT-LOY* K3000SZ is a compound based on Acetal Copolymer resin. Added feature of this material is: AntiSstatic.
Linear Mold Shrinkage, Transverse	0.018 cm/cm @Time 86400 sec	0.018 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP STAT-LOY K3000SZ Acetal Copoly (Asia Pacific) LNP* Stat-loy* K3000SZ is a compound based on Acetal Copolymer resin containing Anti-Static. Added features of this material include: Antistat.
Linear Mold Shrinkage, Transverse	0.018 cm/cm @Time 86400 sec	0.018 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP STAT-LOY K3000Z Acetal LNP* STAT-LOY* K3000Z is a compound based on unfilled Acetal resin. Added feature of this material is: Antistat.
Linear Mold Shrinkage, Transverse	0.018 cm/cm @Time 86400 sec	0.018 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP STAT-LOY KX95702 Acetal LNP STAT-LOY* KX95702 is a compound based on Acetal resin containing Proprietary Filler(s). Added feature of this material is: Antistat.
Linear Mold Shrinkage, Transverse	0.018 cm/cm @Time 86400 sec	0.018 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP STAT-LOY KX96821 Acetal LNP STAT-LOY* KX96821 is a compound based on Acetal resin containing Proprietary Filler(s). Added feature of this material is: Antistat.
Linear Mold Shrinkage, Transverse	0.018 cm/cm @Temperature 240 °C	0.018 in/in @Temperature 464 °F	ASTM D3392
DuPont™ Nomex® Type 993, 120 mil Nominal Thickness Medium-Density Aromatic Nylon Pressboard Type 993 is a medium-density pressboard which offers a balance of rigidity and conformability along with outstanding saturability and excellent properties in air and oil. Typical applications includ..
Linear Mold Shrinkage, Transverse	0.018 cm/cm @Temperature 240 °C	0.018 in/in @Temperature 464 °F	ASTM D3392
DuPont™ Nomex® Type 993, 95 mil Nominal Thickness Medium-Density Aromatic Nylon Pressboard Type 993 is a medium-density pressboard which offers a balance of rigidity and conformability along with outstanding saturability and excellent properties in air and oil. Typical applications includ..
Linear Mold Shrinkage, Transverse	0.018 - 0.021 cm/cm @Thickness 4.00 mm	0.018 - 0.021 in/in @Thickness 0.157 in	Normal, 24h; ISO 294-4
DuPont Performance Polymers Delrin® 111P NC010 Acetal Homopolymer Delrin® 111P is a high viscosity acetal homopolymer with improved thermal stability and modifications for more precise molding (reduced warpage, fewer voids). It has higher tensile strength and mod..
Linear Mold Shrinkage, Transverse	0.018 - 0.020 cm/cm @Time 86400 sec	0.018 - 0.020 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP 2X04505 ETFE LNP* THERMOCOMP* 2X04505 is a compound based on ETFE resin containing Proprietary Filler(s).