Polymer Property : Linear Mold Shrinkage, Transverse = 0.020 cm/cm Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Linear Mold Shrinkage, Transverse 0.018 - 0.020 cm/cm

@Time 86400 sec
0.018 - 0.020 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP SP003 PA 12
LNP* LUBRICOMP* SP003 is a compound based on Nylon 12 resin containing 15% PTFE/Silicone. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Transverse 0.018 - 0.020 cm/cm

@Time 86400 sec
0.018 - 0.020 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP SP003 PA 12 (Asia Pacific)
LNP* Lubricomp* SP003 is a compound based on Nylon 12 resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse 0.0090 - 0.020 cm/cm

@Time 86400 sec
0.0090 - 0.020 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP ZI001XXX PPE+PS (Asia Pacific)
LNP* Lubricomp* ZI001XXX is a compound based on PPE+PS Blend resin.
Linear Mold Shrinkage, Transverse 0.018 - 0.020 cm/cm

@Time 86400 sec
0.018 - 0.020 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP KZ004 Acetal Copolymer
LNP THERMOCOMP* KZ004 is a compound based on Acetal Copolymer resin containing 20% Milled Glass.
Linear Mold Shrinkage, Transverse 0.018 - 0.020 cm/cm

@Time 86400 sec
0.018 - 0.020 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP THERMOCOMP KZ004 Acetal Copolymer
LNP THERMOCOMP* KZ004 is a compound based on Acetal Copolymer resin containing 20% Milled Glass.
Linear Mold Shrinkage, Transverse 0.018 - 0.020 cm/cm

@Time 86400 sec
0.018 - 0.020 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP KZ004 Acetal Copolymer (Asia Pacific)
LNP* THERMOCOMP* KZ004 is a compound based on Acetal Copolymer resin containing Glass Fiber, Milled Glass.
Linear Mold Shrinkage, Transverse 0.018 - 0.020 cm/cm

@Time 86400 sec
0.018 - 0.020 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP THERMOCOMP KZ004 Acetal Copolymer (Asia Pacific)
LNP* THERMOCOMP* KZ004 is a compound based on Acetal Copolymer resin containing Glass Fiber, Milled Glass.
Linear Mold Shrinkage, Transverse 0.010 - 0.020 cm/cm

@Time 86400 sec
0.010 - 0.020 in/in

@Time 24.0 hour
ASTM D 955
SABIC Innovative Plastics LNP Thermocomp WC006 Polyester, TP
LNP* Thermocomp* WC006 is a compound based on Polyester, TP resin containing Carbon Fiber.This data was supplied by SABIC-IP for the Americas region.
Linear Mold Shrinkage, Transverse 0.010 - 0.020 cm/cm

@Time 86400 sec
0.010 - 0.020 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP WC006 Polyester, TP (Asia Pacific)
LNP* Thermocomp* WC006 is a compound based on Polyester, TP resin containing Carbon Fiber.
Linear Mold Shrinkage, Transverse 0.017 - 0.020 cm/cm

@Time 86400 sec
0.017 - 0.020 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP WBL36L PBT
LNP* LUBRICOMP* WBL36L is a compound based on PBT resin containing 30% Glass Bead, 15% PTFE. Added features of this material include: Wear Resistant, Low Extractible.
Linear Mold Shrinkage, Transverse 0.010 - 0.020 cm/cm

@Time 86400 sec
0.010 - 0.020 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP WC006 PBT
LNP* THERMOCOMP* WC006 is a compound based on PBT resin containing 30% Carbon Fiber. Added feature of this grade is: Electrically Conductive.
Linear Mold Shrinkage, Transverse 0.0090 - 0.020 cm/cm

@Time 86400 sec
0.0090 - 0.020 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP THERMOTUF PF006I PA 6
LNP THERMOTUF* PF006I is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: High Impact.
Linear Mold Shrinkage, Transverse 0.018 - 0.020 cm/cm

@Time 86400 sec
0.018 - 0.020 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP 2X04505 ETFE
LNP* THERMOCOMP* 2X04505 is a compound based on ETFE resin containing Proprietary Filler(s).