Polymer Resources NY66-IM2-G33 Nylon 66, 33% Glass Reinforced, Impact Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources NY66-IM2-G33 Nylon 66, 33% Glass Reinforced, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 66, 33% Glass Reinforced, Impact Modified, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 141 MPa | 20500 psi | ASTM D638 |
| Tensile Strength, Yield | 141 MPa | 20500 psi | ASTM D638 |
| Flexural Strength | 204 MPa | 29600 psi | ASTM D790 |
| Flexural Modulus | 6.89 GPa | 1000 ksi | ASTM D790 |
| Izod Impact, Notched | 1.87 J/cm @Temperature 22.8 °C |
3.50 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0626 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 293 - 304 °C | 560 - 580 °F | |
| Middle Barrel Temperature | 277 - 288 °C | 530 - 550 °F | |
| Front Barrel Temperature | 271 - 282 °C | 520 - 540 °F | |
| Melt Temperature | 288 - 299 °C | 550 - 570 °F | |
| Mold Temperature | 65.6 - 104 °C | 150 - 220 °F | |
| Drying Temperature | 73.9 - 85.0 °C | 165 - 185 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0005 |
Users viewing this material also viewed the following: