- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 475 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 475 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| PlastiComp Complet® LGF60-PA66 MT 60% Long Glass Fiber This compound complies with European Union Directive 2002/95/EC Restriction of Hazardous Substances (RoHS).Information provided by PlastiComp, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Polymer Resources NY66-G20-MD Nylon 66, 20% Glass Reinforced with MoS2 Nylon 66, 20% Glass Reinforced with Molybdenum Disulfide for Lubrication and WearProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigment.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Polymer Resources NY66-IM2-G33-[color]-H Nylon 66, 33% Glass Reinforced, Impact Modified, Heat Stabilized Nylon 66, 33% Glass Reinforced, Impact Modified, Heat Stabilized, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, t.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Polymer Resources NY66-IM-G40 Nylon 66, 40% Glass Reinforced, Impact Modified Nylon 66, 40% Glass Reinforced, Toughened and LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon g.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C @Thickness 3.18 mm |
475 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Nymax™ GF 1200 A 40 IM Black 13A Polyamide 66 (Nylon 66) The Nymax® GF 1200 Series of glass fiber-reinforced nylon 6/6 compounds have been specifically formulated for applications requiring high stiffness, tensile properties, heat resistance, and durabil.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| PlastiComp Complet® LCF40-PA66 40% Long Carbon Fiber This compound complies with European Union Directive 2002/95/EC Restriction of Hazardous Substances (RoHS).Information provided by PlastiComp, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Ravago Manufacturing Americas Hylon® N1025HLFR Nylon 6/6, 25% Fiberglass, Heat Stabilized, Lubricated, Flame retardant (DAM) Information provided by Ravago. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | Unannealed; ASTM D648 |
| Ravago Manufacturing Americas Hylon® N1033L Nylon 6/6 (Cond)
(discontinued **) Information provided by Ravago. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 - 255 °C | 475 - 491 °F | Average value: 249 °C Grade Count:3 |
| Overview of materials for Nylon 63, 35% Glass-Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 63, 35% Glass-Filled". Each property range of values reported is minimum and maximum values of app.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C @Thickness 3.20 mm |
475 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON RX05489 PA 66 LNP* STAT-KON* RX05489 is a compound based on Nylon 66 resin containing 10% Carbon Fiber, 20% Glass Fiber, 15% PTFE/Silicone. Added features of this material include: Electrically Conductive, Wear.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Techmer ES Plaslube® J-1/CF/10/TF/13/SI/2 BK223 PA66 |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C @Thickness 3.20 mm |
475 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Thermocomp RF0059 PA 66 (Asia Pacific) LNP STARFLAM* RF0059 is a compound based on Nylon 66 resin containing Flame Retardant, Glass Fiber. Added features of this material include: Flame Retardant.This data was supplied by SABIC-IP for t.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C @Thickness 3.20 mm |
475 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP RF006 PA 66 LNP* THERMOCOMP* RF006 is a compound based on Nylon 66 resin containing 30% Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C @Thickness 3.20 mm |
475 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP RF006LXP PA 66 LNP* THERMOCOMP* RF006LXP is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Low Extractible. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Thermocomp RF00ASXP PA6.6 (Europe-Africa-Middle East) LNP* THERMOCOMP* RF00ASXP is a compound based on PA 66 resin containing Glass Fiber. Added features include: Heat Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-Middle East regi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Chase Plastics CP Pryme® NN133GLUV (COND, 50% RH) Nylon 66, 33% Glass Fiber Reinforced, Internally Lubricated, UV Stabilized Information provided by Chase Plastics. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Chase Plastics CP Pryme® NN230GL (DAM) Nylon 66, 33% Glass Fiber Reinforced, Internally Lubricated Information provided by Chase Plastics. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 GF15H 15% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 GF15H 15% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 GF15H 15% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| DuPont Performance Polymers VESPEL TP-8792 Polyimide DuPont Vespel TP-8792 parts are specified for mechanical, thermal, and tribological properties. TP-8792 offers excellent strength and toughness, dimensional stability, low outgassing, radiation resi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Eurostar Staramide RF00ASXS PA66, 50% Glass Filled, Injection Molded Staramide RF00ASXA is a 50% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Eurostar. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Adell AR-34 Nylon 66, 20% Glass Reinforced Data provided by Adell Plastics, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Adell AT-37 Nylon 66, 35% Glass Reinforced; Impact Modified Data provided by Adell Plastics, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Adell AJ-37 Nylon 66, 35% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ISO 75 |
| BASF Ultramid® A3EG3 BK00564 15% Glass Filled PA66 (Dry) Ultramid A3EG3 BK00564 is a 15% glass fiber reinforced injection molding PA66 grade. It conforms to FDA requirements of 21 CFR 177.1500. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON LX04420C PEEK LNP* STAT-KON* LX04420C is a compound based on Polyetheretherketone resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Clean Compounding Syst.. |
|||