Overview of materials for ABS/Polyester Alloy + GF

Category Polymer , Thermoplastic , ABS Polymer , ABS/Polyester Alloy + GF , Polyester, TP
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for ABS/Polyester Alloy + GF.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "ABS/Polyester Alloy + GF". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.15 - 1.61 g/cc
0.0415 - 0.0582 lb/in³
Average value: 1.42 g/cc Grade Count:27
Water Absorption 0.0800 - 0.150 %
0.0800 - 0.150 %
Average value: 0.121 % Grade Count:9
Linear Mold Shrinkage 0.00200 - 0.0110 cm/cm
0.00200 - 0.0110 in/in
Average value: 0.00463 cm/cm Grade Count:23
Mechanical Properties Metric English Comments
Hardness, Rockwell R 110 - 115
110 - 115
Average value: 113 Grade Count:4
Tensile Strength, Ultimate 50.0 - 123 MPa
7250 - 17900 psi
Average value: 91.5 MPa Grade Count:11
Tensile Strength, Yield 67.6 - 141 MPa
9800 - 20500 psi
Average value: 98.2 MPa Grade Count:17
Elongation at Break 1.20 - 4.00 %
1.20 - 4.00 %
Average value: 2.68 % Grade Count:25
Modulus of Elasticity 3.10 - 9.00 GPa
450 - 1310 ksi
Average value: 6.38 GPa Grade Count:4
Flexural Yield Strength 97.9 - 193 MPa
14200 - 28000 psi
Average value: 139 MPa Grade Count:24
Flexural Modulus 4.22 - 12.1 GPa
612 - 1760 ksi
Average value: 7.10 GPa Grade Count:24
Izod Impact, Notched 0.374 - 1.01 J/cm
0.700 - 1.90 ft-lb/in
Average value: 0.676 J/cm Grade Count:24
Izod Impact, Unnotched 4.00 - 5.07 J/cm
7.50 - 9.50 ft-lb/in
Average value: 4.36 J/cm Grade Count:3
Charpy Impact Unnotched 2.50 - 5.50 J/cm²
11.9 - 26.2 ft-lb/in²
Average value: 4.17 J/cm² Grade Count:3
Charpy Impact, Notched 0.600 - 1.20 J/cm²
2.86 - 5.71 ft-lb/in²
Average value: 0.933 J/cm² Grade Count:3
Thermal Properties Metric English Comments
CTE, linear 28.8 - 54.0 µm/m-°C
16.0 - 30.0 µin/in-°F
Average value: 40.3 µm/m-°C Grade Count:5
Deflection Temperature at 0.46 MPa (66 psi) 100 - 227 °C
212 - 440 °F
Average value: 200 °C Grade Count:22
Deflection Temperature at 1.8 MPa (264 psi) 90.0 - 208 °C
194 - 407 °F
Average value: 153 °C Grade Count:26
Vicat Softening Point 100 - 147 °C
212 - 297 °F
Average value: 127 °C Grade Count:3
UL RTI, Electrical 140 °C
284 °F
Average value: 140 °C Grade Count:7
UL RTI, Mechanical with Impact 95.0 - 100 °C
203 - 212 °F
Average value: 97.1 °C Grade Count:7
UL RTI, Mechanical without Impact 130 °C
266 °F
Average value: 130 °C Grade Count:7
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:26
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+16 - 1.00e+17 ohm-cm
1.00e+16 - 1.00e+17 ohm-cm
Average value: 5.50e+16 ohm-cm Grade Count:6
Dielectric Strength 17.7 - 20.5 kV/mm
450 - 520 kV/in
Average value: 18.4 kV/mm Grade Count:4
Processing Properties Metric English Comments
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Average value: 81.7 °C Grade Count:3