Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 50.0 - 130 MPa @Temperature -20.0 - 100 °C |
7250 - 18900 psi @Temperature -4.00 - 212 °F |
Average value: 53.1 MPa Grade Count:1 |
Overview of materials for Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled".Specific grades with glass content between 5% .. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D651 |
Resinoid 1363 Phenolic Molding, Glass Reinforced Data provided by the manufacturer.The Resinoid 1300 and 7000 glass fiber reinforced series compounds feature mechanical strength, dimensional stability, electrical insulation, and heat resistance |
|||
Tensile Strength, Ultimate | 50.0 - 205 MPa @Temperature -50.0 - 250 °C |
7250 - 29700 psi @Temperature -58.0 - 482 °F |
Average value: 124 MPa Grade Count:1 |
Overview of materials for Polyaryletherketone (PAEK), Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyaryletherketone (PAEK), Glass Fiber Filled". Each property range of values reported is minimum and m.. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ISO 527 |
Eastman EASTALLOY Polymer DA105, Natural Alloy
(discontinued **) General: All ISO tests are run @ 4-mm thickness with the exception of Impact Resistance, which is run @ 2-mm thickness. Comments: Properties reported here are typical of average lots. Eastman ma.. |
|||
Tensile Strength, Ultimate | 50.0 - 123 MPa | 7250 - 17900 psi | Average value: 91.5 MPa Grade Count:11 |
Overview of materials for ABS/Polyester Alloy + GF This property data is a summary of similar materials in the MatWeb database for the category "ABS/Polyester Alloy + GF". Each property range of values reported is minimum and maximum values of appro.. |
|||
Tensile Strength, Ultimate | 50.0 - 228 MPa | 7250 - 33000 psi | Average value: 68.5 MPa Grade Count:33 |
Overview of materials for Polycarbonate, Impact Modified This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Impact Modified". Each property range of values reported is minimum and maximum values of.. |
|||
Tensile Strength, Ultimate | 50.0 - 80.0 MPa @Temperature 60.0 - 120 °C |
7250 - 11600 psi @Temperature 140 - 248 °F |
Average value: 66.7 MPa Grade Count:1 |
Overview of materials for Polycarbonate, 30% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 30% Glass Filled". Specific grades with glass content between 25% and 34% are included. E.. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D638 |
Kleerdex Kydex® P51 Acrylic/PVC Extrusion Compound
(discontinued **) Profile extrusion compound for building productsApplications: Handrails, crashrails, bumper guards, corner guardsFeatures: Extruded profiles made with P51 are extremely resistant to harsh chemicals .. |
|||
Tensile Strength, Ultimate | 50.0 - 125 MPa @Temperature 0.000 - 160 °C |
7250 - 18100 psi @Temperature 32.0 - 320 °F |
Average value: 67.6 MPa Grade Count:4 |
Overview of materials for Polysulfone (PSU) This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone". Each property range of values reported is minimum and maximum values of appropriate MatWeb.. |
|||
Tensile Strength, Ultimate | 50.0 - 2100 MPa | 7250 - 305000 psi | Average value: 760 MPa Grade Count:22 |
Overview of materials for Epoxy/Carbon Fiber Composite This property data is a summary of similar materials in the MatWeb database for the category "Epoxy/Carbon Fiber Composite". Each property range of values reported is minimum and maximum values of a.. |
|||
Tensile Strength, Ultimate | 50.0 - 294 MPa | 7250 - 42600 psi | Average value: 182 MPa Grade Count:253 |
Overview of materials for Nylon 66, 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. .. |
|||
Tensile Strength, Ultimate | 50.0 - 165 MPa | 7250 - 23900 psi | Average value: 111 MPa Grade Count:83 |
Overview of materials for Nylon 66, Glass/Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass/Mineral Filled". Each property range of values reported is minimum and maximum values of.. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D638 |
Plenco 7080 Phenolic, Nodular, Compression Molded PLENCO 07080 is an organic fiber reinforced phenolic molding compound, offering improved mechanical strength properties along with outstanding resistance to cracking and degradation from soap and de.. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D638 |
Tipco Tipcolite® TG 211 Phenolic Compound, Mineral & Wood Flour, Soft Flow & High Electrical Properties Soft Flow Phenolic Compound, Reinforced with Mineral & Wood FlourApplications: Electrical & ElectronicsProcessing: Compression MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | DIN 53504 |
Lubrizol ESTANE® 5701F1 Ester Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability .. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D638 |
Covestro Bayblend® T 85 Polycarbonate/ABS Blend High impact and notched impact strength, little risk of brittle fracture, high dimensional accuracy.Applications: Automotive components, electrical engineering.Information provided by Bayer.As of 1 .. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | cond; ISO 527-1/-2 |
DSM Akulon® K224-PG2 PA6-I-GF8 8% Glass Reinforced, Impact Modified |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D638 |
Covestro Bayblend® T 65 Polycarbonate/ABS Blend High impact and notched impact strength, little risk of brittle fracture, high dimensional accuracy.Applications: Interior automotive components.Information provided by Bayer.As of 1 September 2015,.. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ATSM D638 |
Ashley Polymers Ashlene® 257 PPO A high flow grade for applications requiring high impact strength, heat resistance and dimensional stability.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ATSM D638 |
Ashley Polymers Ashlene® ABS Resin F-214 General purpose, medium impact resin.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 420 Polyester - PBT, Glass/Mineral Reinforced Data provided by the manufacturer, ComAlloy International Company.30% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ATSM D638 |
Ashley Polymers Ashlene® 279 PPO Alloy A general purpose, paintable injection molding grade with high chemical resistance and mechanical performance. Good heat resistance with dimensional stability in dark gray or black only.Data provid.. |
|||
Tensile Strength, Ultimate | 50.0 - 90.0 MPa | 7250 - 13100 psi | Average value: 73.5 MPa Grade Count:7 |
Overview of materials for Nylon 66, Nucleated This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Nucleated". Each property range of values reported is minimum and maximum values of appropriat.. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ATSM D638 |
Ashley Polymers Ashlene® R190TB Acetal Impact modified reprocessed copolymer, excellent toughness, strength, stiffness and lubricity. Black.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 50.0 - 80.0 MPa @Temperature 160 - 160 °C |
7250 - 11600 psi @Temperature 320 - 320 °F |
Average value: 70.2 MPa Grade Count:1 |
Overview of materials for Polyethersulfone (PES), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% .. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | |
Kraton® G1657 + PA-6 blend (16/4/80) Blending KRATON D and G polymers with PA significantly improves the toughness at both room and low temperatures. KRATON polymers are block segments of styrene and rubber monomers (A-B, A-B-A, or [A.. |
|||
Tensile Strength, Ultimate | 50.0 - 70.0 MPa | 7250 - 10200 psi | ASTM D638 |
Chang Chun Plastic PBT2000 Fire Retardant PBT Information provided by Dowell Trading Company Ltd. |
|||
Tensile Strength, Ultimate | 50.0 - 170 MPa @Temperature -40.0 - 120 °C |
7250 - 24700 psi @Temperature -40.0 - 248 °F |
Average value: 83.0 MPa Grade Count:2 |
Overview of materials for Polyethylene Terephthalate (PET), Glass Fiber Filled, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), Glass Fiber Filled, Flame Retardant". Each property range of values re.. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D638 |
Sumitomo Bakelite North America FM 4008 Fiberglass and Mineral Reinforced Phenolic Resole FM 4008 is a fiberglass and mineral reinforced phenolic resole compound, with excellent dimensional stability and good strength at elevated temperatures. Information supplied by Sumitomo Bak North A.. |
|||
Tensile Strength, Ultimate | 50.0 - 90.0 MPa @Temperature 60.0 - 150 °C |
7250 - 13100 psi @Temperature 140 - 302 °F |
Average value: 71.3 MPa Grade Count:2 |
Overview of materials for Polysulfone, 20% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% are inc.. |