Polymer Property : Modulus of Elasticity = 1310 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Modulus of Elasticity	6.00 - 9.00 GPa	870 - 1310 ksi	Compression; ISO 527
Raschig Group 2567 AMC Glass fiber-reinforced and inorganically filled polyester molding compound (UP) in various colors. Outstanding mechanical strength similar to BMC/SMC, very good electrical isolation properties and ..
Modulus of Elasticity	6.00 - 9.00 GPa	870 - 1310 ksi	Compression; ISO 527
Raschig Group 2568 AMC Glass fiber-reinforced polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, heat resistant up to 500°C for short time - usable for s..
Modulus of Elasticity	6.00 - 9.00 GPa	870 - 1310 ksi	Compression; ISO 527
Raschig Group 5553 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona..
Modulus of Elasticity	7.00 - 9.00 GPa	1020 - 1310 ksi	Injection; ISO 527
Raschig Group DECAL® 666/8/2B Phenolic Glass-fiber reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and mechanical properties. This product meets the allowe..
Modulus of Elasticity	7.00 - 9.00 GPa	1020 - 1310 ksi	ISO 527
Raschig Group EN 5004 Epoxy Molding Compound Mica reinforced molding compound. Low mold shrinkage and post-shrinkage, very good electrical values, outstanding heat resistance, very goo pourablity. This product meets the allowed upper limits fo..
Modulus of Elasticity	7.00 - 9.00 GPa	1020 - 1310 ksi	ISO 527
Raschig Group EN 5007 Epoxy Molding Compound Mica reinforced molding compound. Low mold shrinkage and post-shrinkage, very good electrical values, outstanding heat resistance, very goo pourablity. This product meets the allowed upper limits fo..
Modulus of Elasticity	7.00 - 9.00 GPa	1020 - 1310 ksi	Compression; ISO 527
Raschig Group MELOPAS® 156 MF Melamine Glass fiber reinforced Melamine molding compound. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 200..
Modulus of Elasticity	6.00 - 9.00 GPa	870 - 1310 ksi	Injection and Compression; ISO 527
Raschig Group RALUPOL® 4802 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, good electrical values, excellent heat resistance, outstanding pourability. This product meets the allowed u..
Modulus of Elasticity	3.10 - 9.00 GPa	450 - 1310 ksi	Average value: 6.38 GPa Grade Count:4
Overview of materials for ABS/Polyester Alloy + GF This property data is a summary of similar materials in the MatWeb database for the category "ABS/Polyester Alloy + GF". Each property range of values reported is minimum and maximum values of appro..
Modulus of Elasticity	6.00 - 9.00 GPa	870 - 1310 ksi	Injection and Compression; ISO 527
Raschig Group RALUPOL® 802 UP Polyester Glass-fiber reinforced polyester molding compound. Low molding shrinkage and post-shrinkage, good electrical values, good mechanical strength, good heat resistance. This product meets the allowed up..
Modulus of Elasticity	6.00 - 9.00 GPa	870 - 1310 ksi	Injection and Compression; ISO 527
Raschig Group RALUPOL® 804 UP Polyester Glass-fiber reinforced polyester molding compound. Low molding shrinkage and post-shrinkage, good electrical values, good mechanical strength. This product meets the allowed upper limits for heavy m..
Modulus of Elasticity	1.90 - 9.00 GPa @Temperature 50.0 - 200 °C	276 - 1310 ksi @Temperature 122 - 392 °F	Average value: 7.30 GPa Grade Count:7
Overview of materials for Polysulfone (PSU) This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone". Each property range of values reported is minimum and maximum values of appropriate MatWeb..
Modulus of Elasticity	1.64 - 9.00 GPa	238 - 1310 ksi	Average value: 4.66 GPa Grade Count:52
Overview of materials for Nylon 6, 30% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Mineral Filled". Specific grades with primary filler content between 25% and 34% are includ..
Modulus of Elasticity	7.00 - 9.00 GPa @Temperature 70.0 - 70.0 °C	1020 - 1310 ksi @Temperature 158 - 158 °F	Average value: 5.80 GPa Grade Count:1
Overview of materials for Nylon 6, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. E..
Modulus of Elasticity	7.00 - 9.00 GPa @Time 180000 - 1.44e+6 sec	1020 - 1310 ksi @Time 50.0 - 400 hour	Average value: 5.80 GPa Grade Count:1
Overview of materials for Nylon 6, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. E..
Modulus of Elasticity	6.00 - 9.00 GPa	870 - 1310 ksi	Compression; ISO 527
Raschig Group 5567 DAP Diallyl Phthalate (DAP), Cast, Mineral Filler Glass-fiber reinforced diallyl phthalate molding compound free from halogens. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exc..
Modulus of Elasticity	6.00 - 9.00 GPa	870 - 1310 ksi	Injection and Compression; ISO 527
Raschig Group DECAL® 152CL Phenolic Glass-fiber and mineral reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and mechanical properties. This product meet..
Modulus of Elasticity	7.00 - 9.00 GPa	1020 - 1310 ksi	Injection and Compression; ISO 527
Raschig Group RESINOL® 400 EPF Phenolic Glass-fiber reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and very good mechanical properties. This product meets ..
Modulus of Elasticity	5.86 - 9.00 GPa	850 - 1310 ksi	Average value: 8.07 GPa Grade Count:12
Overview of materials for Polyphenylene Ether, 30% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, 30% Glass Filled". Specific grades with glass content between 25% and 34% are inclu..
Modulus of Elasticity	4.50 - 9.00 GPa	653 - 1310 ksi	Average value: 6.20 GPa Grade Count:5
Overview of materials for Polyphenylene Ether + Styrene-Butadiene Blend, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether + Styrene-Butadiene Blend, Glass Filled". Each property range of values reported is ..
Modulus of Elasticity	8.00 - 9.00 GPa	1160 - 1310 ksi	Average value: 8.56 GPa Grade Count:8
Overview of materials for Polysulfone, 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are inc..
Modulus of Elasticity	7.00 - 9.00 GPa @Temperature 60.0 - 160 °C	1020 - 1310 ksi @Temperature 140 - 320 °F	Average value: 7.94 GPa Grade Count:2
Overview of materials for Polysulfone, 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are inc..