Nilit Nilamid A3 H G3 ZB 13% Glass Reinforced High Impact PA66

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled
Manufacturer Nilit
Trade Name Nilamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Nilit Nilamid A3 H G3 ZB 13% Glass Reinforced High Impact PA66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Nilamid A3 H G3 ZB (13% Glass Reinforced) was developed for applications that require a combination of high stiffness and good elongation or impact resistance. It is widely used for applications that need the strength and stiffness of reinforced polyamide, but also need to be snap fitted.Key characteristics: Good stiffness and strengthExcellent impact resistanceHigh elongationGood moldabilityInformation provided by NILIT.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ASTM D792, ISO 1183
Water Absorption 1.0 %
1.0 %
23°C, 24h in H<sub>2</sub>O; sim. ISO 62
Water Absorption at Saturation 6.0 %
6.0 %
sim. ISO 62
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
Euronil
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
Euronil
Mechanical Properties Metric English Comments
Tensile Strength, Yield 90.0 MPa
13100 psi
ISO 527, ASTM D638
Elongation at Break 4.0 %
4.0 %
ISO 527, ASTM D638
Flexural Yield Strength 150 MPa
21800 psi
ISO 178, ASTM D790
Flexural Modulus 3.80 GPa
551 ksi
ISO 178, ASTM D790
Izod Impact, Notched (ISO) 7.00 kJ/m²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
ISO 180/1A
12.0 kJ/m²

@Temperature 23.0 °C
5.71 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Charpy Impact, Notched 1.30 J/cm²
6.19 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 85.0 °C
185 °F
20,000 hr; IEC 216
Deflection Temperature at 1.8 MPa (264 psi) 238 °C
460 °F
ISO 75, ASTM D648
Vicat Softening Point 240 °C
464 °F
49 N; ISO 306, ASTM D1525
255 °C
491 °F
9.8 N; ISO 306, ASTM D1525
Flammability, UL94 HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Glow Wire Test 650 °C

@Thickness 3.20 mm
1200 °F

@Thickness 0.126 in
Glow Wire Flammability Index; IEC 694-2-12
650 °C

@Thickness 0.800 mm
1200 °F

@Thickness 0.0315 in
Glow Wire Flammability Index; IEC 694-2-12
Electrical Properties Metric English Comments
Comparative Tracking Index 350 V

@Thickness 3.20 mm
350 V

@Thickness 0.126 in
Sol. B; IEC 112, UL 746A
500 V

@Thickness 3.20 mm
500 V

@Thickness 0.126 in
Sol. A; IEC 112, UL 746A
Processing Properties Metric English Comments
Nozzle Temperature 280 - 295 °C
536 - 563 °F
Zone 1 270 - 290 °C
518 - 554 °F
hopper
Zone 2 275 - 290 °C
527 - 554 °F
Zone 3 280 - 295 °C
536 - 563 °F
Zone 4 280 - 295 °C
536 - 563 °F
Melt Temperature 275 - 300 °C
527 - 572 °F
Do not melt above 300°C
Mold Temperature 90.0 - 110 °C
194 - 230 °F
Preferred
Drying Temperature 80.0 - 85.0 °C
176 - 185 °F
Dry Time 4 hour
4 hour
Injection Pressure 70.0 - 100 MPa
10200 - 14500 psi
Descriptive Properties Value Comments
Clamping Force in tons, 0.7 times the projected surface area in cm2
Heat Resistance - Ball Test OK
at 125°C, IEC 309
OK
at 165°C, IEC 309
Holding Pressure 90 Mpa