- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 460 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 460 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C @Thickness 6.35 mm |
460 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| PolyOne Therma-Tech™ NN-3000 TC Polyamide 66 (Nylon 66) Therma-Tech™ Thermal Management Compounds have been engineered to combine the heat transfer and cooling capabilities of metals with the design freedom, weight reduction and cost advantages of therm.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C @Thickness 3.20 mm |
460 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Ovation Polymers Opnyl OP66GF15 Nylon 66, 14% Glass Reinforced Nylon 66 - Glass reinforced (14 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Unannealed; ASTM D648 |
| Oxford Polymers PPS/66-505-40GF-BK PPS/PA66, 40% Glass Fiber Reinforced Product Description: Glass Fiber (40% Reinforced), Polyphenylene sulfide injection molding grade based alloy with Nylon 66 Processing and Delivery Form: Pellets and Injection MoldingAppearance: Bla.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | ASTM D648 |
| Niche Polymer PA66GI14BK Nylon 66, 14% Glass Fiber Filled, Impact Modified Information provided by Niche Polymer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C @Thickness 3.20 mm |
460 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics EXTEM UH1006 TPI Blend High Heat Amorphous TPI Blend, Excellent Chemical Resistance, High Continuous Use Temperature (CUT), Best-in-class FR, OSU and LOI. Material is UL-listed. This material is RoHS compliant and also ha.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Unannealed (0.250"); ASTM D648 |
| LTL Color Compounds ColorFast® NY2GF130 Nylon 66, 13% Glass-Filled 13% glass-filled nylon 6,6All information provided by LTL Color Compounders, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | ISO 75-1,-2 |
| Gromax CFG45-RN13N1 Nylon 6 46% Glass Filled (Conditioned) Information provided by Gromax Enterprises Corp. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C @Thickness 3.20 mm |
460 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP RX03643H PA 66 LNP* LUBRICOMP* RX03643H is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C @Thickness 3.20 mm |
460 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP RX03643H PA 66 (Asia Pacific) LNP* Lubricomp* RX03643H is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRILOY RF206 PA 66 (Europe-Africa-Middle East) LNP LUBRILOY* RF206H is a compound based on Nylon 66 resin containing Glass Fiber, Lubricants, Proprietary Lubricant. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRILOY RF208 PA 66 LNP LUBRILOY* RF208 is a compound based on Nylon 66 resin containing 40% Glass Fiber, Proprietary Lubricant. Added features of this material include: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 238 °C | >= 460 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON RX98063 PA 66 (Europe-Africa-Middle East) LNP* STAT-KON* RX98063 is a compound based on PA 66 resin containing Glass Fiber, Stainless Steel Fiber. Added features include; Antistatic. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/6 GF33 TL10 HS 33% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 33% Filler by WeightAdditive: Heat Stabilizer and PTFE Lubricant(10%)Features: Lubricated, Good Wear Resistance, Heat Stab.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Thermocomp RFB24 PA 66 (Europe-Africa-Middle East) LNP* THERMOCOMP* RFB24 is a compound based on PA 66 resin containing Glass Bead, Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | ISO 75-1, 2 |
| Polyplastics FR-PET® B3030FA Glass Fiber Reinforced Polyethylene Terephthalate (GF-PET), Slow burning, General purpose Information provided by PolyPlastics. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | ISO 75-1, 2 |
| Polyplastics FR-PET® C3030FA Glass Fiber Reinforced Polyethylene Terephthalate (GF-PET), Slow burning, General purpose Information provided by PolyPlastics. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | ASTM D648 |
| Resinoid 2016 Phenolic Molding, Fabric Reinforced Data provided by the manufacturer.The Resinoid 2000 organic fiber reinforced series compounds feature mechanical strength, dimensional stability, and shock resistance |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | ASTM D648 |
| Chase Plastics CP Pryme® NN133GTL (DAM) Nylon 66, 33% Glass Fiber Reinforced, Toughened, Internally Lubricated Information provided by Chase Plastics. |
|||