Murtfeldt Murylon® A GF Nylon 66, Glass Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Reinforced, Impact Grade
Manufacturer Murtfeldt Kunststoffe GmbH & Co
Trade Name Murylon®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Murtfeldt Murylon® A GF Nylon 66, Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Murylon® A’s impressive characteristics are enhanced with admixed glass fibers. This results in a clear improvement in cold flow behavior and dimensional stability, enabling higher static pressure loads to be endured.Special Properties:• Improved compressive strength• Excellent cold flow behavior• Increased rigidity• Excellent dimensional stability• Low moisture absorptionInformation provided by Murtfeldt Kunststoffe GmbH & Co. KG.
Physical Properties Metric English Comments
Density 1.29 g/cc
0.0466 lb/in³
ISO 1183-1
Moisture Absorption at Equilibrium 1.7 %

@Temperature 23.0 °C
1.7 %

@Temperature 73.4 °F
50% RH
Water Absorption at Saturation 5.5 %

@Temperature 23.0 °C
5.5 %

@Temperature 73.4 °F
Mechanical Properties Metric English Comments
Hardness, Rockwell M 76
76
dry; ISO 2039-2
Hardness, Shore D 82
82
DIN 53505
Ball Indentation Hardness 165 MPa
23900 psi
dry; ISO 2039-1
Tensile Strength at Break 100 MPa
14500 psi
dry; ISO 527-1
100 MPa
14500 psi
50% RH; ISO 527-1
Elongation at Break 5.0 %
5.0 %
dry; ISO 527-1
12 %
12 %
50% RH; ISO 527-1
Creep Strength 18.0 MPa

@Time 3.60e+6 sec
2610 psi

@Time 1000 hour
stress leading to 1% elongation; 50% RH; ISO 899-1
26.0 MPa

@Time 3.60e+6 sec
3770 psi

@Time 1000 hour
stress leading to 1% elongation; dry; ISO 899-1
Modulus of Elasticity 3.20 GPa
464 ksi
50% RH
5.90 GPa
856 ksi
dry
Compressive Yield Strength 28.0 MPa

@Strain 1.00 %
4060 psi

@Strain 1.00 %
dry; ISO 604
55.0 MPa

@Strain 2.00 %
7980 psi

@Strain 2.00 %
dry; ISO 604
90.0 MPa

@Strain 5.00 %
13100 psi

@Strain 5.00 %
dry; ISO 604
Charpy Impact Unnotched 5.00 J/cm²
23.8 ft-lb/in²
dry; ISO 179-1/1eU
>= 5.00 J/cm²
>= 23.8 ft-lb/in²
ISO 179
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
dry; ISO 179-1/1eA
Coefficient of Friction, Dynamic 0.35
0.35
Sand Slurry 0.28
0.28
µm/km
Thermal Properties Metric English Comments
CTE, linear 50.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
27.8 µin/in-°F

@Temperature 73.4 - 140 °F
60.0 µm/m-°C

@Temperature 23.0 - 100 °C
33.3 µin/in-°F

@Temperature 73.4 - 212 °F
Thermal Conductivity 0.300 W/m-K
2.08 BTU-in/hr-ft²-°F
Melting Point 260 °C
500 °F
ISO 11357-1
Maximum Service Temperature, Air 110 °C

@Time 7.20e+7 sec
230 °F

@Time 20000 hour
120 °C

@Time 1.80e+7 sec
248 °F

@Time 5000 hour
200 °C

@Time <=86400 sec
392 °F

@Time <=24.0 hour
Minimum Service Temperature, Air -20.0 °C
-4.00 °F
Glass Transition Temp, Tg 60.0 °C
140 °F
ISO 11357-1
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Electrical Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
50% RH; IEC 60093
>= 1.00e+14 ohm-cm
>= 1.00e+14 ohm-cm
dry; IEC 60093
Surface Resistance >= 1.00e+12 ohm
>= 1.00e+12 ohm
50% RH; IEC 60093
>= 1.00e+13 ohm
>= 1.00e+13 ohm
dry; IEC 60093
Dielectric Constant 3.6

@Frequency 1.00e+6 Hz
3.6

@Frequency 1.00e+6 Hz
dry; IEC 60250
3.90

@Frequency 1.00e+6 Hz
3.90

@Frequency 1.00e+6 Hz
50% RH; IEC 60250
3.9

@Frequency 100 Hz
3.9

@Frequency 100 Hz
dry; IEC 60250
6.9

@Frequency 100 Hz
6.9

@Frequency 100 Hz
50% RH; IEC 60250
Dielectric Strength 20.0 kV/mm
508 kV/in
50% RH; IEC 60243-1
30.0 kV/mm
762 kV/in
dry; IEC 60243-1
Dielectric Loss Index 0.012

@Frequency 100 Hz
0.012

@Frequency 100 Hz
dry; IEC 60250
0.014

@Frequency 1.00e+6 Hz
0.014

@Frequency 1.00e+6 Hz
dry; IEC 60250
0.040

@Frequency 1.00e+6 Hz
0.040

@Frequency 1.00e+6 Hz
50% RH; IEC 60250
0.19

@Frequency 100 Hz
0.19

@Frequency 100 Hz
50% RH; IEC 60250
Compliance Properties Metric English Comments
FDA Yes
Yes
Descriptive Properties Value Comments
Color Black