LNP Thermocomp® SF-1006 Polyamide 12, Glass Fiber Reinforcement (discontinued **)

Category	Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LNP Thermocomp® SF-1006 Polyamide 12, Glass Fiber Reinforcement (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.

Physical Properties	Metric	English	Comments
Specific Gravity	1.24 g/cc	1.24 g/cc	Method A; ASTM D792
Water Absorption	0.10 %	0.10 %	at 24 hrs; ASTM D570
Linear Mold Shrinkage	0.0020 - 0.0030 cm/cm	0.0020 - 0.0030 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.0070 - 0.0080 cm/cm	0.0070 - 0.0080 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	106 MPa	15400 psi	ASTM D638
Tensile Strength, Yield	107 MPa	15500 psi	ASTM D638
Elongation at Break	4.7 %	4.7 %	ASTM D638
Elongation at Yield	4.2 %	4.2 %	ASTM D638
Tensile Modulus	6.55 GPa	950 ksi	ASTM D638
Flexural Strength	165 MPa	23900 psi	ASTM D790
Flexural Modulus	5.86 GPa	850 ksi	ASTM D790
Izod Impact, Notched	1.49 J/cm @Thickness 3.18 mm	2.79 ft-lb/in @Thickness 0.125 in	ASTM D256
Izod Impact, Unnotched	9.50 J/cm @Thickness 3.18 mm	17.8 ft-lb/in @Thickness 0.125 in	ASTM D256
Izod Impact, Notched (ISO)	15.0 kJ/m²	7.14 ft-lb/in²	ISO 180
Izod Impact, Unnotched (ISO)	58.1 kJ/m²	27.6 ft-lb/in²	ISO 180
Falling Dart Impact	13.0 J	9.59 ft-lb	ASTM D3763
Impact Test	3.61 J	2.66 ft-lb	Multi-Axial Instrumented Impact Energy; ISO 6603-2

Thermal Properties	Metric	English	Comments
CTE, linear	43.0 µm/m-°C @Temperature 20.0 °C	23.9 µin/in-°F @Temperature 68.0 °F	TMA; ASTM E831
CTE, linear, Transverse to Flow	110 µm/m-°C @Temperature 20.0 °C	61.1 µin/in-°F @Temperature 68.0 °F	TMA; ASTM E831
Deflection Temperature at 1.8 MPa (264 psi)	164 °C	327 °F	Unannealed; ASTM D648

Processing Properties	Metric	English	Comments
Melt Temperature	227 - 235 °C	441 - 455 °F
Mold Temperature	71.1 - 82.2 °C	160 - 180 °F
Drying Temperature	82.2 °C	180 °F
Dry Time	4 hour	4 hour
Moisture Content	0.020 %	0.020 %	Suggested
Back Pressure	0.172 - 0.345 MPa	24.9 - 50.0 psi