Polymer Property : Tensile Strength at Break = 15400 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 106 MPa
15400 psi
cond.; ISO 527-1, -2; 5 mm/min
Lanxess Durethan® BKV 30 G W1 901317 Nylon 6, Glass Fiber Reinforced
PA 6, 30% glass fibers, injection molding, weather stabilizedInformation provided by LANXESS.
Tensile Strength at Break 106 MPa
15400 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL SE1GFN2 PPE+PS
PPE+PS blend. 20% Glass reinforced. Non-brominated, non-chlorinated FR system. UL94 V1 and 5VA listing. RTI 110/105/110. Dielectric strength. Dimensional stability. Suitable for E/E applications.
Tensile Strength at Break 106 MPa
15400 psi
ISO 527
SABIC Innovative Plastics LNP LUBRICOMP WFL369 PBT
LNP* Lubricomp* WFL369 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Ret..
Tensile Strength at Break 106 MPa
15400 psi
ISO 527
SABIC Innovative Plastics LNP LUBRICOMP WFL369 PBT (Asia Pacific)
LNP* Lubricomp* WFL369 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Ret..
Tensile Strength at Break 106 MPa
15400 psi
ASTM D638
SABIC Innovative Plastics LNP STAT-KON AE004 ABS (Asia Pacific)
LNP* STAT-KON* AE004 is a compound based on Acrylonitrile Butadiene Styrene resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
Tensile Strength at Break 106 MPa
15400 psi
ASTM D638
SABIC Innovative Plastics LNP STAT-KON AX02747 ABS (Asia Pacific)
LNP* Stat-kon* AX02747 is a compound based on Acrylonitrile Butadiene Styrene resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive.
Tensile Strength at Break 106 MPa
15400 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics Valox® 830 PBT
30% GR PBTP, excellent surface finish. Typical applications are hot air gun housing assemblies, industrial glue guns, appliance housings and handles.
Tensile Strength at Break 106 MPa
15400 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics Valox® 830 PBT (Asia Pacific)
30% GR PBTP, excellent surface finish. Typical applications are hot air gun housing assemblies, industrial glue guns, appliance housings and handles.
Tensile Strength at Break 106 MPa
15400 psi
Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Valox® 830R PBT (Asia Pacific)
30% glass filled, release grade, polyester alloy.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength at Break 106 MPa
15400 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON Noryl_NC2525 PPE+HIPS (Europe-Africa-Middle East)
LNP* Stat-kon* Noryl_NC2525 compound is a 25% CFR PPE+PS. Highly conductive. High heat. May be added to similar material/regrind to add some conductivity to the blend.
Tensile Strength at Break 106 MPa
15400 psi
ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF006ER PC
LNP THERMOCOMP* DF006ER is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material include: Easy Molding, Mold Release.
Tensile Strength at Break 106 MPa
15400 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP JF002 PES (Europe-Africa-Middle East)
LNP* Thermocomp* JF002 is a compound based on Polyethersulfone resin containing Glass Fiber.
Tensile Strength at Break 106 MPa
15400 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP Noryl_PCN2910 PPE+PS
LNP* Thermodcomp* Noryl_PCN2910 compound is a 35% Glass/Mica filled. High modulus and tight tolerance molding for the chassis market.
Tensile Strength at Break 106 MPa
15400 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP PF002 PA 6
LNP THERMOCOMP* PF002 is a compound based on Nylon 6 resin containing 10% Glass Fiber.
Tensile Strength at Break 106 MPa
15400 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP SF006 PA 12
LNP THERMOCOMP* SF006 is a compound based on Nylon 12 resin containing 30% Glass Fiber.
Tensile Strength at Break 106 MPa
15400 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOTUF WF006I PBT
LNP THERMOTUF* WF006I is a compound based on PBT containing 30% Glass Fiber. Added features of this material include: High Impact.
Tensile Strength at Break 106 MPa
15400 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON KE002 ACETAL
LNP* STAT-KON* KE002 is a compound based on Acetal resin containing 10% Carbon Fiber. Added feature of this material is: Electrically Conductive.
Tensile Strength at Break 106 MPa
15400 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics Valox® 430 PBT
33 % glass reinforced, impact modified. Connectors, etc.
Tensile Strength at Break 106 MPa
15400 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP Noryl_PCN2910 PPE+PS (Asia Pacific)
35% Glass/Mica filled. High modulus and tight tolerance molding for the chassis market.
Tensile Strength at Break 106 MPa
15400 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP Noryl_PX2926 PPE+HIPS (Europe-Africa-Middle East)
LNP* Thermocomp* Noryl_PX2926 compound is a reinforced high modulus PPE+PS. 5VA rated at 2.5 in black and at 3.0 in gray.
Tensile Strength at Break 106 MPa
15400 psi
ASTM D 638
SABIC Innovative Plastics LNP Thermocomp SF006S PA 12
LNP* Thermocomp* SF006S is a compound based on Nylon 12 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Americas re..
Tensile Strength at Break 106 MPa
15400 psi
ISO 527-2
Borealis Xmod™ GD301FE Polypropylene, Glass Fiber Reinforced
Xmod™ GD301FE is a 30 % chemically coupled high performance glass fiber reinforced polypropylene compound intended for injection molding. This material shows excellent mechanical properties also a..
Tensile Strength at Break 106 MPa
15400 psi
ASTM D638
BLUESTAR 201-G20202 PBT, 20% Glass Filled
Typical Applications: Energy saving lighting, E/E applicationsInformation provided by Polymer Technology and Services, LLC (PTS).
Tensile Strength at Break 106 MPa
15400 psi
ASTM D638
LNP Thermocomp® SF-1006 Polyamide 12, Glass Fiber Reinforcement  (discontinued **)
Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names..
Tensile Strength at Break 106 MPa
15400 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® 3412HF PC (Asia Pacific)
20% glass reinforced, high flow PC. UL rated V-1 at 0.059"",
Tensile Strength at Break 106 MPa
15400 psi
ASTM D 638
SABIC Innovative Plastics LNP Thermotuf WF006I Polyester, TP
LNP THERMOTUF* WF006I is a compound based on Polyester, TP resin containing Glass Fiber. Added features of this material include: High Impact.This data was supplied by SABIC-IP for the Americas reg..