Aardvark Polymers Aarlon® 2000 Rotational Molding Resin, 50% RH

Category	Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer	Gehrig & Associates
Trade Name	Aarlon®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Aardvark Polymers Aarlon® 2000 Rotational Molding Resin, 50% RH.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Aarlon® 2000 PA 6/6 is a high performance nylon for rotational molding applications. Aarlon® 2000 offers high heat capabilities with exceptional mechanical properties.Information provided by Gehrig & Associates

Physical Properties	Metric	English	Comments
Density	1.14 g/cc	0.0412 lb/in³	ASTM D792
Water Absorption	1.2 %	1.2 %	Immersion 24h; ASTM D570
Moisture Absorption at Equilibrium	2.6 %	2.6 %	ISO 62
Water Absorption at Saturation	8.5 %	8.5 %	ASTM D570
Linear Mold Shrinkage	0.014 cm/cm @Thickness 2.00 mm	0.014 in/in @Thickness 0.0787 in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.014 cm/cm @Thickness 2.00 mm	0.014 in/in @Thickness 0.0787 in	ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	77.0 MPa	11200 psi	ASTM D638
Tensile Strength, Yield	55.0 MPa	7980 psi	ISO 527
	58.0 MPa	8410 psi	ASTM D638
Elongation at Break	>= 300 %	>= 300 %	ASTM D638
Elongation at Yield	25 %	25 %	ASTM D638
	25 %	25 %	ISO 527
Tensile Modulus	1.40 GPa	203 ksi	ISO 527
Flexural Modulus	1.20 GPa	174 ksi	ISO 178
Izod Impact, Unnotched	1.12 J/cm	2.10 ft-lb/in	ASTM D256
	0.270 J/cm @Temperature -40.0 °C	0.506 ft-lb/in @Temperature -40.0 °F	ASTM D256
Izod Impact, Notched (ISO)	12.0 kJ/m²	5.71 ft-lb/in²	ISO 180/1A
Charpy Impact, Notched	1.50 J/cm²	7.14 ft-lb/in²	ISO 179/1eA
	0.300 J/cm² @Temperature -30.0 °C	1.43 ft-lb/in² @Temperature -22.0 °F	ISO 179/1E
	0.450 J/cm² @Temperature -30.0 °C	2.14 ft-lb/in² @Temperature -22.0 °F	ISO 179/1EA
Tensile Impact Strength	504 kJ/m²	240 ft-lb/in²	Long Specimen; ISO 179/1eA
	1470 kJ/m²	699 ft-lb/in²	ISO 179/1eA

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+13 ohm-cm	1.00e+13 ohm-cm	ASTM D257
Dielectric Constant	4.6 @Frequency 100 Hz	4.6 @Frequency 100 Hz	ASTM D150
	7.0 @Frequency 1000 Hz	7.0 @Frequency 1000 Hz	ASTM D150
	8.0 @Frequency 1e+6 Hz	8.0 @Frequency 1e+6 Hz	ASTM D150
Dissipation Factor	0.10 @Frequency 1e+6 Hz	0.10 @Frequency 1e+6 Hz	ASTM D150
	0.20 @Frequency 100 Hz	0.20 @Frequency 100 Hz	ASTM D150
	0.20 @Frequency 1000 Hz	0.20 @Frequency 1000 Hz	ASTM D150