- Kingfa PBT-G15 15% Glass Fiber Reinforced PBT
Kingfa PBT-G15 15% Glass Fiber Reinforced PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled |
| Manufacturer | Kingfa Sci. & Tech. Co. |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kingfa PBT-G15 15% Glass Fiber Reinforced PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features:Good size stabilityHigh mechanical propertiesHigh heat resistanceExcellent balance propertiesApplications:Injection moldingApplication partsAuto handleDoor latchE & E partsInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc @Temperature 23.0 °C |
1.42 g/cc @Temperature 73.4 °F |
ASTM D792 |
| Water Absorption | 0.060 % @Temperature 23.0 °C, Time 86400 sec |
0.060 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.011 cm/cm @Temperature 23.0 °C |
0.0050 - 0.011 in/in @Temperature 73.4 °F |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength at Break | 100 MPa | 14500 psi | 10mm/min; ASTM D638 |
| Elongation at Break | 3.5 % | 3.5 % | 10mm/min; ASTM D638 |
| Flexural Strength | 150 MPa | 21800 psi | 2mm/min; ASTM D790 |
| Flexural Modulus | 5.00 GPa | 725 ksi | 2mm/min; ASTM D790 |
| Izod Impact, Notched | 0.950 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.78 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C @Thickness 6.40 mm |
419 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C @Thickness 6.40 mm |
406 °F @Thickness 0.252 in |
ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 - 1.65 mm |
HB @Thickness 0.0591 - 0.0650 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 270 °C | <= 518 °F | |
| Rear Barrel Temperature | 220 - 240 °C | 428 - 464 °F | Start Point: 230°C |
| Middle Barrel Temperature | 230 - 250 °C | 446 - 482 °F | Start Point: 240°C |
| Front Barrel Temperature | 240 - 260 °C | 464 - 500 °F | Start Point: 250°C |
| Melt Temperature | 240 - 260 °C | 464 - 500 °F | Start Point: 250°C |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | Start Point: 60°C |
| Drying Temperature | 120 - 140 °C @Time 10800 - 18000 sec |
248 - 284 °F @Time 3.00 - 5.00 hour |
Pre-dry |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Glass Fiber Content (%) | 15 | |
| Injection Speed | Moderate to High |