- Polymer Property : Linear Mold Shrinkage = 0.011 cm/cm
Polymer Property : Linear Mold Shrinkage = 0.011 cm/cm Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage | 0.0080 - 0.011 cm/cm @Thickness 3.17 mm |
0.0080 - 0.011 in/in @Thickness 0.125 in |
|
| Ovation Polymers Opnyl OP66UT105 Nylon 66 Ultra Tough - High Impact, Excellent retention of mechanical properties, High service temperature. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All.. |
|||
| Linear Mold Shrinkage | 0.0090 - 0.011 cm/cm | 0.0090 - 0.011 in/in | With Flow; ISO 2577 |
| Polykemi AB POLYelast TPE EC88R Thermoplastic Elastomer, PP/EPDM Information provided by Polykemi AB |
|||
| Linear Mold Shrinkage | 0.0090 - 0.011 cm/cm | 0.0090 - 0.011 in/in | With Flow; ISO 2577 |
| Polykemi AB POLYfill PP EIP5025 F VT2 Polypropylene, Mineral Reinforced, Extrusion grade, Low CLTE Information provided by Polykemi AB |
|||
| Linear Mold Shrinkage | 0.0090 - 0.011 cm/cm | 0.0090 - 0.011 in/in | Across Flow; ISO 2577 |
| Polykemi AB POLYfill PP EIP5025 F VT2 Polypropylene, Mineral Reinforced, Extrusion grade, Low CLTE Information provided by Polykemi AB |
|||
| Linear Mold Shrinkage | 0.0030 - 0.011 cm/cm | 0.0030 - 0.011 in/in | FRISETTA Test Method |
| Nilit FRIANYL A63 GV40 Nylon 6.6 for injection molding, 40% glass fiber reinforced Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Linear Mold Shrinkage | 0.0090 - 0.011 cm/cm | 0.0090 - 0.011 in/in | Across Flow; ISO 2577 |
| Polykemi AB POLYfill PPH GF5020 HC Polypropylene Homopolymer, Glass Fiber Reinforced Information provided by Polykemi AB |
|||
| Linear Mold Shrinkage | 0.0090 - 0.011 cm/cm | 0.0090 - 0.011 in/in | Across Flow; ISO 2577 |
| Polykemi AB SCANMID 6 B32^ E Q30 Nylon 6, Glass Fiber Reinforced, Modified Information provided by Polykemi AB |
|||
| Linear Mold Shrinkage | 0.0090 - 0.011 cm/cm | 0.0090 - 0.011 in/in | after bake; ISO 294 |
| Solvay Engineered Polymers DEXFLEX® 990 TPO
(discontinued **) Description: DEXFLEX® 990 is a thermoplastic olefinic elastomer (TPO) designed for automotive exterior applications that require a combination of stiffness, low-temperature impact, and excellent pr.. |
|||
| Linear Mold Shrinkage | 0.0070 - 0.011 cm/cm | 0.0070 - 0.011 in/in | |
| Lehmann & Voss LUVOCOM® 1301-7836 PPS, linear, with glass fiber, lubricant modified Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.Low warpage, isotropic shrinkage characteristics.Chemical and hydrolysis resistance parts.High dim.. |
|||
| Linear Mold Shrinkage | 0.0050 - 0.011 cm/cm @Temperature 23.0 °C |
0.0050 - 0.011 in/in @Temperature 73.4 °F |
ASTM D955 |
| Kingfa PA66-RG201 Flame Retardant, 20% Glass Fiber Reinforced PA66 Features:Flame retardantHigh strengthHigh temperature propertiesGood electric propertiesNo bloomingApplications:Injection moldingConnectorsRelayBobbins, plugsE & E partsInformation Provided by Kingf.. |
|||
| Linear Mold Shrinkage | 0.0050 - 0.011 cm/cm @Temperature 23.0 °C |
0.0050 - 0.011 in/in @Temperature 73.4 °F |
ASTM D955 |
| Kingfa PBT-G15 15% Glass Fiber Reinforced PBT Features:Good size stabilityHigh mechanical propertiesHigh heat resistanceExcellent balance propertiesApplications:Injection moldingApplication partsAuto handleDoor latchE & E partsInformation Provi.. |
|||
| Linear Mold Shrinkage | 0.0050 - 0.011 cm/cm @Temperature 23.0 °C |
0.0050 - 0.011 in/in @Temperature 73.4 °F |
ASTM D955 |
| Kingfa PBT-RG151 Flame Retardant, 15% Glass Fiber Reinforced PBT Features:Flame retardantHigh strengthHigh temperature propertiesGood electric propertiesExcellent size stabilityNo bloomingApplications:Injection moldingConnectorsRelayBobbinsPlugsE & E partsInforma.. |
|||
| Linear Mold Shrinkage | 0.0080 - 0.011 cm/cm | 0.0080 - 0.011 in/in | ASTM D955 |
| Star Plastics PC/PBT7820 Molding Grade PC/PBT Information provided by Star Plastics, Inc. |
|||
| Linear Mold Shrinkage | 0.0090 - 0.011 cm/cm | 0.0090 - 0.011 in/in | |
| A. Schulman POLYTROPE™ TPP 504 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 504 is an injection molding grade olefinic thermoplastic elastomer. This product is recommended for parts requiring flexibility and high impact strength at sub-ambient temp.. |
|||
| Linear Mold Shrinkage | 0.0080 - 0.011 cm/cm | 0.0080 - 0.011 in/in | ASTM D955 |
| A. Schulman POLYFORT™ FPP 1602 Glass Reinforced, Chemically Coupled Homopolymer DescriptionPolyfort® FPP 1602 is a 10% glass reinforced chemically coupled homopolymer.Information provided by A. Schulman. |
|||
| Linear Mold Shrinkage | 0.0090 - 0.011 cm/cm | 0.0090 - 0.011 in/in | |
| A. Schulman POLYTROPE™ TPP 293 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP293 is an injection molding grade olefinic thermoplastic elastomer. This product is recommended for parts requiring excellent low temperature impact properties with good dim.. |
|||
| Linear Mold Shrinkage | 0.0090 - 0.011 cm/cm | 0.0090 - 0.011 in/in | |
| A. Schulman POLYTROPE™ TPP 512 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 512 is an injection molding grade olefinic thermoplastic elastomer. This product has excellent low temperature impact properties and flow characteristics suitable for moldi.. |
|||
| Linear Mold Shrinkage | 0.0090 - 0.011 cm/cm | 0.0090 - 0.011 in/in | |
| A. Schulman POLYTROPE™ TPP 512 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 512 is an injection molding grade olefinic thermoplastic elastomer. This product has excellent low temperature impact properties and flow characteristics suitable for moldi.. |
|||
| Linear Mold Shrinkage | 0.0090 - 0.011 cm/cm | 0.0090 - 0.011 in/in | |
| A. Schulman POLYTROPE™ TPP 503 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 503 is an injection molding grade olefinic thermoplastic elastomer. This product is recommended for parts requiring flexibility and high impact strength at sub-ambient temp.. |
|||
| Linear Mold Shrinkage | 0.0070 - 0.011 cm/cm @Thickness 3.17 mm |
0.0070 - 0.011 in/in @Thickness 0.125 in |
ASTM D955 |
| RTP Company RTP 227 Nylon 6/6 (PA), Mineral |
|||
| Linear Mold Shrinkage | 0.0080 - 0.011 cm/cm | 0.0080 - 0.011 in/in | |
| Voloknohim Filament Nylon Linear Density 93.5 tex Application: for production of goods for fishery and for other technical purposes. The produced yarn is bright, UV-stabilized, thermostabilized, UV-thermostabilized, not dyed, dyedInformation provi.. |
|||
| Linear Mold Shrinkage | 0.0090 - 0.011 cm/cm @Thickness 4.00 mm |
0.0090 - 0.011 in/in @Thickness 0.157 in |
|
| CP-Polymer-Technik Wellamid® 6600 MR 409 HWCP 40% Mineral Nylon 66, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
| Linear Mold Shrinkage | 0.0020 - 0.011 cm/cm | 0.0020 - 0.011 in/in | ASTM D955 |
| EPICHEM PA 66 GF 30 Polyamide 66, 30% Glass Characteristics: 30% glass fibre filled |
|||
| Linear Mold Shrinkage | 0.0040 - 0.011 cm/cm | 0.0040 - 0.011 in/in | ASTM D955 |
| Beijing Ranger Chem PBT-201-G20 202 Environmental Protection Flame Retarding FR PBT Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin.. |
|||
| Linear Mold Shrinkage | 0.0090 - 0.011 cm/cm | 0.0090 - 0.011 in/in | With Flow; ISO 2577 |
| Polykemi AB POLYfill PPH TS5040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Linear Mold Shrinkage | 0.0090 - 0.011 cm/cm | 0.0090 - 0.011 in/in | With Flow; ISO 2577 |
| Polykemi AB POLYfill PPHC K1035 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
| Linear Mold Shrinkage | 0.0070 - 0.011 cm/cm @Thickness 3.17 mm |
0.0070 - 0.011 in/in @Thickness 0.125 in |
ASTM D955 |
| RTP Company RTP 127 HB Polypropylene (PP), Talc - UL94 HB Talc reinforced polypropylene offers improved stiffness, hardness and heat distortion temperature vs. the base resin. RTP 127 HB exhibits lower mold shrinkage and better dimensional stability. |
|||
| Linear Mold Shrinkage | 0.0090 - 0.011 cm/cm | 0.0090 - 0.011 in/in | With Flow; ISO 2577 |
| Polykemi AB POLYfill PPH TS2040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Linear Mold Shrinkage | 0.0050 - 0.011 cm/cm @Thickness 3.17 mm |
0.0050 - 0.011 in/in @Thickness 0.125 in |
ASTM D955 |
| RTP Company RTP 1200-80A BLACK Ester-based Thermoplastic Polyurethane Elastomer
(discontinued **) Data for this product has not been recently verified, please contact RTP Company for more information before specifying this grade. |
|||
| Linear Mold Shrinkage | 0.0070 - 0.011 cm/cm @Thickness 3.17 mm |
0.0070 - 0.011 in/in @Thickness 0.125 in |
ASTM D955 |
| RTP Company RTP 200.5 A Nylon 6 (PA), Glass Fiber |
|||