Ineos ABS Lustran® 633 ABS, Injection Molding Grade

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer Ineos ABS
Trade Name Lustran®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos ABS Lustran® 633 ABS, Injection Molding Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lustran® ABS 633 is a general-purpose injection molding grade of ABS (Acrylonitrile Butadiene Styrene). It offers a good balance of physical properties, high gloss, and good moldability. Typical applications include housings, toys, small appliances, and consumer goods.
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
ASTM-D792
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM-D955
Melt Flow 4.5 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 4.5 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ASTM-D1238
14.5 g/10 min

@Load 10.0 kg,
Temperature 230 °C
 14.5 g/10 min

@Load 22.0 lb,
Temperature 446 °F
 ASTM-D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 109
109
ASTM-D785
Tensile Strength, Yield 41.3 MPa
5990 psi
ASTM-D638
Tensile Modulus 2.20 GPa
319 ksi
ASTM-D638
Flexural Yield Strength 65.5 MPa
9500 psi
ASTM-D790
Flexural Modulus 2.20 GPa
319 ksi
ASTM-D790
Izod Impact, Notched 0.640 J/cm

@Thickness 3.20 mm,
Temperature -40.0 °C
 1.20 ft-lb/in

@Thickness 0.126 in,
Temperature -40.0 °F
 ASTM-D256
3.47 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 6.50 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM-D256
Thermal Properties Metric English Comments
CTE, linear 90.0 µm/m-°C
50.0 µin/in-°F
ASTM-D696
Deflection Temperature at 0.46 MPa (66 psi) 96.0 °C

@Thickness 12.7 mm
 205 °F

@Thickness 0.500 in
 Unannealed; ASTM-D648
102 °C

@Thickness 12.7 mm
 216 °F

@Thickness 0.500 in
 Annealed; ASTM-D648
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C

@Thickness 12.7 mm
 185 °F

@Thickness 0.500 in
 Unannealed; ASTM-D648
97.0 °C

@Thickness 12.7 mm
 207 °F

@Thickness 0.500 in
 Annealed; ASTM-D648
Vicat Softening Point 106 °C
223 °F
Rate B; ASTM-D1525
UL RTI, Electrical 60.0 °C

@Thickness 1.50 mm
 140 °F

@Thickness 0.0591 in
 UL746B
UL RTI, Mechanical with Impact 60.0 °C

@Thickness 1.50 mm
 140 °F

@Thickness 0.0591 in
 UL746B
UL RTI, Mechanical without Impact 60.0 °C

@Thickness 1.50 mm
 140 °F

@Thickness 0.0591 in
 UL746B
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
Optical Properties Metric English Comments
Gloss 90 %
90 %
Angle 60°; ASTM-D523
Processing Properties Metric English Comments
Rear Barrel Temperature 235 - 249 °C
455 - 480 °F
Injection Molding
Middle Barrel Temperature 241 - 254 °C
466 - 489 °F
Injection Molding
Front Barrel Temperature 246 - 260 °C
475 - 500 °F
Injection Molding
Nozzle Temperature 246 - 260 °C
475 - 500 °F
Injection Molding
Melt Temperature 246 - 274 °C
475 - 525 °F
Injection Molding
Mold Temperature 43.0 - 66.0 °C
109 - 151 °F
Injection Molding
Drying Temperature 71.0 - 77.0 °C

@Time 14400 sec
 160 - 171 °F

@Time 4.00 hour
82.0 - 88.0 °C

@Time 7200 sec
 180 - 190 °F

@Time 2.00 hour
Moisture Content <= 0.10 %
<= 0.10 %
Dew Point <= -29.0 °C
<= -20.2 °F
inlet air
Injection Pressure 68.9 - 110 MPa
10000 - 16000 psi
Injection Molding
Back Pressure 0.000 - 0.172 MPa
0.000 - 25.0 psi
Injection Molding
Clamp Pressure 30.8 - 61.6 MPa
4470 - 8930 psi
Injection Molding
Cushion <= 0.635 cm
<= 0.250 in
Injection Molding
Descriptive Properties Value Comments
Hold Pressure 50-75% of Injection Pressure, Injection Molding
Injection Speed High
Injection Molding
Screw Compression Ratio 2.5:1
Injection Molding
Screw Length-to-Diameter Ratio >= 20:1
Injection Molding
Screw Speed Moderate, Injection Molding
Shot Weight-to-Machine Capacity Ratio 0.5-0.75
Injection Molding