Eastman Drystar 0601 Copolyester, Injection Molded

Category Polymer , Thermoplastic , Polyester, TP
Manufacturer Eastman Chemical
Trade Name Drystar
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eastman Drystar 0601 Copolyester, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This product-line is designed to meet the needs of converters seeking value-added solutions to their drying requirements of copolyesters. Eastman’s copolyesters are highly valued for their excellent balance of properties such as superior aesthetics, impact strength, and chemical resistance. These properties can be optimally realized when the resins are properly dehydrated in accordance to recommended drying conditions and equipment.Recognizing this value, Eastman conceived DRYSTAR copolyesters to allow converters with limited access to desiccant dryers to achieve these optimizations. In addition, some converters with desiccant dryers may still find DRYSTAR copolyesters value-adding to attain production flexibility and cost saving by removing the drying process prior to injection molding, profile extruding, or extrusion blow molding copolyesters. The initial launch comprises of the commercialization of four grades of DRYSTAR copolyesters and Eastman has on-going program to extend this strategic product-line in the future.*DRYSTAR is only available in the Asia Pacific Region.Applications/UsesInjection molding
Physical Properties Metric English Comments
Specific Gravity 1.27 g/cc
1.27 g/cc
ASTM D792
Density 1.27 g/cc
0.0459 lb/in³
ISO 1183
Water Absorption 0.13 %
0.13 %
24h Immersion; ISO 62
0.13 %
0.13 %
24h Immersion; ASTM D570
Mechanical Properties Metric English Comments
Hardness, Rockwell R 106
106
ASTM D785
109
109
ISO 2039-2
Tensile Strength at Break 28.0 MPa
4060 psi
ISO 527
28.0 MPa
4060 psi
ASTM D638
Tensile Strength, Yield 50.0 MPa
7250 psi
ASTM D638
50.0 MPa
7250 psi
ISO 527
Elongation at Break 100 %
100 %
ISO 527
130 %
130 %
ASTM D638
Tensile Modulus 2.10 GPa
305 ksi
ASTM D638
2.10 GPa
305 ksi
ISO 527
Flexural Yield Strength 68.0 MPa
9860 psi
ISO 178
70.0 MPa
10200 psi
ASTM D790
Flexural Modulus 2.00 GPa
290 ksi
ISO 178
2.10 GPa
305 ksi
ASTM D790
Izod Impact, Notched 0.370 J/cm

@Temperature -40.0 °C
 0.693 ft-lb/in

@Temperature -40.0 °F
 ASTM D256
1.01 J/cm

@Temperature 23.0 °C
 1.89 ft-lb/in

@Temperature 73.4 °F
 ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D4812
NB

@Temperature -40.0 °C
 NB

@Temperature -40.0 °F
 ASTM D4812
Izod Impact, Notched (ISO) 4.20 kJ/m²

@Temperature -40.0 °C
 2.00 ft-lb/in²

@Temperature -40.0 °F
 ISO 180
6.20 kJ/m²

@Temperature 23.0 °C
 2.95 ft-lb/in²

@Temperature 73.4 °F
 ISO 180
Izod Impact, Unnotched (ISO) NB
NB
ISO 180
NB

@Temperature -40.0 °C
 NB

@Temperature -40.0 °F
 ISO 180
Puncture Energy 28.0 J

@Thickness 2.50 mm,
Temperature 23.0 °C
 20.7 ft-lb

@Thickness 0.0984 in,
Temperature 73.4 °F
 max load; ASTM D3763
33.0 J

@Thickness 3.20 mm,
Temperature 23.0 °C
 24.3 ft-lb

@Thickness 0.126 in,
Temperature 73.4 °F
 max load; ASTM D3763
35.0 J

@Thickness 2.50 mm,
Temperature -40.0 °C
 25.8 ft-lb

@Thickness 0.0984 in,
Temperature -40.0 °F
 max load; ISO 6603-2
36.0 J

@Thickness 3.20 mm,
Temperature -40.0 °C
 26.6 ft-lb

@Thickness 0.126 in,
Temperature -40.0 °F
 max load; ISO 6603-2
40.0 J

@Thickness 2.50 mm,
Temperature 23.0 °C
 29.5 ft-lb

@Thickness 0.0984 in,
Temperature 73.4 °F
 max load; ISO 6603-2
41.0 J

@Thickness 2.50 mm,
Temperature -40.0 °C
 30.2 ft-lb

@Thickness 0.0984 in,
Temperature -40.0 °F
 max load; ASTM D3763
44.0 J

@Thickness 3.20 mm,
Temperature 23.0 °C
 32.5 ft-lb

@Thickness 0.126 in,
Temperature 73.4 °F
 max load; ISO 6603-2
50.0 J

@Thickness 3.20 mm,
Temperature -40.0 °C
 36.9 ft-lb

@Thickness 0.126 in,
Temperature -40.0 °F
 max load; ASTM D3763
Thermal Properties Metric English Comments
CTE, linear 51.0 µm/m-°C

@Temperature 20.0 °C
 28.3 µin/in-°F

@Temperature 68.0 °F
 ASTM D696
Specific Heat Capacity 1.30 J/g-°C

@Temperature 60.0 °C
 0.311 BTU/lb-°F

@Temperature 140 °F
 DSC
1.76 J/g-°C

@Temperature 100 °C
 0.421 BTU/lb-°F

@Temperature 212 °F
 DSC
1.88 J/g-°C

@Temperature 150 °C
 0.449 BTU/lb-°F

@Temperature 302 °F
 DSC
2.05 J/g-°C

@Temperature 250 °C
 0.490 BTU/lb-°F

@Temperature 482 °F
 DSC
Thermal Conductivity 0.210 W/m-K
1.46 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 0.46 MPa (66 psi) 70.0 °C
158 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 64.0 °C
147 °F
ASTM D648
Vicat Softening Point 85.0 °C
185 °F
ASTM D1525
Glass Transition Temp, Tg 80.0 °C
176 °F
DSC
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Surface Resistivity per Square 1.00e+16 ohm
1.00e+16 ohm
ASTM D257
Dielectric Constant 2.4

@Frequency 1e+6 Hz
 2.4

@Frequency 1e+6 Hz
 ASTM D150
2.6

@Frequency 1000 Hz
 2.6

@Frequency 1000 Hz
 ASTM D150
Dielectric Strength 16.0 kV/mm
406 kV/in
Short Time, 500V/sec; ASTM D149
Dissipation Factor 0.0050

@Frequency 1000 Hz
 0.0050

@Frequency 1000 Hz
 ASTM D150
0.020

@Frequency 1e+6 Hz
 0.020

@Frequency 1e+6 Hz
 ASTM D150
Arc Resistance 158 sec
158 sec
ASTM D495
Processing Properties Metric English Comments
Melt Temperature 250 - 270 °C
482 - 518 °F
Mold Temperature 15.0 - 40.0 °C
59.0 - 104 °F
Drying Temperature 70.0 °C
158 °F
Dry Time 6 hour
6 hour