Polymer Property : Specific Heat Capacity = 0.311 BTU/lb-°F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Specific Heat Capacity	1.30 J/g-°C @Temperature 60.0 °C	0.311 BTU/lb-°F @Temperature 140 °F	DSC
Eastman Eastar GN002 Copolyester, Natural (discontinued **) Eastar GN002 Copolyester is a glycol modified polyethylene terephthalate (PET) with an added mold release. Eastar GN002 copolyester will not crystallize and thus offers wider processing latitude tha..
Specific Heat Capacity	1.30 J/g-°C @Temperature 60.0 °C	0.311 BTU/lb-°F @Temperature 140 °F	DSC
Eastman Eastar GN005 Copolyester, Natural (discontinued **) Eastar GN005 Copolyester is a glycol modified polyethylene terephthalate (PET) with an added mold release. Eastar GN005 copolyester will not crystallize and thus offers wider processing latitude tha..
Specific Heat Capacity	1.30 J/g-°C @Temperature 50.0 °C	0.311 BTU/lb-°F @Temperature 122 °F	DSC
Solvay Specialty Polymers KetaSpire® KT-820 GF30 Polyetheretherketone (PEEK) (Unverified Data**) KetaSpire KT-820 GF30 is a medium flow, 30% glass fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaSpire..
Specific Heat Capacity	1.30 J/g-Â°C @Temperature 50.0 Â°C	0.311 BTU/lb-Â°F @Temperature 122 Â°F	ASTM C351
Solvay Specialty Polymers AvaSpireÂ® AV-848 GF30 Polyaryletherketone (PAEK), 30% Glass Fiber AvaSpireÂ® AV-848 GF30 is a 30% glass fiber-reinforced, high-temperature, polyaryletherketone (PAEK) that has been specifically formulated to provide several performance advantages over comparable..
Specific Heat Capacity	1.30 J/g-Â°C @Temperature 50.0 Â°C	0.311 BTU/lb-Â°F @Temperature 122 Â°F	ASTM C351
Solvay Specialty Polymers KetaSpireÂ® KT-820 GF30 Polyetheretherketone (PEEK), 30% Glass Fiber KetaSpireÂ® KT-820 GF30 is a medium flow, 30% glass fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaS..
Specific Heat Capacity	1.30 J/g-°C @Temperature 1000 °C	0.311 BTU/lb-°F @Temperature 1830 °F	DINV ENV 821-3
CeramTec Rocar® SiG Silicon Carbide, SiSiC Rocar® is an extremely lightweight silicon carbide ceramic. It permits a reduction in mass forces at high speeds, and is considered for its hardness, excellent resistance to corrosion and sudden ch..
Specific Heat Capacity	1.30 J/g-°C @Temperature 60.0 °C	0.311 BTU/lb-°F @Temperature 140 °F	DSC
Eastman Drystar 0601 Copolyester, Injection Molded This product-line is designed to meet the needs of converters seeking value-added solutions to their drying requirements of copolyesters. Eastman’s copolyesters are highly valued for their excellen..
Specific Heat Capacity	1.30 J/g-°C @Temperature 60.0 °C	0.311 BTU/lb-°F @Temperature 140 °F	DSC
Eastman Eastar MN211 Copolyester, Natural Eastar copolyesters are brilliantly clear polymers that have excellent impact strength, chemical resistance, dimensional stability, and low shrinkage rates. MN211 contains a mold release.Application..
Specific Heat Capacity	1.30 J/g-°C @Temperature 60.0 °C	0.311 BTU/lb-°F @Temperature 140 °F	DSC
Eastman Eastman 1223 Copolyester Applications:Blown filmCredit cardsDebit cardsDeodorant packagingElectronic packagingFabricated boxesFlexible packagingFood packagingFurniture/Furniture trimGaming cardsGift cardsIdentification card..
Specific Heat Capacity	1.30 J/g-°C @Temperature 250 °C	0.311 BTU/lb-°F @Temperature 482 °F
Carlisle 201HD Carbon-Carbon Composite Carbon-Carbon Composite manufactured as sheets from 4mm to 125mm thick this material is essentially a fracture tough, fiber reinforced graphite often referred to as a “CFC”. Good for use in air t..
Specific Heat Capacity	1.30 J/g-°C @Temperature 250 °C	0.311 BTU/lb-°F @Temperature 482 °F
Carlisle 201HL Carbon-Carbon Composite Carbon-Carbon Composite manufactured as sheets from 4mm to 125mm thick this material is essentially a fracture tough, fiber reinforced graphite often referred to as a “CFC”. Good for use in air t..
Specific Heat Capacity	1.30 J/g-°C @Temperature 250 °C	0.311 BTU/lb-°F @Temperature 482 °F
Carlisle 201LD Carbon-Carbon Composite Carbon-Carbon Composite manufactured as sheets from 4mm to 125mm thick this material is essentially a fracture tough, fiber reinforced graphite often referred to as a “CFC”. Good for use in air t..