Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
Polymer Resources PC-IM1-UV Polycarbonate, Impact Modified, Low Flow, UV-stabilized Polycarbonate, Impact Modified, Low Flow, UV-stabilizedProcess: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Inform.. |
|||
Flexural Modulus | 2.00 GPa | 290 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycoloy® CP8320 PC+ABS (Europe-Africa-Middle East) Cycoloy Medium Heat Plating Grade for Automotive |
|||
Flexural Modulus | 2.00 GPa @Temperature 23.0 °C |
290 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB POLYlux 3809SLB PC/PBT-Blend, Paintable Information provided by Polykemi AB |
|||
Flexural Modulus | 2.00 - 8.00 GPa | 290 - 1160 ksi | Average value: 5.22 GPa Grade Count:112 |
Overview of materials for Polycarbonate, 20% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 20% Glass Filled". Specific grades with glass content between 15% and 24% are included. E.. |
|||
Flexural Modulus | 2.00 GPa | 290 ksi | 2nd Grade |
Kazanorgsintez PC-005 Polycarbonate Production Method: Obtained by means of polycondensation method. Application: Intended for product manufacture by method of extrusion and die-casting.Information Provided by Kazanorgsintez |
|||
Flexural Modulus | 2.00 GPa | 290 ksi | |
Lehmann & Voss LUVOCOM® 1850-7795 PBT, with PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri.. |
|||
Flexural Modulus | 2.00 GPa | 290 ksi | |
Lehmann & Voss LUVOCOM® 50-8479/BL-1 Polycarbonate, unreinforced Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Isotropic shrinkage characteristics.Reduced moment of inertia .. |
|||
Flexural Modulus | 2.00 GPa | 290 ksi | |
Lehmann & Voss LUVOCOM® 80-7655/RD Polyacetal-copolymer, with aramid reinforcement and PTFE, toughness-modified, high viscosity Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.High dimensionally stable prec.. |
|||
Flexural Modulus | 2.00 GPa | 290 ksi | 2mm/min; ASTM D790 |
Kingfa HF-618 Flame Retardant ABS Features:UL 94 V-0 @ 1.6-3.0mmHigh toughnessEasy flowApplications:Injection moldingShell of applianceCD-ROMPower switchInformation Provided by Kingfa Sci. & Tech. Co., Ltd. |
|||
Flexural Modulus | 2.00 GPa | 290 ksi | 1.3 mm/min; ASTM D790 |
Lavergne VYSTYRENE PS 3901 High Impact Polystyrene Vystyrene PS 3901 is a black impact modified polystyrene compound with balanced impact/stiffness properties designed for injection molding applicationsFeatures: -High resilience -Excellent process.. |
|||
Flexural Modulus | 2.00 GPa | 290 ksi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP KP002 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KP002 is a compound based on Acetal Copolymer resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated. |
|||
Flexural Modulus | 2.00 GPa | 290 ksi | ISO 178 |
SABIC Innovative Plastics LNP LUBRILOY R2000 PA 66 (Asia Pacific) LNP* Lubriloy* R2000 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated. |
|||
Flexural Modulus | 2.00 GPa | 290 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics XYLEX X8419 PC+POLYESTER (Europe-Africa-Middle East) Low-medium flow, suitable for blow molding, injection molding, extrusion. |
|||
Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
Techmer ES Plaslube® PC-50/TF/13/SI/2 NAT Polycarbonate |
|||
Flexural Modulus | 2.00 GPa | 290 ksi | ISO 178 |
Unitika A3030N-2 PA6, 30% Mineral Reinforced, Conditioned Information provided by Unitika Ltd. |
|||
Flexural Modulus | 2.00 GPa | 290 ksi | ISO 178 |
Polyram RamLloy PJ702 ASA & ABS Alloy A general purpose injection molding ASA & ABS alloy. It has good mechanical properties similar to ABS with much better weather resistance.Information provided by Polyram. |
|||
Flexural Modulus | 2.00 GPa | 290 ksi | 1.3mm per min, 1% secant; ASTM D790 |
Formosa Plastics Formolene® 5144L Homopolymer Polypropylene Homopolymer for Injection Molded Applications requiring Heat Resistance Formolene® 5144L is a highly isotactic, nucleated polypropylene homopolymer designed for consumer products and appliance appl.. |
|||
Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D 790 |
RTP Company RTP 100 GB 30 Polypropylene (PP), Glass Bead |
|||
Flexural Modulus | 2.00 GPa | 290 ksi | ASTM-D790 |
Polyram RamOfin PPH353M8 Polypropylene, 40% Mineral Filled 40% mineral filled polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Modulus | 2.00 GPa | 290 ksi | ISO 178 |
Eastman Drystar 0113 Copolyester This product-line is designed to meet the needs of converters seeking value-added solutions to their drying requirements of copolyesters. Eastman’s copolyesters are highly valued for their excellen.. |
|||
Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
Eastman DuraStar DS1110UVI Polymer, Natural Durastar DS1110UVI polymer, contains an ultraviolet light stabilization package. It is recommended for indoor applications requiring enhanced color stability upon extended exposure to fluorescent li.. |
|||
Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
Eastman DuraStar MN610 Polymer, Natural Durastar MN610 polymer has excellent appearance and is nearly water-clear. Its most outstanding features are toughness, chemical resistance, and excellent processing characteristics. MN610 has very .. |
|||
Flexural Modulus | 2.00 GPa | 290 ksi | 2mm/min; ISO 178 |
Denka CL-430 Transparent Resin Polymer (MABS) ABS "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
Flexural Modulus | 2.00 GPa | 290 ksi | SAE J949 |
Azdel SuperLite® SL550900-100 PP Resin Matrix / 55% Glass Fiber (2 mm Molded Thickness) AZDEL SuperLite® SL550900-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Flexural Modulus | 2.00 GPa | 290 ksi | cond.; ISO 178 |
Azoty Tarnow™ Tarnamid® T-27 GF15 Polyamide 6 - Glass Fiber Reinforced 15% Glass fiber reinforced, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main properties:High.. |
|||
Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
Ashley Polymers Ashlene® 279 PPO Alloy A general purpose, paintable injection molding grade with high chemical resistance and mechanical performance. Good heat resistance with dimensional stability in dark gray or black only.Data provid.. |
|||
Flexural Modulus | 2.00 GPa | 290 ksi | 50%RH; ISO 178 |
DuPont Performance Polymers Minlon® 11C40 NC010 Nylon 66
(Unverified Data**) 40% Mineral Reinforced Polyamide 66 Minlon 11C40 NC010 is a 40% mineral reinforced heat stabilized polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers |
|||
Flexural Modulus | 2.00 - 24.1 GPa | 290 - 3500 ksi | Average value: 7.17 GPa Grade Count:230 |
Overview of materials for Polyethersulfone (PES) This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
Flexural Modulus | 2.00 GPa | 290 ksi | STN EN ISO 178 |
Plastcom SLOVALEN PH 51 T 10 Polypropylene Homopolymer, 10% Mineral Filled FeaturesModified homopolymer PP for injection moulding with the content of 10% mineral filler. Increased rigidity, strength and thermal use up to 120°C. Decreased shrinkage. General application .. |
|||
Flexural Modulus | 2.00 GPa | 290 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycoloy® CP8320 PC+ABS (Asia Pacific) Cycoloy Medium Heat Plating Grade for Automotive |