Polymer Property : Tensile Strength at Break = 28.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	28.0 MPa	4060 psi	STN EN ISO 527-2
Plastcom SLOVALEN PC 78 FRD 1 Polypropylene Copolymer, Halogen Flame Retardant, UV Stabilized FeaturesModified copolymer PP with the possibility of changing the MFI within the interval 5 - 20 g/10min. Stabilized against the UV-radiation by the UV stabilizer on the HALS basis. Retarded with..
Tensile Strength at Break	28.0 MPa	4060 psi
Plastcom SLOVAMID 66 HI/1 PA66, improved strength FeaturesModified with thermoplastic reactive caoutchouc, determined for mouldings with high toughness also at minus temperatures. Eligible application for ski-shoes, helmets for sport and other safe..
Tensile Strength at Break	<= 28.0 MPa	<= 4060 psi	ISO/R527
Polykemi AB POLYfill PPC TS16020 LE Polypropylene Copolymer, Mineral Reinforced, Low Emission Information provided by Polykemi AB
Tensile Strength at Break	<= 28.0 MPa	<= 4060 psi	ISO/R527
Polykemi AB POLYfill PPH TS15040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB
Tensile Strength at Break	<= 28.0 MPa	<= 4060 psi	ISO/R527
Polykemi AB POLYfill PPH TS2020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB
Tensile Strength at Break	28.0 MPa	4060 psi	ISO 527
Eastman Eastar GN005 Copolyester, Natural (discontinued **) Eastar GN005 Copolyester is a glycol modified polyethylene terephthalate (PET) with an added mold release. Eastar GN005 copolyester will not crystallize and thus offers wider processing latitude tha..
Tensile Strength at Break	28.0 MPa	4060 psi	ASTM D638
Braskem BT 003 HDPE Blow Molding Polyethylene (discontinued **) Applications: Bottles for food products, lubricating and cooking oil; toys; bottler for surface-active agents; sheets. Information provided by Braskem
Tensile Strength at Break	28.0 MPa	4060 psi	ASTM D4895
3M Dyneon™ TF 2071 PTFE (discontinued **) Processable by standard paste extrusion methodTF 2071 and TF 2072 have a wide processing range because of high maximum allowable reduction ratioTF 2071 is recommended for high quality tubing and wir..
Tensile Strength at Break	28.0 MPa	4060 psi	ISO 37
Huntsman AVALONÂ® 85 AE Thermoplastic Polyurethane Introduction: AVALON 85 AE is a general purpose polyester based thermoplastic polyurethane for injection molding. AVALON 85 AE is part of the AVALON Perform Range and offers a premium soiling materi..
Tensile Strength at Break	28.0 MPa	4060 psi	50 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP SP003 PA12 (Europe-Africa-Middle East) LNP* LUBRICOMP* SP003 is a compound based on PA 12 resin containing PTFE/Silicone. Added features include: Internally Lubricated.
Tensile Strength at Break	28.0 MPa	4060 psi	ISO 527
SABIC Innovative Plastics LNP STAT-LOY A30009 ABS (Asia Pacific) LNP* Stat-loy* A30009 is a compound based on Acrylonitrile Butadiene Styrene resin containing Flame Retardant. Added features of this material include: Antistat, Flame Retardant.
Tensile Strength at Break	28.0 MPa	4060 psi	100mm/min, 4mm injection molded, unannealed; ISO 527-2
Styron EMERGEâ„¢ 5100 Acrylonitrile Butadiene Styrene (ABS) EMERGEâ„¢ ABS 5100 is a pre-colored, white, ABS resin, having high opacity and excellent toughness intended for manufacture of laser-marketable injection-molded smart cards.Information provided b..
Tensile Strength at Break	28.0 MPa	4060 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP WH0450E PBT LNP* Thermocomp* WH0450E is a compound based on Polybutylene Terephalate resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.
Tensile Strength at Break	28.0 MPa	4060 psi	50 mm/min; ISO 527
SABIC Innovative Plastics NORYL PPX PPX7200 PPE+PP+PS (Asia Pacific) PP+PPE+PS. Improved chemical resistance and surface aesthetics in injection molded applications. NSF61-capable. UL-94 HB listed.
Tensile Strength at Break	28.0 MPa	4060 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP MB006HS PP LNP* THERMOCOMP* MB006HS is a compound based on Polypropylene resin containing 30% Glass Bead. Added features of this material include: Heat Stabilized, Healthcare.
Tensile Strength at Break	28.0 MPa	4060 psi	50mm/min; ISO 527
Borealis Borstar® LE8706 Natural Bimodal LLDPE Jacketing Compound for Energy and Communication Cables Borstar® LE8706 is a natural colorable linear low density (LLD) jacketing compound, which is produced with the Borealis proprietary Borstar® bimodal process technology. Borstar technology allows ..
Tensile Strength at Break	28.0 MPa	4060 psi	ISO 527-2
Tisan TISOPLEN® 40% Calcite Filled Heat Stabilized Copolymer Polypropylene TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois..
Tensile Strength at Break	28.0 MPa	4060 psi	ISO 527
Eastman Drystar 0113 Copolyester This product-line is designed to meet the needs of converters seeking value-added solutions to their drying requirements of copolyesters. Eastman’s copolyesters are highly valued for their excellen..
Tensile Strength at Break	28.0 MPa	4060 psi	ASTM D 638
Cossa Polimeri ESTAPROP H0260 MC/EC Conductive Polypropylene, Mineral Filled Information provided by Cossa Polimeri S.r.l.
Tensile Strength at Break	28.0 MPa @Temperature 23.0 °C	4060 psi @Temperature 73.4 °F	DAM; ISO 527
DuPont Performance Polymers Zytel® FN727 BK230A Nylon 6 Zytel® FN727 BK230A is a black, impact modified, plasticizer free, very flexible polyamide 6 alloy resin having good low temperature toughness, good heat aging and good chemical resistance. Uses in..
Tensile Strength at Break	28.0 MPa	4060 psi	ISO 527
Eurostar Starpylen HU 30E4 ECR PP, Mineral Filled, Injection Molding Starpylen HU 30E4 ECR is a reinforced Polypropylene with a low carbon footprint renewable mineral filler, Injection Molding Resin (also known as HUS30E4ECR)Information provided by Eurostar.
Tensile Strength at Break	28.0 MPa	4060 psi	50 mm/min; ISO 527
Fainplast Compounds Propylplus 707E Polypropylene Cable Compound Polypropylene, halogen-free cable compound with superior thermo-mechanical properties, outstanding heat resistance, and high electrical propertiesExpandable PolypropyleneInformation provided by Fain..
Tensile Strength at Break	28.0 MPa	4060 psi	ISO 527-1/-2
DuPont Performance Polymers Hytrel® HTR8341C BK320 Polyester Elastomer TPC-ET (Unverified Data**) 40 Shore D Lubricated High Viscosity Polyester Elastomer with Superior Fatigue Resistance Developed for Blow Molding Information provided by DuPont Performance Polymers
Tensile Strength at Break	28.0 MPa	4060 psi	ASTM D3759
3M 2542/Silver Damping Foils Thinner, general purpose vibration dampingInformation provided by 3M
Tensile Strength at Break	28.0 MPa	4060 psi	ASTM D638
Aclo Accutech Polypropylene Homopolymer HP0339M40L Mica Reinforced
Tensile Strength at Break	28.0 MPa	4060 psi	ASTM D638
Aclo Accutech Polypropylene Homopolymer HP0339W10L Wollastonite Reinforced
Tensile Strength at Break	<= 28.0 MPa	<= 4060 psi	ISO/R527
Polykemi AB POLYfill PPC 15000 Polypropylene Copolymer Information provided by Polykemi AB
Tensile Strength at Break	<= 28.0 MPa	<= 4060 psi	ISO/R527
Polykemi AB POLYfill PPH TS5040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB
Tensile Strength at Break	28.0 MPa	4060 psi	ASTM D 638
SABIC Innovative Plastics LNP Lubricomp CI001 PS (Asia Pacific) LNP* Lubricomp* CI001 is a compound based on Polystyrene resin containing Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Asia Pa..
Tensile Strength at Break	28.0 MPa	4060 psi	ASTM D638
Lushan M-12A Adhesive Resin for Multi-layer Oxygen Barrier Pipe Adhesive resin Lushan series for multi-layer oxygen barrier pipe is a modified polyolefin with functional groups. It’s designed to bond to a variety of barrier materials, such as nylon and ethylene..