DuPont Performance Polymers Zytel® ST801 BK010A Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® ST801 BK010A Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Super Toughened Polyamide 66 Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 0.920 g/cc
0.0332 lb/in³
1.08 g/cc
0.0390 lb/in³
DAM; ISO 1183
Water Absorption 6.7 %

@Thickness 2.00 mm
 6.7 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 2.20 %

@Thickness 2.00 mm
 2.20 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Viscosity 78340 cP

@Shear Rate 5000 1/s,
Temperature 300 °C
 78340 cP

@Shear Rate 5000 1/s,
Temperature 572 °F
 ISO 11403-1 -2
94140 cP

@Shear Rate 5000 1/s,
Temperature 290 °C
 94140 cP

@Shear Rate 5000 1/s,
Temperature 554 °F
 ISO 11403-1 -2
113400 cP

@Shear Rate 5000 1/s,
Temperature 280 °C
 113400 cP

@Shear Rate 5000 1/s,
Temperature 536 °F
 ISO 11403-1 -2
224640 cP

@Shear Rate 500 1/s,
Temperature 300 °C
 224640 cP

@Shear Rate 500 1/s,
Temperature 572 °F
 ISO 11403-1 -2
276400 cP

@Shear Rate 500 1/s,
Temperature 290 °C
 276400 cP

@Shear Rate 500 1/s,
Temperature 554 °F
 ISO 11403-1 -2
344660 cP

@Shear Rate 500 1/s,
Temperature 280 °C
 344660 cP

@Shear Rate 500 1/s,
Temperature 536 °F
 ISO 11403-1 -2
Viscosity Test 150 cm³/g
150 cm³/g
DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.018 cm/cm
0.018 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.014 cm/cm
0.014 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Stress 2.00 MPa

@Strain 0.150 %,
Time 3600 sec
 290 psi

@Strain 0.150 %,
Time 1.00 hour
 50%RH; isochronous; ISO 11403-1 -2
2.00 MPa

@Strain 0.200 %,
Time 36000 sec
 290 psi

@Strain 0.200 %,
Time 10.0 hour
 50%RH; isochronous; ISO 11403-1 -2
2.00 MPa

@Strain 0.235 %,
Time 360000 sec
 290 psi

@Strain 0.235 %,
Time 100 hour
 50%RH; isochronous; ISO 11403-1 -2
2.00 MPa

@Strain 0.280 %,
Time 3.60e+6 sec
 290 psi

@Strain 0.280 %,
Time 1000 hour
 50%RH; isochronous; ISO 11403-1 -2
2.00 MPa

@Strain 0.342 %,
Time 3.60e+7 sec
 290 psi

@Strain 0.342 %,
Time 10000 hour
 50%RH; isochronous; ISO 11403-1 -2
8.00 MPa

@Strain 1.22 %,
Time 360000 sec
 1160 psi

@Strain 1.22 %,
Time 100 hour
 50%RH; isochronous; ISO 11403-1 -2
8.00 MPa

@Strain 1.00 %,
Time 36000 sec
 1160 psi

@Strain 1.00 %,
Time 10.0 hour
 50%RH; isochronous; ISO 11403-1 -2
10.0 MPa

@Time 3600 sec,
Strain 1.142 %
 1450 psi

@Time 1.00 hour,
Strain 1.142 %
 50%RH; isochronous; ISO 11403-1 -2
10.0 MPa

@Strain 2.23 %,
Time 3.60e+6 sec
 1450 psi

@Strain 2.23 %,
Time 1000 hour
 50%RH; isochronous; ISO 11403-1 -2
10.0 MPa

@Strain 2.94 %,
Time 3.60e+7 sec
 1450 psi

@Strain 2.94 %,
Time 10000 hour
 50%RH; isochronous; ISO 11403-1 -2
Tensile Strength, Yield 43.0 MPa
6240 psi
50%RH; ISO 527-1/-2
50.0 MPa
7250 psi
DAM; ISO 527-1/-2
Elongation at Break 32 %
32 %
DAM; Nominal; ISO 527-1/-2
>= 50 %
>= 50 %
50%RH; Nominal; ISO 527-1/-2
Elongation at Yield 5.7 %
5.7 %
DAM; ISO 527-1/-2
5.7 %
5.7 %
DAM; ISO 527-3
37 %
37 %
50%RH; ISO 527-1/-2
Tensile Modulus 0.900 GPa
131 ksi
50%RH; ISO 527-1/-2
2.00 GPa
290 ksi
DAM; ISO 527-1/-2
0.221 GPa

@Temperature 120 °C
 32.1 ksi

@Temperature 248 °F
 50%RH; ISO 11403-1 -2
0.2409 GPa

@Temperature 170 °C
 34.94 ksi

@Temperature 338 °F
 DAM; Dynamic; ISO 11403-1 -2
0.267 GPa

@Temperature 120 °C
 38.7 ksi

@Temperature 248 °F
 DAM; ISO 11403-1 -2
0.360 GPa

@Temperature 110 °C
 52.2 ksi

@Temperature 230 °F
 DAM; Dynamic; ISO 11403-1 -2
0.568 GPa

@Temperature 40.0 °C
 82.4 ksi

@Temperature 104 °F
 50%RH; ISO 11403-1 -2
1.647 GPa

@Temperature 40.0 °C
 238.9 ksi

@Temperature 104 °F
 DAM; ISO 11403-1 -2
1.98 GPa

@Temperature 30.0 °C
 287 ksi

@Temperature 86.0 °F
 DAM; Dynamic; ISO 11403-1 -2
2.13 GPa

@Temperature -20.0 °C
 309 ksi

@Temperature -4.00 °F
 DAM; Dynamic; ISO 11403-1 -2
2.347 GPa

@Temperature -40.0 °C
 340.4 ksi

@Temperature -40.0 °F
 DAM; ISO 11403-1 -2
2.716 GPa

@Temperature -40.0 °C
 393.9 ksi

@Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
3.22 GPa

@Temperature -70.0 °C
 468 ksi

@Temperature -94.0 °F
 DAM; Dynamic; ISO 11403-1 -2
3.73 GPa

@Temperature -100 °C
 541 ksi

@Temperature -148 °F
 DAM; Dynamic; ISO 11403-1 -2
Shear Modulus 0.0781 GPa

@Temperature 160 °C
 11.3 ksi

@Temperature 320 °F
 DAM; Dynamic; ISO 11403-1 -2
0.0992 GPa

@Temperature 120 °C
 14.4 ksi

@Temperature 248 °F
 DAM; Dynamic; ISO 11403-1 -2
0.220 GPa

@Temperature 68.0 °C
 31.9 ksi

@Temperature 154 °F
 DAM; Dynamic; ISO 11403-1 -2
0.6535 GPa

@Temperature 20.0 °C
 94.78 ksi

@Temperature 68.0 °F
 DAM; Dynamic; ISO 11403-1 -2
0.719 GPa

@Temperature -20.0 °C
 104 ksi

@Temperature -4.00 °F
 DAM; Dynamic; ISO 11403-1 -2
0.935 GPa

@Temperature -50.0 °C
 136 ksi

@Temperature -58.0 °F
 DAM; Dynamic; ISO 11403-1 -2
Charpy Impact Unnotched NB
NB
DAM; ISO 179/1eU
NB
NB
50%RH; ISO 179/1eU
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 DAM; ISO 179/1eU
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 50%RH; ISO 179/1eU
Charpy Impact, Notched 8.00 J/cm²
38.1 ft-lb/in²
DAM; ISO 179/1eA
11.5 J/cm²
54.7 ft-lb/in²
50%RH; ISO 179/1eA
1.70 J/cm²

@Temperature -30.0 °C
 8.09 ft-lb/in²

@Temperature -22.0 °F
 50%RH; ISO 179/1eA
1.80 J/cm²

@Temperature -30.0 °C
 8.57 ft-lb/in²

@Temperature -22.0 °F
 DAM; ISO 179/1eA
Tensile Creep Modulus, 1 hour 588 MPa

@Pressure 7.00 MPa,
Temperature 60.0 °C
 85300 psi

@Pressure 1020 psi,
Temperature 140 °F
 50%RH; ISO 11403-1 -2
621 MPa

@Pressure 6.00 MPa,
Temperature 60.0 °C
 90100 psi

@Pressure 870 psi,
Temperature 140 °F
 50%RH; ISO 11403-1 -2
667 MPa

@Pressure 5.00 MPa,
Temperature 60.0 °C
 96700 psi

@Pressure 725 psi,
Temperature 140 °F
 50%RH; ISO 11403-1 -2
727 MPa

@Pressure 4.00 MPa,
Temperature 60.0 °C
 105000 psi

@Pressure 580 psi,
Temperature 140 °F
 50%RH; ISO 11403-1 -2
811 MPa

@Pressure 3.00 MPa,
Temperature 60.0 °C
 118000 psi

@Pressure 435 psi,
Temperature 140 °F
 50%RH; ISO 11403-1 -2
876 MPa

@Pressure 10.0 MPa,
Temperature 23.0 °C
 127000 psi

@Pressure 1450 psi,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
936 MPa

@Pressure 2.00 MPa,
Temperature 60.0 °C
 136000 psi

@Pressure 290 psi,
Temperature 140 °F
 50%RH; ISO 11403-1 -2
1020 MPa

@Pressure 8.00 MPa,
Temperature 23.0 °C
 147000 psi

@Pressure 1160 psi,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
1110 MPa

@Pressure 1.00 MPa,
Temperature 60.0 °C
 161000 psi

@Pressure 145 psi,
Temperature 140 °F
 50%RH; ISO 11403-1 -2
1120 MPa

@Pressure 6.00 MPa,
Temperature 23.0 °C
 163000 psi

@Pressure 870 psi,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2