Polymer Property : Tensile Modulus = 1.98 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Modulus 1.98 GPa
287 ksi
Type I, 5.1 mm/min; ASTM D638
PolyOne Geon™ HTX Ultra LA426 Black 2880 Polyvinyl Chloride Alloy (PVC Alloy)
Recommend drying material for a minimum of 2 hours at 160 degrees Farenheit. Physical properties measured on LA426 Black 2880.Information provided by PolyOne
Tensile Modulus 1.98 GPa
287 ksi
ASTM D638
Metton LMR M1539 Liquid Molding Resin
Metton LMR is a tough and durable engineering plastic material used to produce large or thick molded parts for many diversified applications. The Metton LMR reaction injection molding process can ..
Tensile Modulus 1.98 GPa
287 ksi
ASTM D638
Metton LMR M2100VO Liquid Molding Resin
Metton LMR is a tough and durable engineering plastic material used to produce large or thick molded parts for many diversified applications. The Metton LMR reaction injection molding process can ..
Tensile Modulus 1.98 GPa
287 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP DL003EXJ PC
LNP* Lubricomp* DL003EXJ is a compound based on Polycarbonate containing 15% PTFE. Characteristics of this grade are Easy Molding, Low Extractable, Internally Lubricated, Healthcare.
Tensile Modulus 1.98 GPa
287 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP ML003S PP
LNP* LUBRICOMP* ML003S is a compound based on Polypropylene resin containing 15% PTFE. Added features include: Heat Stabilized, Wear Resistant.
Tensile Modulus 1.98 GPa
287 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRILOY D2000AXH PC
LNP LUBRILOY* D2000AXH is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Wear Resistant, Healthcare.
Tensile Modulus 1.98 GPa
287 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON MD000AP PP
LNP* STAT-KON* MD000AP is a compound based on Polypropylene containing Carbon Powder. Added features of this grade include: Electrically Conductive, Exceptional Processing.
Tensile Modulus 1.98 GPa
287 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics Xenoy® 1105 PBT+PC (Asia Pacific)
PBT/PC blend, injection molding grade, non-reinforced, impact modified, excellent toughness at low temperatures, very good paintability
Tensile Modulus 1.98 GPa
287 ksi
50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOTUF VX99809 Super Tough Nylon
Super Tough Nylon, Proprietary Filler(s),
Tensile Modulus 1.98 GPa
287 ksi
Storage
Epoxy Technology EPO-TEK® CF6-2 High Temperature Epoxy
Product Description: EPO-TEK® CF6-2 is a two component, high temperature and high Tg epoxy designed for fiber optic packaging. Advantages & Application Notes: The low viscosity nature allows for wi..
Tensile Modulus 1.98 GPa

@Temperature 30.0 °C
287 ksi

@Temperature 86.0 °F
DAM; Dynamic; ISO 11403-1 -2
DuPont Performance Polymers Zytel® ST801 BK010A Nylon 66  (Unverified Data**)
Super Toughened Polyamide 66 Information provided by DuPont Performance Polymers