DuPont Performance Polymers Delrin® FG900P NC010 Acetal Homopolymer (Unverified Data**)
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Delrin® FG900P NC010 Acetal Homopolymer
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Delrin® FG900P is a low viscosity acetal homopolymer, with improved thermal stability. It has been developed for consideration into applications such as parts for the food industry.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Water Absorption | 0.26 % @Temperature 23.0 °C |
0.26 % @Temperature 73.4 °F |
Equilibrium 50%RH; ISO 62, Similar to |
| 0.56 % @Temperature 23.0 °C |
0.56 % @Temperature 73.4 °F |
Immersion 24h; ISO 62, Similar to | |
| 1.4 % @Temperature 23.0 °C |
1.4 % @Temperature 73.4 °F |
Saturation, immersed; ISO 62, Similar to | |
| Linear Mold Shrinkage, Flow | 0.019 cm/cm @Thickness 2.00 mm |
0.019 in/in @Thickness 0.0787 in |
ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.019 cm/cm @Thickness 2.00 mm |
0.019 in/in @Thickness 0.0787 in |
ISO 294-4 |
| Melt Flow | 25 g/10 min @Load 2.16 kg, Temperature 190 °C |
25 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Melt Index of Compound | 21 g/10 min @Load 2.16 kg, Temperature 190 °C |
21 g/10 min @Load 4.76 lb, Temperature 374 °F |
cm3/10 min; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 71.0 MPa @Temperature 23.0 °C |
10300 psi @Temperature 73.4 °F |
ISO 527 |
| Elongation at Break | 23 % @Temperature 23.0 °C |
23 % @Temperature 73.4 °F |
nominal; ISO 527 |
| Elongation at Yield | 12 % @Temperature 23.0 °C |
12 % @Temperature 73.4 °F |
ISO 527 |
| Tensile Modulus | 3.30 GPa @Temperature 23.0 °C |
479 ksi @Temperature 73.4 °F |
ISO 527 |
| Flexural Modulus | 3.00 GPa @Temperature 23.0 °C |
435 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact Unnotched | 20.0 J/cm² @Temperature -30.0 °C |
95.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 20.0 J/cm² @Temperature 23.0 °C |
95.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.800 J/cm² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| Tensile Creep Modulus, 1 hour | 2800 MPa @Temperature 23.0 °C |
406000 psi @Temperature 73.4 °F |
ISO 899 |
| Tensile Creep Modulus, 1000 hours | 1500 MPa @Temperature 23.0 °C |
218000 psi @Temperature 73.4 °F |
ISO 899 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature -40.0 - 30.0 °C |
278 µin/in-°F @Temperature -40.0 - 86.0 °F |
ISO 11359-1/-2 |
| 500 µm/m-°C @Temperature 105 - 150 °C |
278 µin/in-°F @Temperature 221 - 302 °F |
ISO 11359-1/-2 | |
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1/-2 | |
| 500 µm/m-°C @Temperature 60.0 - 105 °C |
278 µin/in-°F @Temperature 140 - 221 °F |
ISO 11359-1/-2 | |
| CTE, linear, Transverse to Flow | 120 µm/m-°C @Temperature 23.0 - 55.0 °C |
66.7 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1/-2 |
| Melting Point | 178 °C | 352 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C | 324 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | ISO 75-1/-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 215 °C | 419 °F | Optimum; Injection Molding |
| 210 - 220 °C | 410 - 428 °F | Injection Molding | |
| Mold Temperature | 90.0 °C | 194 °F | optimum; Injection Molding |
| 80.0 - 100 °C | 176 - 212 °F | Injection Molding | |
| Drying Temperature | 80.0 °C | 176 °F | Injection Molding |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Injection Molding |
| Moisture Content | <= 0.20 % | <= 0.20 % | Injection Molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Natural Color | |
| Features | Creep Resistance, Good | |
| Dimensional Stability, Good | ||
| Fatigue Resistant | ||
| Homopolymer | ||
| Stiffness, High | ||
| Strength, High | ||
| Viscosity, Low | ||
| Forms | Pellets | |
| Generic | Acetal (POM) Homopolymer | |
| Material Status | Preliminary Data | |
| Part Marking Code | >POM< | ISO 11469 |
| Processing Method | Injection Molding | |
| Product Category | Food Contact Resins | |
| Unreinforced Resins | ||
| Region Available - Global | Yes | |
| Resin Identification | POM | ISO 1043 |
| RoHS Compliance | Contact Manufacturer | |
| Uses | Food Applications, Non-specific | |
| Gears | ||
| General Purpose | ||
| Parts, Engineering | ||
| Parts, Thin-walled |