Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 71.0 MPa | 10300 psi | chs 2 in/min; ASTM D638 |
Network Polymers PC-1011 L Description: Natural PolycarbonateInformation provided by Network Polymers Inc. |
|||
Tensile Strength, Yield | 71.0 MPa | 10300 psi | chs 2 in/min; ASTM D638 |
Network Polymers PC-1015R Description: Natural PolycarbonateInformation provided by Network Polymers Inc. |
|||
Tensile Strength, Yield | 71.0 MPa | 10300 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® ML6451 PC UV-stabilized, co-extrusion capstock material. Minimal processing values available at this time. |
|||
Tensile Strength, Yield | 71.0 MPa | 10300 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® ML6451 PC (Asia Pacific) UV-stabilized, co-extrusion capstock material. Minimal processing values available at this time. |
|||
Tensile Strength, Yield | 71.0 MPa | 10300 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP DFL22 PC (Asia Pacific) LNP* Lubricomp* DFL22 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength, Yield | 71.0 MPa | 10300 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DFL22 PC (Asia Pacific) LNP* Lubricomp* DFL22 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength, Yield | 71.0 MPa @Temperature 23.0 °C |
10300 psi @Temperature 73.4 °F |
ISO 527 |
DuPont Performance Polymers Delrin® 100TL NC010 Acetal Homopolymer
(Unverified Data**) Delrin® 100TL NC010 is a high viscosity acetal homopolymer with 1.5% Teflon® PTFE Micropowder.Information provided by DuPont Performance Polymers |
|||
Tensile Strength, Yield | 71.0 MPa @Temperature 23.0 °C |
10300 psi @Temperature 73.4 °F |
ISO 527 |
DuPont Performance Polymers Delrin® 300CP NC010 Acetal Homopolymer
(Unverified Data**) Delrin® 300CP is a medium-high viscosity acetal homopolymer with improved thermal stability and an outstanding balance of ease of processing and part performance.Information provided by DuPont Perf.. |
|||
Tensile Strength, Yield | 71.0 MPa @Temperature 23.0 °C |
10300 psi @Temperature 73.4 °F |
ISO 527 |
DuPont Performance Polymers Delrin® 500P BK602 Acetal Homopolymer
(Unverified Data**) Delrin® 500P BK602 is a general purpose medium viscosity black acetal homopolymer resin for injection molding. Delrin® 500P has improved processing thermal stability compared to Delrin® 500.Infor.. |
|||
Tensile Strength, Yield | 71.0 MPa @Temperature 23.0 °C |
10300 psi @Temperature 73.4 °F |
ISO 527 |
DuPont Performance Polymers Delrin® 527UV BK701 Acetal Homopolymer
(Unverified Data**) Delrin® 527UV BK701 is a medium viscosity black acetal homopolymer resin with UV stabilizers developed for automotive interior applications. It has improvements in UV aging characteristics and ther.. |
|||
Tensile Strength, Yield | 71.0 MPa | 10300 psi | ISO 527 |
Aardvark Polymers AARTEL® 2000 Rotational Molding Resin Aartel® 2000 POM is a premium homopolymer acetal for rotational molding applications. Aartel® 2000 offers high performance properties and is a high flow, fast cycling polymer.Information prov.. |
|||
Tensile Strength, Yield | 71.0 MPa | 10300 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL PX9406P PPE+PS (Europe-Africa-Middle East) |
|||
Tensile Strength, Yield | 71.0 MPa | 10300 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RX99518 PA 66 LNP* LUBRICOMP* RX99518 is a compound based on PA66 containing Proprietary Fillers. Added feature of this material is: Wear Resistant. |
|||
Tensile Strength, Yield | 71.0 MPa @Temperature -40.0 °C |
10300 psi @Temperature -40.0 °F |
ISO Data |
Styrolution Luran® S 757 G ASA Luran S 757 G is an easy flowing injection molding ASA grade with large flow path/wall thickness ratios.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS. |
|||
Tensile Strength, Yield | 71.0 MPa | 10300 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL HNA033 PPE+HIPS Noryl* HNA033 resin is an unfilled modified polyphenylene ether resin designed to withstand several cycles in an autoclave. This resin is suitable for multiple conversion routes and is available in.. |
|||
Tensile Strength, Yield | 71.0 MPa | 10300 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL HNA033 PPE+HIPS (Asia Pacific) Noryl* HNA033 resin is an unfilled modified polyphenylene ether resin designed to withstand several cycles in an autoclave. This resin is suitable for multiple conversion routes and is available in.. |
|||
Tensile Strength, Yield | 71.0 MPa | 10300 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL HNA033 PPE+HIPS (Europe-Africa-Middle East) Noryl* HNA033 resin is an unfilled modified polyphenylene ether resin designed to withstand several cycles in an autoclave. This resin is suitable for multiple conversion routes and is available in.. |
|||
Tensile Strength, Yield | 71.0 MPa | 10300 psi | ISO 527 |
SABIC Innovative Plastics NORYL HS2000X PPE+PS PPE+PS blend. 17% Mineral reinforced. Non-brominated, non-chlorinated FR system. UL94 V0 and 5VA listing. UL746C f1. Radiant panel listing. Dielectric strength. Dimensional stability. Suitable for E.. |
|||
Tensile Strength, Yield | 71.0 MPa | 10300 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL LTA6020 PPE+PS (Asia Pacific) |
|||
Tensile Strength, Yield | 71.0 MPa | 10300 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL PX500 PPE (Asia Pacific) Noryl PX500 is an unfilled modified polyphenylene ether resin capable of multiple conversion routes. This resin is designed for lower odor during conversion than many standard modified PPE resins. .. |
|||
Tensile Strength, Yield | 71.0 MPa | 10300 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP 9X10401H ABS LNP* THERMOCOMP* 9X10401H is a compound based on Polyphenylsulfone containing proprietary filler(s). Added feature of this grade is: X-Ray Opaque. |
|||
Tensile Strength, Yield | 71.0 MPa | 10300 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP 9X11428J PPS LNP* THERMOCOMP* 9X11428J is a compound based on Polyphenylsulfone containing Proprietary Fillers. Added features of this material include: Healthcare, Low Extractable. |
|||
Tensile Strength, Yield | 71.0 MPa | 10300 psi | SABIC - Japan Method |
SABIC Innovative Plastics NORYL PX1712 PPE+HIPS (Asia Pacific) PPE/HIPS unfilled high heat for auto interior |
|||
Tensile Strength, Yield | 71.0 MPa | 10300 psi | ASTM D638 |
Washington Penn Homopolymer Polypropylene 27% Glass Reinforced Fiberglass & mineral-reinforced polypropylene compounds provide excellent tensile and impact properties. Mold shrinkage is similar to ABS and polystyrene. Compounds also have dimensional stability. .. |
|||
Tensile Strength, Yield | 71.0 MPa | 10300 psi | ISO 527-2 |
Tisan TISLAMID® 6 15% Mineral Filled Flame Retardant (V0). Heat Stabilized Nylon 6 TISLAMID has a wide area of application in electric/electronic, automotive, durable goods and telecommunications industries. It demonstrates characteristics such as Excellent chemical resistanceElec.. |
|||
Tensile Strength, Yield | 71.0 MPa | 10300 psi | ISO 527-1/-2 |
DuPont Performance Polymers Delrin® 100TL NC010 Acetal (POM)
(Unverified Data**) Teflon® Lubricated High Viscosity Acetal Homopolymer with Low Wear and Low FrictionDelrin 100TL NC010 (formerly Delrin 100TL NC000) is a high viscosity acetal homopolymer with 1.5% TeflonInformatio.. |
|||
Tensile Strength, Yield | 71.0 MPa | 10300 psi | ISO 527-1/-2 |
DuPont Performance Polymers Delrin® PC690 NC010 Acetal (POM)
(Unverified Data**) Low Viscosity Acetal Homopolymer Developed for the Healthcare Industry Delrin SC690 is a low viscosity acetal homopolymer developed for parts requiring high precision molding in the healthcare indus.. |
|||
Tensile Strength, Yield | 71.0 MPa | 10300 psi | ISO 527 |
Eurostar Star L PA66 D51 PA66, Injection Molded Star L PA66 D51 is a PTFE Lubricated, Unreinforced, Polyamide 66 Injection Molding ResinInformation provided by Eurostar. |
|||
Tensile Strength, Yield | 71.0 MPa | 10300 psi | 50 mm/min |
Arkema Group Cristamid® MS 1300 Semi-Aromatic Nylon (PASA) (Conditioned) Designation ISO 1874-PA12/xx,MR,12-020Semi-aromatic polyamide (PASA) grade for injection molding and tubes extrusion.Transparency even thick. High resistance to environmental stress cracking. Good t.. |
|||
Tensile Strength, Yield | 71.0 - 174 MPa | 10300 - 25200 psi | Average value: 111 MPa Grade Count:5 |
Overview of materials for Polyphthalamide (PPA), Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, Mineral Filled". Each property range of values reported is minimum and maximum values o.. |