Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 3.00 GPa | 435 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Cycoloy® CE1821 PC+ABS (Asia Pacific) High stiffness PC/ABS blend offering high impact, high heat, low CTE, good surface quality and excellent extrusion and thermoforming characteristics. |
|||
Flexural Modulus | 3.00 GPa | 435 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycoloy® CE1821 PC+ABS (Europe-Africa-Middle East) High stiffness PC/ABS blend offering high impact, high heat, low CTE, good surface quality and excellent extrusion and thermoforming characteristics.This data was supplied by SABIC-IP for the Europe.. |
|||
Flexural Modulus | 3.00 GPa | 435 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics EXTEM UH1006 TPI Blend (Asia Pacific) High heat amorphous TPI Blend, Chemical Resistant |
|||
Flexural Modulus | 3.00 GPa | 435 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics EXTEM UH1006M TPI Blend High heat amorphous TPI Blend, Chemical Resistant |
|||
Flexural Modulus | 3.00 GPa | 435 ksi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DAL22 PC LNP* Lubricomp* DAL22 is a compound based on Polycarbonate resin containing 10% PTFE and 10% Aramid Fiber. Added features of this material include: Internally Lubricated. |
|||
Flexural Modulus | 3.00 GPa | 435 ksi | |
Lehmann & Voss LUVOCOM® 1106-8032/GY Polyether imide, unreinforced, laser markable Applications: High continuous use and heat distortion temperature. Non flammable.Dynamic stressed parts at high movement velocity.High dimensionally stable precision parts.Information provided by Le.. |
|||
Flexural Modulus | 3.00 GPa | 435 ksi | |
Lehmann & Voss LUVOCOM® 20-7314 Polyphthalamide, with PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Low influence from moisture an.. |
|||
Flexural Modulus | 3.00 GPa @Temperature 22.0 °C |
435 ksi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
Menzolit Menzolit® SMC 0520 Unsaturated Polyester UP SMC 0520 is a special SMC with significantly reduced density. The glass level has been selected to combine good moulding with sufficient strength and stiffness properties. Even without a specific fi.. |
|||
Flexural Modulus | 3.00 GPa | 435 ksi | ASTM D790 |
Iran Petrochemical (PCC) GPPS 1540 Polystyrene GPPS 1540 is an easy flowing crystal polystyrene designed for extrusion or injection applications. In extrusion, it improves extruder output and thermoforming cycle times when mixed with a high impa.. |
|||
Flexural Modulus | 3.00 - 3.50 GPa | 435 - 508 ksi | ASTM D790 |
Loxim 820 01 HB Polypropylene Compound, Flame Retardant Information provided by Loxim Industries |
|||
Flexural Modulus | 3.00 GPa | 435 ksi | ASTM D790 |
Mitsui Arlen™ AE4200N Modified Nylon 6T, for Tribolic Applications, Flame Retardant (DAM) ARLEN™ is a heat resistant, modified polyamide 6T developed by Mitsui Chemicals, Inc. With a high melting point (320°C) and a rigidity level comparable to super engineering plastics, it poss.. |
|||
Flexural Modulus | 3.00 GPa | 435 ksi | |
Lehmann & Voss LUVOCOM® 1/AR/5/NT Polyamide 66, with aramid reinforcement Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved wear behaviour, low warpage.Isotropic shrinkage characteristics.Control disks, cams, s.. |
|||
Flexural Modulus | 3.00 GPa | 435 ksi | |
Lehmann & Voss LUVOCOM® 1105-7685 PEEK, unreinforced Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High chemical resistance parts, non flammable.Suitable for biocompatible application.Super.. |
|||
Flexural Modulus | 3.00 GPa | 435 ksi | |
Lehmann & Voss LUVOCOM® 1105/TF/20/NAT PEEK, with PTFE Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts, non flammable.Improved friction and wear behavio.. |
|||
Flexural Modulus | 3.00 GPa | 435 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics ULTEM 4001 PEI (Europe-Africa-Middle East) PTFE filled, standard flow Polyetherimide (Tg 217C). Resin is RoHS compliant. UL94 V0 and 5VA listing. |
|||
Flexural Modulus | 3.00 GPa | 435 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM HU1004 PEI (Asia Pacific) High Temperature, Transparent, Polyetherimide Blend with Improved Ductility and Enhanced Hydrostability. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI) and FDA and EUFC f.. |
|||
Flexural Modulus | >= 3.00 GPa | >= 435 ksi | GB/T 9341-2008 |
Sichuan Deyang Haton® hb DL Polyphenylene Sulfide Resin Extrusion, low chlorineInformation provided by Sichuan Deyang Chemical Co., LTD |
|||
Flexural Modulus | 3.00 GPa | 435 ksi | ISO 178 |
Polyram PlusTek PA108 Nylon6/6.6 Alloy for Injection Molding Good surface finish Nylon 6/6.6 alloy for injection molding.Information provided by Polyram. |
|||
Flexural Modulus | 3.00 GPa | 435 ksi | ASTM D790 |
Tipco Tipcolene® FPT 30 PPC - 30% Talc Reinforced Polypropylene Copolymer Compound 30% Talc Reinforced PP CopolymerApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
Flexural Modulus | 3.00 GPa | 435 ksi | ISO 178 |
Polyram RamTal PMH2010 Polyacetal Homopolymer for Injection Molding General purpose polyacetal homopolymer for injection molding applications, MFI 10.Information provided by Polyram. |
|||
Flexural Modulus | 3.00 GPa | 435 ksi | ISO 178 |
Polyram RamTough RZ300G2 Polycarbonate, 10% Glass Fiber 10% Glass fiber reinforced polycarbonate for injection molding applications.Information provided by Polyram. |
|||
Flexural Modulus | 3.00 GPa | 435 ksi | ASTM D790 |
A. Schulman POLYFORT™ FPP 1602 Glass Reinforced, Chemically Coupled Homopolymer DescriptionPolyfort® FPP 1602 is a 10% glass reinforced chemically coupled homopolymer.Information provided by A. Schulman. |
|||
Flexural Modulus | 3.00 GPa | 435 ksi | DIN 52457 |
CP-Polymer-Technik Wellamid® 6000/505 GS 30 HWCP 30% Impact Modified Glass Sphere Filled Nylon 6, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Flexural Modulus | 3.00 GPa | 435 ksi | 2 mm/min; ISO 178 |
Chi Mei Kibisan® PN-107 L125 SAN High Clarity |
|||
Flexural Modulus | 3.00 GPa | 435 ksi | |
Abatron AboCast 50-3/AboCure 50-12 Epoxy Data provided by the manufacturer, Abatron, Inc. Light motor oil viscosity, almost colorless. Shelf life is 12+ months. |
|||
Flexural Modulus | 3.00 GPa | 435 ksi | ISO 178 |
Celanese Hostaform® C 13031 LS POM, UV Resistant POM copolymerInformation provided by Celanese |
|||
Flexural Modulus | 3.00 GPa | 435 ksi | ISO 178 |
BASF Ultramid® B3GK24 BK 00564 10/20% Glass/Glass Bead Filled PA6 (Conditioned) Description: combined 10% glass-fiber and 20% glass-bead reinforced injection-molding grade for technical articles of very good dimensional stability, for instance, vehicle ash tray housings and ele.. |
|||
Flexural Modulus | 3.00 GPa | 435 ksi | ASTM D790 |
Chem Polymer Formax 605 G Acetal, 5% Glass Reinforced A lubricated, 5% glass reinforced acetal offering a balance of rigidity, dimensional stability and tensile strength.Data provided by the manufacturer, Chem Polymer. |