- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 162 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 162 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C @Thickness 3.18 mm |
324 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Maxxam™ PPR-30G Black Polypropylene Homopolymer (PP Homopolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C @Thickness 3.18 mm |
324 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Maxxam™ PPR-30G Nat Polypropylene Homopolymer (PP Homopolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C @Thickness 3.18 mm |
324 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Maxxam™ PPR-40G Black Polypropylene Homopolymer (PP Homopolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C | 324 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Delrin® 500P BK602 Acetal Homopolymer
(Unverified Data**) Delrin® 500P BK602 is a general purpose medium viscosity black acetal homopolymer resin for injection molding. Delrin® 500P has improved processing thermal stability compared to Delrin® 500.Infor.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C | 324 °F | ASTM D648 |
| Kolon Kocetal® CL704 Reinforced Grade Acetal Copolymer
(discontinued **) Thermal properties: Kocetal has excellent heat stability; heat degradation is little under long term and high temperature application, compared to other POM. Maximum applicable temperature of produ.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C @Thickness 3.20 mm |
324 °F @Thickness 0.126 in |
ASTM D648 |
| Covestro Apec® DP9-9340R High-Heat Polycarbonate, Medical with Release
(discontinued **) It is the responsibility of the medical device, biological product, or pharmaceutical manufacturer (Manufacturer) to determine the suitability of all component parts and raw materials, including the.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C @Thickness 3.20 mm |
324 °F @Thickness 0.126 in |
ASTM D648 |
| Covestro Apec® DP9-9341 High-Heat Polycarbonate, General Purpose
(discontinued **) Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C @Thickness 3.20 mm |
324 °F @Thickness 0.126 in |
ASTM D648 |
| Covestro Apec® DP9-9343 High-Heat Polycarbonate, UV Stabilized
(discontinued **) Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C @Thickness 6.40 mm |
324 °F @Thickness 0.252 in |
ASTM D648 |
| Kingfa PBT-R0N Flame Retardant PBT Features:Flame retardantGood chemical resistanceOutstanding surfaceEasy processingHigh impactApplications:Injection moldingConnectors, terminal blocksRelay, switchBobbinsPlugsE & E partsInformation .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C @Thickness 3.20 mm |
324 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Noryl PX7446 PPE+PS This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C @Thickness 3.20 mm |
324 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP KAL22 Acetal Copolymer LNP* LUBRICOMP* KAL22 is a compound based on Acetal Copolymer resin containing 10% PTFE, 10% Aramid Fiber. Added feature of this material is: Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C @Thickness 3.20 mm |
324 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Lubricomp KCL22 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KCL22 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This data .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C @Thickness 3.20 mm |
324 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Lubricomp KCL34 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KCL34 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This data .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C @Thickness 3.20 mm |
324 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP KFP032 Acetal Copolymer LNP LUBRICOMP* KFP032 is a compound based on Acetal Copolymer resin containing 10% Glass Fiber, 15% PTFE/Silicone. Added feature of this material is: Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C @Thickness 3.20 mm |
324 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON KE004 Acetal Copoly LNP* STAT-KON* KE004 is a compound based on Acetal Copolymer resin containing 20% Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C @Thickness 3.20 mm |
324 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Thermocomp KF003 Acetal Copoly (Asia Pacific) LNP* Thermocomp* KF003 is a compound based on Acetal Copolymer resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C @Thickness 3.20 mm |
324 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP KF006XXC Acetal Copolymer LNP* THERMOCOMP* KF006XXC is a compound based on Acetal Copolymer resin containing 30% Glass Fiber. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C | 324 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP VERTON MV007SUP PP (Europe-Africa-Middle East) LNP* VERTON* MV007SUP is a compound based on PP resin containing Long Glass Fiber. Added features include; Chemically Coupled, Heat Stabilized, UV Stabilized. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C @Thickness 3.20 mm |
324 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Lubricomp KCL34 Acetal Copoly LNP* Lubricomp* KCL34 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This data .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C @Thickness 3.20 mm |
324 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP KCL36 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KCL36 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C | 324 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP STAT-LOY P3000U PA 6 (Europe-Africa-Middle East) LNP* Stat-loy* P3000U is a compound based on PA 6 resin. Added features include; Antistatic, UV - Stabilized. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C | 324 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP VERTON MX02795 PP LNP* VERTON* MX02795 is a compound based on Polypropylene resin containing Proprietary Fillers. Added features of this material include: Heat Stabilized, UV Stabilized, Structural. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C | 324 °F | ISO 75-1/-2 |
| Unitika A1030SR PA6, Dry Information provided by Unitika Ltd. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C | 324 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Delrin® 127UV BK701 Acetal (POM)
(Unverified Data**) UV Stabilized High Viscosity Acetal Homopolymer Delrin 127UV BK701 is a high viscosity UV stabilized acetal homopolymer. It has excellent impact strength UV resistance and thermal stability. It is w.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C | 324 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Delrin® 500P BK602 Acetal (POM)
(Unverified Data**) Medium Viscosity Acetal Homopolymer with Improved ProcessingDelrin 500P BK602 is a general purpose medium viscosity black acetal homopolymer resin for injection molding. Delrin 500P has improved pro.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C | 324 °F | 0.125";; ASTM D648 |
| Diamond Polymers NPP30-0800 GF40 40% Glass Filled Homopolymer Polypropylene Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C | 324 °F | |
| Arkema Group Rilsan® AESN G9 T6L Nylon 12, Graphite Filled (Conditioned) Designation ISO 1874-PA12,EHLS,22-010,CD10Rigid grade with graphite fillers for extrusion. Available color: steel gray. Reinforced light and heat stabilizing agents.Very low friction coefficient. No.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C | 324 °F | ASTM D648 |
| Aclo Accutech Polypropylene CP0435G43CV Copolymer Glass Reinforced Coupled Approved to GMP.PP.039 Black A13054 |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C | 324 °F | ASTM D648 |
| Asahi Kasei Thermylene® P6-30FG-0600 30% Glass Fiber Reinforced, Heat Stabilized Information provided by Asahi Thermofil |
|||