3M Scotch-Weld™ DP110 Gray Epoxy Adhesive

Category	Polymer , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer	3M
Trade Name	Scotch-Weld™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Scotch-Weld™ DP110 Gray Epoxy Adhesive.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

3M™ Scotch-Weld™ Epoxy Adhesive DP110 Translucent and Gray are two-part epoxy adhesive which combine a fast cure with flexibilityInformation provided by 3M

Physical Properties	Metric	English	Comments
Viscosity	40000 - 90000 cP	40000 - 90000 cP	Base
	40000 - 90000 cP	40000 - 90000 cP	Accelerator

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	45	45
Elongation at Break	40 %	40 %
Shear Strength	0.276 - 0.414 MPa	40.0 - 60.0 psi	Overlap, Neoprene Rubber/Steel
	0.552 - 0.689 MPa	80.0 - 100 psi	Overlap, SBR/Steel
	1.03 MPa	150 psi	Overlap, Abraded Aluminum, 14 days in 5% salt spray @ 35°C
	2.69 MPa	390 psi	Overlap, PVC/PVC, Rigid
	3.31 MPa	480 psi	Overlap, Acrylic/Acrylic
	3.45 MPa	500 psi	Overlap, Etched Aluminum, 14 days in 5% salt spray @ 35°C
	4.69 MPa	680 psi	Overlap, ABS/ABS Plastic
	4.69 MPa	680 psi	Overlap. PC/PC
	4.83 MPa	700 psi	Overlap, Abraded Aluminum, 3 days, 71°C, 100% RH
	8.27 MPa	1200 psi	Overlap, Etched Aluminum, 3 days, 71°C, 100% RH
	8.62 MPa	1250 psi	Overlap, Abraded Aluminum, 30 days tap water @ RT
	9.65 MPa	1400 psi	Overlap, Fiber Reinforced Polyester/Fiber Reinforced Polyester
	12.1 MPa	1750 psi	Overlap, Copper/Copper
	15.9 MPa	2300 psi	Overlap, Al/Al
	15.9 MPa	2300 psi	Overlap, Etched Aluminum, 30 days tap water @ RT
	15.9 MPa	2300 psi	Overlap, Abraded Aluminum, Initial
	16.9 MPa	2450 psi	Overlap, Stainless Steel/Stainless Steel
	16.9 MPa	2450 psi	Overlap, Brass/Brash
	17.2 MPa	2500 psi	Overlap, CRS/CRS
	17.2 MPa	2500 psi	Overlap, Etched Aluminum, Initial
	17.9 MPa	2600 psi	Overlap, Galvanized Steel/Galvanized Steel
	1.72 MPa @Temperature 82.0 °C	250 psi @Temperature 180 °F	Overlap
	1.86 MPa @Temperature 71.0 °C	270 psi @Temperature 160 °F	Overlap
	18.6 MPa @Temperature -55.0 °C	2700 psi @Temperature -67.0 °F	Overlap
	24.1 MPa @Temperature 24.0 °C	3500 psi @Temperature 75.2 °F	Overlap
Peel Strength	3.51 kN/m	20.0 pli	T-Peel

Thermal Properties	Metric	English
CTE, linear	73.0 µm/m-°C @Temperature -50.0 - 0.000 °C	40.6 µin/in-°F @Temperature -58.0 - 32.0 °F
	165 µm/m-°C @Temperature -50.0 - 110 °C	91.7 µin/in-°F @Temperature -58.0 - 230 °F
Thermal Conductivity	0.180 W/m-K @Temperature 45.0 °C	1.25 BTU-in/hr-ft²-°F @Temperature 113 °F
Glass Transition Temp, Tg	16.0 °C	60.8 °F

Electrical Properties	Metric	English	Comments
Volume Resistivity	6.90e+10 ohm-cm	6.90e+10 ohm-cm
Dielectric Strength	18.5 kV/mm	470 kV/in

Descriptive Properties	Value	Comments
Appearance	Black
	Gray	Base
	White	Accelerator